Reactive consolidation of medium entropy diboride in the ZrB2–TaB2–NbB2 system was performed by spark plasma sintering of diboride powders at 2000 °C. The 3:2:1 ratio between Zr, Ta, and Nb showed the highest specific strength at room temperature during the initial screening of the mechanical properties. The flexural strength gradually decreased from 700 ± 42 MPa at RT to 518 ± 30 MPa at 1600 °C with the Weibull parameter exceeding 15. Diborides with an equimolar composition did not show a maximum in their strength, fracture toughness or hardness.

権利情報:

• In Copyright
  

キーワード: diborides, high-temperature strength, high-entropy ceramic, Reactive SPS

刊行年月日: 2022-11-16

出版者: Elsevier BV

掲載誌:

• Scripta Materialia (ISSN: 13596462) vol. 225 115170

研究助成金:

• NIMS PA3030 (粉体・セラミックス 結晶・界面の階層的構造制御による機能顕在化のための研究 30)
• NIMS PA5180 (セラミックスプロセッシング - 70 )

原稿種別: 著者最終稿 (Accepted manuscript)

MDR DOI: https://doi.org/10.48505/nims.4960

公開URL: https://doi.org/10.1016/j.scriptamat.2022.115170

関連資料:

その他の識別子:

連絡先:

更新時刻: 2024-11-21 16:31:55 +0900

MDRでの公開時刻: 2024-11-21 16:31:57 +0900