Rare-earth barium copper oxide (REBCO) superconductors can be applied to superconducting magnets in low-temperature and high-magnetic-field and electric power equipment. Currently available superconducting wires supplied by many companies are tape-shaped, and a thin REBCO film is formed by depositing multiple buffer layers on a thin metal substrate. Coated conductors fabricated on such a flat substrate have a structure close to a single crystal and have high critical current density properties. In contrast, reducing the screening current is an important issue for practical applications such as high-field superconducting coils. In this study, we proposed a patterned multi-filamentary thin film with a stripe pattern, fabricated on a substrate via photolithography. YBa2Cu3Ox was deposited onto stripe with Nb metal. Any stripe material can be used to separate superconducting and non-superconducting wires based on magneto-optical observations. Based on TEM/STEM-EDX observations, impurity phases such as NbBaO were formed on the STO/Nb strip. These results suggested that the use of a substrate with a stripe pattern is useful for fabricating multifilamentary coated conductors.

権利情報:

• In Copyright
  

  © 2024 IEEE. Personal use of this material is permitted. Permission from IEEE must be obtained for all other uses, in any current or future media, including reprinting/republishing this material for advertising or promotional purposes, creating new collective works, for resale or redistribution to servers or lists, or reuse of any copyrighted component of this work in other works.

キーワード: Multifilamentary superconductors

刊行年月日: 2024-02-16

出版者: Institute of Electrical and Electronics Engineers (IEEE)

掲載誌:

• IEEE Transactions on Applied Superconductivity (ISSN: 10518223) vol. 34 issue. 3 p. 1-4 7500404

研究助成金:

• Japan IKETANIZAIDAN

原稿種別: 著者最終稿 (Accepted manuscript)

MDR DOI: https://doi.org/10.48505/nims.4461

公開URL: https://doi.org/10.1109/tasc.2024.3366159

関連資料:

その他の識別子:

連絡先:

更新時刻: 2026-02-16 12:30:06 +0900

MDRでの公開時刻: 2026-02-16 09:51:51 +0900