In this study, flexural strength measurements and microstructural studies have been combined to evaluate the effect of elevated temperatures on the fracture behavior of B4C–TaB2 ceramic composites that have a eutectic structure. Mechanical characterization was carried out at 1600 °C, 1800 °C and 2000 °C. The B4C–TaB2 eutectic composites were prepared in situ using a spark plasma sintering technique. The eutectic composites exhibited strengths of 483±17 MPa and 525±12 MPa at 1600 °C and 1800 °C, respectively, which is higher than the strength of 430±25 MPa measured at room temperature. The flexural strength of the B4C–TaB2 eutectic composites was 511±16 MPa at 2000 °C (i.e. 0.86 of the melting point of the B4C–TaB2 eutectic), indicating plastic behavior. An

権利情報:

• Creative Commons BY-NC-ND Attribution-NonCommercial-NoDerivs 4.0 International
  

キーワード: boron carbide, high-temperature strength, eutectic composite, tantalum diboride, spark plasma sintering

刊行年月日: 2017-04-25

出版者: Elsevier BV

掲載誌:

• Materials Science and Engineering: A (ISSN: 09215093) vol. 697 p. 71-78

研究助成金:

• NIMS AB3080

原稿種別: 著者最終稿 (Accepted manuscript)

MDR DOI: https://doi.org/10.48505/nims.5504

公開URL: https://doi.org/10.1016/j.msea.2017.04.093