# Fileset

[1-13_dataset.xlsx](https://mdr.nims.go.jp/filesets/a16fd3fa-5839-4799-a69d-2ddef6162e83/download)

## Creator

Anton Bolyachkin, Srinithi Ashok Krishnaswamy

## Rights

[Creative Commons BY Attribution 4.0 International](https://creativecommons.org/licenses/by/4.0/)

## Other metadata

[Dataset of La(Fe,Si)13-based magnetocaloric alloys](https://mdr.nims.go.jp/datasets/d7b80863-6b14-41c2-ab01-8debc43945d5)

## Fulltext

1-13 dataset ID Article ID Article DOI Composition in the article Composition details Fe Si Al Ga Co V Cr Ni Cu Nb Mn P Zn Ca La Nd Ce Pr Dy Ho Gd Y Tb Er 1:13 Total H [or D] C N B Method Ann. Time (h) Ann. Temp. (K) NaZn13 (%) α-Fe (%) LaFeSi (%) La2Fe17 (%) La5Si3 (%) La-rich (%) La(OH)3 (%) Fe-O (%) La-O (%) vol./wt. [1/0] Total (%) a@PM (Å) a@FM (Å) Htr (T) Ttr (K) ΔThys (K) HS (T) |ΔSM|max (J/kg K)  T@|ΔSM|max (K) ΔSM FWHM (K) Had (T) |ΔTad|max (K) T@|ΔTad|max (K) Density (g/cm3) isoT/isoH [1/0] COMMENTS 1 2 10.1063/1.1375836 LaFe11.4Si1.6  81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1273  8        0 8 11.48 11.52 0.02 208 0 [1, 2, 5] [10.5, 14.3, 19.4] [209, 209, 213] [7.55, 11.6, 23.8] 2   LaFe10.4Si2.6  74.29 18.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1273            11.46 11.468 0.02 243 0 2 2.4 245 61.5 3 34 10.1103/PhysRevB.67.10441610.1063/1.1498148 La(FexSi(1-x))13 x = 0.87 80.79 12.07 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323              0.02 208  2 14        CL values, ∆Sm and ∆Tad vs ∆H for given T 4    x = 0.88 81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323              0.2 195 2 [1, 2, 3, 5] [18.6, 20, 21.2, 23] [195, 195, 195, 195] [4.6, 8.4, 12.7, 20.4] [1, 2, 3, 5] [3.9, 6.5, 7.7, 8.6] [195, 195, 194.8, 195] 5    x = 0.89 82.64 10.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323               188  [2, 5] [24, 26] [189, 189] [8.8, 20.8] [2, 5] [7.5, 10.7] [NaN, 188.9] 6    x = 0.90 83.57 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323               184  [2, 5] [28, 30] [184, 184] [8.9, 20.4] [2, 5] [8.1, 12.1] [NaN, 183.8] 7   La(Fe0.88Si0.12)13Hy y = 0.5 81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 3.57 0.00 0.00 0.00 arc_or_ind_melting 240 1323               233  [2, 5] [20, 24] [234, 236] [8.6, 18.9] [2, 5] [6, 10.7] [234, 234] 8    y = 1.0 81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 7.14 0.00 0.00 0.00 arc_or_ind_melting 240 1323               274  [2, 5] [19, 23] [277, 277] [8.6, 18.9] [2, 5] [6.2, 11.1] [277, 277.1] 9    y = 1.5 81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 10.71 0.00 0.00 0.00 arc_or_ind_melting 240 1323               323  [2, 5] [19, 23] [324, 324] [8.2, 18.1] [2, 5] [6.8, 12.6] [323, 324.2] 10   La(Fe0.89Si0.11)13H1.3  82.64 10.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 9.29 0.00 0.00 0.00 arc_or_ind_melting 240 1323               291  [2, 5] [24, 28]   [2, 5] [6.9, 12.8] 11   La(Fe0.9Si0.1)13H1.1  83.57 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 7.86 0.00 0.00 0.00 arc_or_ind_melting 240 1323               287  [2, 5] [28, 31]   [2, 5] [7.1, 15.4] 12 17 10.1109/TMAG.2011.2147774 La1.04Fe11.44Si1.56H1.63  81.48 11.11 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.41 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 11.61 0.00 0.00 0.00 melt_spinning                0 334 13   La1.04Fe11.44Si1.56H1.35  81.48 11.11 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.41 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 9.62 0.00 0.00 0.00 arc_or_ind_melting 240 1323              0 309 14   La1.04Fe11.44Si1.56H1.17  81.48 11.11 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.41 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 8.33 0.00 0.00 0.00 melt_spinning                0 295  1 12.1 295 5.3 15   LaFe(11.74-y)MnySi1.26Hz y = 0.390, z = 1.530 81.07 9.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.79 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 10.93 0.00 0.00 0.00 mech_alloying                   1.6 10.7 283 9.3 16    y = 0.373, z = 1.539 81.19 9.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.66 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 10.99 0.00 0.00 0.00 mech_alloying                   1.6 11 287 9.3 17    y = 0.356, z = 1.523 81.31 9.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.54 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 10.88 0.00 0.00 0.00 mech_alloying                   1.6 12.4 290 8.5 18    y = 0.338, z = 1.524 81.44 9.