Deformation induced martensitic transformation during tensile or compressive deformation of the high-carbon bainitic steel (0.62wt%C-2.02%Si-0.23%Mn-1.01%Cr-Fe) was studied. The microstructure before the deformation was bainite with the retained austenite whose volume fraction was 35%. The tensile deformation is accompanied by more significant work hardening than that at the compression. This was due to the suppression of deformation induced martensitic transformation at the compression, which was confirmed mainly by the in situ neutron diffraction at TAKUMI, J-PARC. It was also found that the increasing lattice strain at austenite by tensile deformation retarded with the deformation-induced martensitic transformation, while this retardation was not found at the compression.

Rights:

• In Copyright
  

Keyword: high carbon steel, bainite, retained austenite, deformation-induced martensitic transformation, tension, compression, in-situ neutron diffraction

Date published: 2023-06-30

Publisher: Association for Iron & Steel Technology

Journal:

Conference:

Funding:

• JSPS 20H02488

Manuscript type: Publisher's version (Version of record)

MDR DOI:

First published URL: https://doi.org/10.33313/298/030

Related item:

Other identifier(s):

Contact agent:

Updated at: 2024-02-01 08:55:50 +0900

Published on MDR: 2024-01-30 12:30:18 +0900