All-solid-state lithium-ion batteries are a promising next-generation technology because they have higher energy densities than their liquid-electrolyte counterparts. Halogen-rich argyrodite, specifically Li5.4(PS4)(S0.4Cl1.0Br0.6), was recently shown to have higher ionic conductivities compared with those of other argyrodite-like sulfides. Although the Li5.4(PS4)(S0.4Cl1.0Br0.6) in Li | Li5.4(PS4)(S0.4Cl1.0Br0.6) | Li(Ni0.8Co0.1Mn0.1)O2–Li5.4(PS4)(S0.4Cl1.0Br0.6) batteries have shown good electrochemical stability, the low discharge capacity limits the application of the battery. In continuation, this study examined the potential of a carbon additive for altering the electronic conductivity of the cathode and enhancing the capacity of Li | Li5.4(PS4)(S0.4Cl1.0Br0.6) | Li(Ni0.8Co0.1Mn0.1)O2–Li5.4(PS4)(S0.4Cl1.0Br0.6) batteries. After a 50-cycle charge/discharge, the carbon additive (0.1 C) enhanced the discharge capacity from 3.1 to 167 mAh/g, resulted in a capacity retention rate and coulombic efficiency of 95.4% and 99.9% when using 0.1 C and 0.5 C, respectively, and increased the resistance of the battery from 53 to 56 Ω. Therefore, the all-solid-state battery employing high-ion-conductive Li5.4(PS4)(S0.4Cl1.0Br0.6) and a carbon-modified cathode showed improved capacity. This study provides a proven framework for developing all-solid-state batteries employing halogen-rich argyrodite (Li7-α(PS4)(S2-αXα); α > 1) with enhanced ionic conductivities.

権利情報:

• In Copyright
  

  This version of the article has been accepted for publication, after peer review (when applicable) and is subject to Springer Nature’s AM terms of use, but is not the Version of Record and does not reflect post-acceptance improvements, or any corrections. The Version of Record is available online at: http://dx.doi.org/10.1007/s10008-024-05886-7

キーワード: All-solid-state battery, argyrodite, halogen-rich, high capacity, solid electrolyte

刊行年月日: 2024-04-04

出版者: Springer Science and Business Media LLC

掲載誌:

• Journal of Solid State Electrochemistry (ISSN: 14330768) p. 4409-4417

研究助成金:

原稿種別: 著者最終稿 (Accepted manuscript)

MDR DOI: https://doi.org/10.48505/nims.5091

公開URL: https://doi.org/10.1007/s10008-024-05886-7

関連資料:

その他の識別子:

連絡先:

更新時刻: 2025-04-09 08:30:14 +0900

MDRでの公開時刻: 2025-04-08 21:53:58 +0900