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.41 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 10.89 0.00 0.00 0.00 mech_alloying                   1.6 11.8 293 9 19    y = 0.322, z = 1.525 81.56 9.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.30 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 10.89 0.00 0.00 0.00 mech_alloying                   1.6 11.6 296 9.5 20 21 10.1088/0953-8984/19/23/236230 LaFe(11.7-x)CoxSi1.3 x = 0.0 83.57 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323            11.467   190  [2, 5] [NaN, 25.1]      7.3  RCP 21    x = 0.3 81.43 9.29 0.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323            11.469   223  [2, 5] [20, 24]      7.31 22    x = 0.4 80.71 9.29 0.00 0.00 2.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323            11.474   240  [2, 5] [12.3, 18.4]      7.3 23    x = 0.5 80.00 9.29 0.00 0.00 3.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323            11.475   253  [2, 5] [9.2, 15.5]      7.3 24    x = 0.6 79.29 9.29 0.00 0.00 4.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323            11.478   265  [2, 5] [8.7, 15]      7.3 25   LaFe(11.2-x)Co(0.7+x)Si1.1 x = 0.0 80.00 7.86 0.00 0.00 5.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323            11.476   270  [2, 5] [9.4, 16.5]      7.35 26    x = 0.1 79.29 7.86 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323            11.478   282  [2, 5] [8, 15]      7.35 27    x = 0.2 78.57 7.86 0.00 0.00 6.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323            11.477   294  [2, 5] [7.4, 13.5]      7.36 28 22 10.1016/j.jallcom.2014.02.015 LaFe(11.8-x)Si1.2Mnx x = 0.0 84.29 8.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1373 90 9.5 0.5       0 100    185.1  2 24 185 9.4 1.95 7 185   Cooling power 29    x = 0.1 83.57 8.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.71 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1373 88 11.5 0.5       0 100    175.2  2 20.5 175 11 1.95 6.2 175 30    x = 0.2 82.86 8.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.43 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1373 84 15.5 0.5       0 100    160.1  2 14.9 160 10.7 1.95 5.1 160 31    x = 0.3 82.14 8.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.14 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1373 83 16.5 0.5       0 100    146.4  2 10.6 146 14.5 1.95 3.8 146 32    x = 0.4 81.43 8.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.86 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1373 82.6 16.9 0.5       0 100    134.5  2 8.5 134 16.9 1.95 2.8 134 33   LaFe(11.6-x)Si1.4Mnx x = 0.0 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1323 95.6 3.9 0.5       0 100    198.1  2 20.2 198 9.9 1.95 6.2 198 34    x = 0.1 82.14 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.71 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1323 92 6 2       0 100    184.1  2 17 184 11.3 1.95 6.7 184 35    x = 0.2 81.43 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.43 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1323 90.5 8.5 1       0 100    173.1  2 14.7 173 11.8 1.95 5.3 173 36    x = 0.3 80.71 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.14 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1323 93.5 5 1.5       0 100    159.1  2 11.4 159 13.7 1.95 3.9 159 37    x = 0.4 80.00 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.86 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1323 92 6 2       0 100    143.2  2 5.4 143 27.1 1.95 2.8 143 38   LaFe(11.8-x)Si1.2MnxHy x = 0.0, y = 1.97 84.29 8.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 14.07 0.00 0.00 0.00 arc_or_ind_melting 168 1373               345.1  2 15.1 345.5 9.3 1.95 5.1 344 39    x = 0.1, y = 1.75 83.57 8.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.71 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.50 0.00 0.00 0.00 arc_or_ind_melting 168 1373               328.1  2 12.3 329.7 12.1 1.95 4.3 328.9 40    x = 0.2, y = 1.88 82.86 8.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.43 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 13.43 0.00 0.00 0.00 arc_or_ind_melting 168 1373               313.1  2 10.9 314.8 11.1 1.95 3.5 314 41    x = 0.3, y = 1.80 82.14 8.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.14 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.86 0.00 0.00 0.00 arc_or_ind_melting 168 1373               295.1  2 8.3 293.4 13.3 1.95 3.2 298 42    x = 0.4, y = 1.68 81.43 8.