We report for the first time the effect of temperature on the mechanical properties of (Ta1/3Ti1/3Zr1/3)C carbide. Flexural strength and fracture toughness were investigated using the three-point bending technique in argon. Using commercially available carbide powders with an equimolar ratio and performing spark plasma consolidation at 1973°C, we obtained a bulk single-phase medium-entropy carbide ceramic with the lattice parameter a= 4.458 Å. The flexural strength and fracture toughness at room temperature reached on average 700 MPa and 3.2 MPa m1/2, respectively. At 1800°C, local decomposition of the medium-entropy carbide took place as a structure with a local chemical gradient was observed after high-temperature tests, which increased fracture toughness by 30% (to 4.4 MPa m1/2). © 2020 The Author(s). Published by Informa UK Limited, trading as Taylor & Francis Group on behalf of The Korean Ceramic Society and The Ceramic Society of Japan.

権利情報:

• Creative Commons BY Attribution 4.0 International
  

キーワード: tantalum carbide, high-entropy ceramics, flexural strength, toughness, high-temperature materials

刊行年月日: 2020-10-01

出版者: Informa UK Limited

掲載誌:

• JOURNAL OF ASIAN CERAMIC SOCIETIES vol. 8 issue. 4

研究助成金:

• NIMS 70% AB3080, 30% AB3020

原稿種別: 著者最終稿 (Accepted manuscript)

MDR DOI: https://doi.org/10.48505/nims.5497

公開URL: https://doi.org/10.1080/21870764.2020.1840703

関連資料:

その他の識別子:

連絡先:

更新時刻: 2025-05-23 08:30:24 +0900

MDRでの公開時刻: 2025-05-22 16:32:07 +0900