Mixtures of B4C, AlB12 and B powders were reactively spark plasma sintered at 1800 C. Crystalline and amorphous boron powders were used. Samples were tested for their impact behavior by the Split Hopkinson Pressure Bar method. When the ratio R = B4C/AlB12 exceeding 1.3 for a constant B-amount, the major phase in the samples was the orthorhombic AlB24C4, and when R < 1 the amount of AlB24C4 significantly decreased. Predictions that AlB24C4 has the best mechanical impact properties since it is the most compact and close to the ideal cubic packing among the Al-B-C phases containing B12-type icosahedra were partially confirmed. Namely, the highest values of Vickers hardness (32.4 GPa), dynamic strength (1323 MPa), strain and toughness were determined for the samples with R =1.3, i.e. for the samples with a high amount of AlB24C4. However, the existence of a maximum, visible especially in the dynamic strength vs. R, indicated the additional influence of the phases and the composites microstructure in the samples. The type of boron does not influence the dependencies of the indicated mechanical parameters with R, but the curves are shifted to slightly higher values for the samples in which amorphous boron was used.

権利情報:

• In Copyright
  

キーワード: Reactive spark plasma sintering, impact properties, Split Hopkinson Pressure Bar Test, Aluminum dodecaboride

刊行年月日: 2019-12-20

出版者: Springer Science and Business Media LLC

掲載誌:

• Scientific Reports (ISSN: 20452322) vol. 9 19484

研究助成金:

• UEFISCDI project, Romania, EU POC 37_697 no. 28/01.09.2016 REBMAT
• NIMS PA5180 (セラミックスプロセッシング)

原稿種別: 著者最終稿 (Accepted manuscript)

MDR DOI: https://doi.org/10.48505/nims.4981

公開URL: https://doi.org/10.1038/s41598-019-55888-z

関連資料:

その他の識別子:

連絡先:

更新時刻: 2024-11-21 16:35:46 +0900

MDRでの公開時刻: 2024-11-21 16:35:47 +0900