High-aspect-ratio ZrB2 rod crystals were synthesized via a molten-salt-mediated boro/carbothermal reduction using ZrOCl2⋅8H2O/B4C/C as the raw material and NaCl as the flux material. This synthesis may improve the poor fracture toughness of monolithic ZrB2 ceramics. X-ray diffraction and scanning electron microscopy confirmed that the heat-treatment temperature of 1550 ◦C and the addition of 50 wt% NaCl were the most effective in the preparation of ZrB2 grains with a high aspect ratio. Thermogravimetric and differential scanning calorimetry was used to study the influence of NaCl addition, which increased the liquid-phase content. Finally, the growth of ZrB2 grains along the c-axis into rod-like morphology at elevated temperatures was investigated by transmission electron microscopy. This work revealed that the addition of NaCl has a positive effect on the reducing of synthesis temperature and increasing of products particle size.

権利情報:

• Creative Commons BY-NC-ND Attribution-NonCommercial-NoDerivs 4.0 International
  

キーワード: high aspect ratio, liquid phase, ZrB2 ceramics, ZrB2 rod crystals

刊行年月日: 2023-06-07

出版者: Elsevier BV

掲載誌:

• Ceramics International (ISSN: 02728842) vol. 49 issue. 17 p. 28030-28035

研究助成金:

• National Natural Science Foundation of China 52172075

原稿種別: 著者最終稿 (Accepted manuscript)

MDR DOI: https://doi.org/10.48505/nims.5180

公開URL: https://doi.org/10.1016/j.ceramint.2023.06.049