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.86 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.00 0.00 0.00 0.00 arc_or_ind_melting 168 1373               280.2  2 7.7 282.4 14.6 1.95 2.7 283.9 43   LaFe(11.6-x)Si1.4MnxHy x = 0.0, y = 1.90 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 13.57 0.00 0.00 0.00 arc_or_ind_melting 168 1323               337  2 15.6 338.7 10.1 1.95 4.8 337.9 44    x = 0.1, y = 1.81 82.14 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.71 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.93 0.00 0.00 0.00 arc_or_ind_melting 168 1323               324.1  2 11.9 325.7 11.4 1.95 4.1 324.1 45    x = 0.2, y = 1.87 81.43 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.43 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 13.36 0.00 0.00 0.00 arc_or_ind_melting 168 1323               307.1  2 10.1 308.6 12.7 1.95 3.5 307.5 46    x = 0.3, y = 1.77 80.71 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.14 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.64 0.00 0.00 0.00 arc_or_ind_melting 168 1323               293.3  2 8.2 294.6 15.4 1.95 3 293.4 47    x = 0.4, y = 1.78 80.00 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.86 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.71 0.00 0.00 0.00 arc_or_ind_melting 168 1323               278.1  2 7.3 279.8 17.5 1.95 2.8 277.9 48 29 10.1016/j.jmmm.2008.04.116 LaFe11.57Si1.43  82.64 10.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 1 1273 90.2 7.9 1.9       0 100 11.477  0.01 198 3 [2, 5] [11, 17.6] [194.9, 198.4] [7.3, 22.2]      Wheel speed 20 m/s 49     82.64 10.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 1 1273 93 5.7 1.3       0 100 11.481  0.01 210 0.4 [2, 5] [5.4, 14.2] [201.2, 207.2] [13, 26]      Wheel speed 40 m/s 50     82.64 10.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1273 82.2 12.9 4.9       0 100 11.475  0.01 192 6 [2, 5] [10.5, 19] [189.3, 192.6] [6.7, 21.9] 51   LaFe(13-x)Six x = 1.0 85.71 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 1 1273              0.01 185  [2, 5] [16.1, 26.6] [195.8, 201.1] [7.2, 22.8] 52    x = 1.2 84.29 8.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 1 1273 95.4 4.6        0 100 11.482  0.01 194.8 53    x = 1.4 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 1 1273              0.01 210  [2, 5] [4.7, 14.2] [221.5, 225.3] [16.9, 29.8] 54    x = 1.6 81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 1 1273              0.01 220 55    x = 1.8 80.00 12.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 1 1273              0.01 231.1  [2, 5] [3.5, 11.7] [235.4, 239.4] [26.7, 39.8] 56   LaFe(11.8-x)CoxSi1.2 x = 0.2 82.86 8.57 0.00 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 1 1323 87.5 10.1 2.4       0 100 11.483  0.01 222.2  5 22.2 219.3 23.5 57    x = 0.4 81.43 8.57 0.00 0.00 2.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 1 1323 90.2 8.2 1.6       0 100 11.486  0.01 247  5 18.1 246 28.5 58    x = 0.6 80.00 8.57 0.00 0.00 4.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 1 1323 87.8 10.1 2.1       0 100 11.487  0.01 267.2  5 17.3 264 29.3 59    x = 0.8 78.57 8.57 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 1 1323 86.3 11.8 1.9       0 100 11.49  0.01 290  5 12.8 289.8 35.6 60   LaFe11.57Si1.43Hx x = 0.8 82.64 10.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 5.71 0.00 0.00 0.00 arc_or_ind_melting 240 1323 94 6        0 100   0.01 237  5 16.3 240.3 31.9 61    x = 1.2 82.64 10.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 8.57 0.00 0.00 0.00 arc_or_ind_melting 240 1323 94 6        0 100   0.01 277  5 16.8 273.4 38.1 62    x = 2.3 82.64 10.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 16.43 0.00 0.00 0.00 arc_or_ind_melting 240 1323 94 6        0 100   0.01 348.3  5 17.2 342.6 22.2 63 5 10.1016/0304-8853(83)90128-2 LaFe11.5Si1.5  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1173              0.3 198 64   LaFe11.2Si1.8  80.00 12.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1173              0.3 211 65   LaFe11.1Si1.9  79.29 13.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1173              0.3 219 66   LaFe11Si2  78.57 14.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1173              0.3 230 67   LaFe10.9Si2.1  77.86 15.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1173              0.3 234 68   LaFe10.8Si2.2  77.14 15.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1173              0.3 245 69   LaFe10.5Si2.5  75.00 17.