A novel testing method was developed to evaluate the fracture toughness of ultra-high-strength (UHS) steel sheets. The study also examined the influence of specimen thickness, utilizing specimens of varying thicknesses (1.6 ~ 10 mm). While the toughness of all specimens was determined by the threshold for planar crack propagation originating from the fatigue pre-crack-front near the mid-thickness zone, the apparent fracture toughness was dependent on specimen thickness. This phenomenon was attributed to the crack-closure effects experienced during the pre-cracking process. In-depth analyses revealed that, in the absence of crack-closure effects, the intrinsic toughness remained unaffected by changes in specimen thickness.

権利情報:

• Creative Commons BY-NC-ND Attribution-NonCommercial-NoDerivs 4.0 International
  

キーワード: Ultra-high-strength steel, Fracture toughness, Thickness effect, Crack-closure, MT specimen

刊行年月日: 2024-07-17

出版者: Elsevier BV

掲載誌:

• Engineering Fracture Mechanics (ISSN: 00137944) 110322

研究助成金:

原稿種別: 著者最終稿 (Accepted manuscript)

MDR DOI: https://doi.org/10.48505/nims.4914

公開URL: https://doi.org/10.1016/j.engfracmech.2024.110322

関連資料:

その他の識別子:

連絡先:

更新時刻: 2024-11-01 13:08:08 +0900

MDRでの公開時刻: 2026-07-17 08:34:15 +0900