Surface modification of Li3PO4 to Li1.3Al0.3Ti1.7(PO4)3 by wet chemical process and its sintering behavior

Kento Ishii; Yuri Taniguchi; Akira Miura; Shogo Miyoshi; Kazunori Takada; Go Kawamura; Hiroyuki Muto; Atsunori Matsuda; Masayoshi Fuji; Tetsuo Uchikoshi

doi:10.2109/jcersj2.23208

論文 Surface modification of Li₃PO₄ to Li_1.3Al_0.3Ti_1.7(PO₄)₃ by wet chemical process and its sintering behavior

Kento Ishii ; Yuri Taniguchi ; Akira Miura ; Shogo Miyoshi (National Institute for Materials Science) ; Kazunori Takada (National Institute for Materials Science) ; Go Kawamura ; Hiroyuki Muto ; Atsunori Matsuda ; Masayoshi Fuji ; Tetsuo Uchikoshi (National Institute for Materials Science)

Download file (3.9MB)
Download as zip (3.88MB)

コレクション

引用

Kento Ishii, Yuri Taniguchi, Akira Miura, Shogo Miyoshi, Kazunori Takada, Go Kawamura, Hiroyuki Muto, Atsunori Matsuda, Masayoshi Fuji, Tetsuo Uchikoshi. Surface modification of Li₃PO₄ to Li_1.3Al_0.3Ti_1.7(PO₄)₃ by wet chemical process and its sintering behavior. Journal of the Ceramic Society of Japan. 2024, 132 (6), 23208. https://doi.org/10.2109/jcersj2.23208

(BibTeX)

説明:

(abstract)

The surface modification of lithium phosphate on lithium alumina titanium phosphate (LATP) by a wet chemical method densified the LATP to over 90% at a sintering temperature of 800 °C. This temperature was approximately 300 °C lower than that of LATP without additives. Densification of LATP with lithium phosphate significantly progressed from 700°C to 800°C, and endothermic peaks corresponding to its melting were found in a similar temperature range, suggesting that the densification mechanism would be due to liquid phase sintering. The liquid phase of Li3PO4 is produced by a multi-step thermal decomposition involving the reaction with LATP. The sintered LATP with lithium phosphate showed a density of about 90% and the highest ionic conductivity of 3.5×10-4 S/cm at 25 °C, suggesting an excellent Li ion conducting, solid electrolyte material.