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1173              0.3 262 70 6 10.1002/adma.201000177 LaFe11.6Si1.4  82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1423 98.2 1.8        0 100      2 22.2 195  1.93 7.3 191.3 7.2 71   LaFe11.6Si1.4H1.6  82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 11.43 0.00 0.00 0.00 melt_spinning 2 1323 91 9        0 100          1.93 3.7 72 7 10.1103/PhysRevB.31.4622 La(FexAl(1-x))13 x = 0.46 42.71 0.00 50.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1173            11.922   53 73    x = 0.54 50.14 0.00 42.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1173            11.851   45 74    x = 0.58 53.86 0.00 39.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1173               42 75    x = 0.62 57.57 0.00 35.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1173            11.791   136 76    x = 0.65 60.36 0.00 32.50 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1173               199 77    x = 0.70 65.00 0.00 27.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1173            11.726   235 78    x = 0.73 67.79 0.00 25.07 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1173               249 79    x = 0.77 71.50 0.00 21.36 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1173            11.674   249 80    x = 0.80 74.29 0.00 18.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1173               227 81    x = 0.83 77.07 0.00 15.79 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1173            11.621   197 82    x = 0.84 78.00 0.00 14.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1173            11.619   194 83    x = 0.86 79.86 0.00 13.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1173               168 84    x = 0.87 80.79 0.00 12.07 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1173               187 85    x = 0.88 81.71 0.00 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1173            11.585   200 86    x = 0.89 82.64 0.00 10.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1173               207 87    x = 0.90 83.57 0.00 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1173            11.566   214 88    x = 0.91 84.50 0.00 8.36 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1173               221 89    x = 0.92 85.43 0.00 7.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1173            11.549   222 90 88-8 10.1063/1.291316610.1016/j.jmmm.2007.04.030 La(Fe0.92Co0.08)11.83Al1.17  77.74 0.00 8.36 0.00 6.76 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting                 303 91   LaFe10.8Si2.2  77.14 15.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting                 242 92   LaFe11Al2C0.5  78.57 0.00 14.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 3.57 0.00 0.00 arc_or_ind_melting                 291 93 9 10.1021/ja405161z LaFe(11.5-x)CoxSi1.5 x = 0.2 80.71 10.71 0.00 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1323              0.3 220 94    x = 0.4 79.29 10.71 0.00 0.00 2.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1323              0.3 242 95    x = 0.6 77.86 10.71 0.00 0.00 4.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1323              0.3 263 96    x = 0.8 76.43 10.71 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1323              0.3 288 97    x = 1.0 75.00 10.71 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1323              0.3 302 98 12 10.1098/rsta.2015.0308 LaFe11.74Co0.13Si1.13  83.86 8.07 0.00 0.00 0.93 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                    1.93 20.1 198.6 10.1 1.93 6.8 196.4 99   LaFe11.4Co0.52Si1.09  81.37 7.78 0.00 0.00 3.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                    1.93 16.7 238.8 8.5 1.93 4.2 238.1 100   LaFe11.05Co0.91Si1.04  78.93 7.43 0.00 0.00 6.50 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                    1.93 10.5 282.5 16.5 1.93 3.2 282.6 101   LaFe10.71Co1.3Si  76.45 7.14 0.00 0.00 9.28 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                    1.93 6.8 326.7 27.1 1.93 2.8 326.3 102   LaFe11.6-xMnxSi1.4 x = 0.0 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                    0    1.93 5.6 192.2 103    x = 0.1 82.14 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.71 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                    0    1.93 5.2 172.8 104    x = 0.2 81.43 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.43 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                    0    1.93 3.75 159.1 105    x = 0.3 80.71 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.14 