説明:

The paper investigates the microstructure evolution and phase analysis of the Sm60Ni40 alloy. The arc melted sample retained the high temperature stable (>873 K) Sm7Ni3 and Sm3Ni2 phases along with the congruently melting SmNi phase. Annealing the as-cast sample at 903 K for 100 h stabilized the high temperature stable (873 K − 903 K) Sm3Ni2 phase. Rietveld refinement was performed to resolve the crystal structure of Sm3Ni2 phase and it was observed that Sm3Ni2 phase stabilizes in monoclinic crystal structure (space group: C2/m) with a lattice parameter of a = 13.49 Å, b = 3.75 Å, c = 9.68 Å and β = 106.6°. The Curie temperature of the Sm3Ni2 phase was determined to be ∼ 110 K. The high squareness ratio of 82 % along with high coercivity of 3 T indicates that the Sm3Ni2 phase possess spontaneous uniaxial magnetic anisotropy.

権利情報:

• In Copyright
  

キーワード: Sm-Ni alloy, Annealing, Microstructure, Magnetic property, Crystal structure

刊行年月日: 2022-12-26

出版者: Elsevier

掲載誌:

• Journal of Magnetism and Magnetic Materials (ISSN: 03048853) vol. 566 170323

研究助成金:

原稿種別: 査読前原稿 (Author's original)

MDR DOI: https://doi.org/10.48505/nims.4628

公開URL: https://doi.org/10.1016/j.jmmm.2022.170323