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                    0    1.93 2.7 142.9 106   LaFe(11.6-x)MnxSi1.4Hy x = 0.27 80.93 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.93 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.86 0.00 0.00 0.00 mech_alloying                   1.93 4.9 306.5 10 1.93 4.6 305.5 107    x = 0.34 80.43 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.43 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.86 0.00 0.00 0.00 mech_alloying                   1.93 4.9 294.8 10 1.93 4.1 274.1 108    x = 0.39 80.07 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.79 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.86 0.00 0.00 0.00 mech_alloying                   1.93 3.9 284.7 10.5 1.93 4.1 284.7 109    x = 0.43 79.79 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 3.07 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.86 0.00 0.00 0.00 mech_alloying                   1.93 3.5 276.9 11.1 1.93 3.8 276.9 110 13 10.1016/j.actamat.2011.02.033 LaFe11.8Si1.2  84.29 8.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1273 37.8 42.6 19.6       1 100 111     84.29 8.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1323 82.4 10.5 7.1       1 100 112     84.29 8.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1373 90.8 6.8 2.3       1 100   0.05 185 5 [2, 5] [21.4, 24.3] [186.7, 193.4] [8.5, 20.2] 1.9 7.3 188 113     84.29 8.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1423 81.4 11.8 6.8       1 100   0.05 191 1.6 [2, 5] [15.4, 17.2] [189.5, 195.6] [9.4, 20.8] 114     84.29 8.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1473 68.1 23.1 8.9       1 100   0.05 202  [2, 5] [6.8, 8.9] [195.8, 198.7] [9.8, 20.5] 115   LaFe11.6Si1.4  82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1323 97.6 1.8 0.7       1 100      [2, 5] [19.2, 21.7] [195.6, 201.7] [9.8, 21.5] 1.9 7 195 116     82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 24 1373 54.4 30.5 15.1       1 100 117     82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 72 1373 64.2 25.2 10.6       1 100 118     82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 120 1373 66.0 28.4 5.7       1 100 119     82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 144 1373 97.6 1.8 0.7       1 100 120     82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 336 1373 95.7 2.9 1.4       1 100 121 14 10.1038/ncomms1606 LaFe11.33Co0.47Si1.2  80.93 8.57 0.00 0.00 3.36 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting              11.48  0 250           Barocaloric effect 122 15 10.1016/j.scriptamat.2012.05.039 LaFe11.6Si1.4  82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting   95          95   0.01 198 2 2 19.9 200.8 10.3      Resistivity, barocaloric effect 123     82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting                0.01 202 0.4 2 13.5 203 10.3 124   LaFe11.35Mn0.39Si1.26H1.53  81.07 9.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.79 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 10.93 0.00 0.00 0.00                        1.93  283.3 125   LaFe11.37Mn0.37Si1.26H1.54  81.21 9.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.64 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 11.00 0.00 0.00 0.00                        1.93 4.2 287.2 126   LaFe11.38Mn0.36Si1.26H1.52  81.29 9.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.57 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 10.86 0.00 0.00 0.00                        1.93 4.4 290 127   LaFe11.40Mn0.34Si1.26H1.52  81.43 9.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.43 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 10.86 0.00 0.00 0.00                        1.93 4.5 293.2 128   LaFe11.42Mn0.32Si1.26H1.53  81.57 9.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.29 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 10.93 0.00 0.00 0.00                        1.93 4.1 296.1 129   LaFe11.4Co0.52Si1.09  81.37 7.78 0.00 0.00 3.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  240         7.24 130 19 10.1063/1.1643774 La(Fe0.88Si0.12)13  81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323              0 195           Thermal diffusion 131   La(Fe0.88Si0.12)13H1  81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 7.14 0.00 0.00 0.00 arc_or_ind_melting 240 1323              0 274 132 23 10.1016/j.jallcom.2004.12.112 La(1-z)Cez(Fe0.88Si0.12)13 z = 0.0 81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323            11.468  0.4 197 0.85 [1, 2, 3, 4] [18.7, 20.2, 21.2, 22.1] [195.1, 195.2, 194.9, 194.9] [4.7, 8.5, 12.8, 16.9] [1, 2, 3, 4] [3.8, 6.5, 7.7, 7.9] [195, 195, 195, 195]   Critical field T dependance 133    z = 0.1 81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.43 0.00 0.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 336 1323            11.462  0.4 192 2 134    z = 0.2 81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 336 1373            11.457  0.4 184 2 135    z = 0.3 81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00  240 1423            11.452  0.4 176 1.8 [1, 2, 3, 4] [28.3, 29, 29.7, 30.4] [175.1, 175.1, 175, 176.3] [3.6, 8, 12.2, 15.9] [1, 2, 3, 4] [3.6, 7.4, 10.6, 12.2] [175, 174.9, 175.2, 175] 136 24 10.1103/PhysRevB.64.012409 La( Fe(1-x)Cox)11.83Al1.17 x = 0.06 79.43 0.00 8.36 0.00 5.07 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 1200 1273 100          100    273  [2, 5] [4.8, 9.5] [267.9, 272.1] [41.2, 55.3]      ΔS vs. H 137    x = 0.08 77.74 0.00 8.36 0.00 6.76 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 1200 1273 100          100    303  [2, 5] [4.5, 9] [302.7, 303.3] [44.9, 60.1] 138 25 10.1016/j.stam.2003.07.002 La(FexSi(1-x))13 x = 0.84 78.00 14.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323                 [2, 5] [2.1, 9] [237.3, 234.2] [36.9, 41.6] [2, 5] [2.1, 4.3] [233.6, 233.6]   Time dependence 139    x = 0.86 79.86 13.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323                 [2, 5] [8.8, 14.8] [214.7, 217.8] [18, 28.9] [2, 5] [3, 5.8] [215.9, 217.1] 140    x = 0.88 81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323                 [2, 5] [20.1, 23] [195.2, 204.1] [9.6, 21.5] [2, 5] [6.4, 7.9] [196, 200.2] 141    x = 0.90 83.57 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323                 [2, 5] [28, 30] [184.3, 192.9] [8.7, 20.4] [2, 5] [8.1, 11.1] [184, 187.8] 142   La(Fe0.9Si0.1)13H1.1  83.57 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 7.86 0.00 0.00 0.00 arc_or_ind_melting 240 1323                 [2, 5] [28, 31] [287, 287] [7, 17.2] [2, 5] [7.1, 15.4] [287, 287] 143 26 10.1016/j.jallcom.2005.04.022 La(Fe0.88Si0.12)13  81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323              0.3 195.5 1 2 20 194.2 9.6      RCP 144   La(Fe0.9Si0.1)13  83.57 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323               183  2 28 183.3 8.5 145   La(Fe0.88Si0.12)13Hy y = 0.5 81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 3.57 0.00 0.00 0.00 arc_or_ind_melting 240 1323                 2 19.6 233  2 6.1 233 146    y = 1.0 81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 7.14 0.00 0.00 0.00 arc_or_ind_melting 240 1323                 2 18.9 275  2 6.2 277 147    y = 1.5 81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 10.71 0.00 0.00 0.00 arc_or_ind_melting 240 1323                 2 19.1 322  2 6.6 325 148   La(Fe0.9Si0.1)13Hy y = 1.1 83.57 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 7.86 0.00 0.00 0.00 arc_or_ind_melting 240 1323                 2 27.8 286  2 7.2 287 149 27 10.1063/1.3276565 LaFe11.71Co0.193Si1.11  83.57 7.92 0.00 0.00 1.38 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  202  2 26.8 203 8.2      Time dependence 150   LaFe10.97Co1.03Si  78.36 7.14 0.00 0.00 7.36 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  293 151 30 10.1063/1.1847071 La(Fe1-xCox)11.9Si1.1 x = 0.04 81.60 7.86 0.00 0.00 3.40 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1323  5        0 5 11.477 11.551 0.01 243  [2, 5] [16.4, 22.9] [241.5, 245.6] [10.8, 22.1]      ΔTad vs H 152    x = 0.06 79.90 7.86 0.00 0.00 5.10 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1323  5        0 5 11.481 11.534 0.01 274  [2, 5] [12.3, 19.8] [271.2, 273.7] [14.9, 26.7] 1.1 2.4 271 153    x = 0.08 78.20 7.86 0.00 0.00 6.80 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1323  5        0 5 11.48 11.528 0.01 301  [2, 5] [8.8, 15.6] [298.5, 298.8] [16.6, 33.4] 154 32 10.1002/adma.200800955 LaFe11.6Si1.4  82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 1343 1392                 [1, 2, 5] [20.5, 23.4, 27] [189.3, 193, 189] [2.8, 8.3, 19.3] 155   La0.8Nd0.2Fe11.5Si1.5  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 1343 1392                 [1, 2, 5] [22.8, 24.1, 27.3] [190.5, 190.4, 190.5] [2.3, 3.2, 5.7] 156 34 10.1016/j.jallcom.2004.11.106 La(Fe0.88Si0.12)13Hy y = 0.0 81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323              0.5 195  [1, 2, 3, 4, 5] [18.3, 19.9, 21.1, 22.1, 22.8]  [4, 7.7, 12.1, 15.9, 19.8] [1, 2, 3, 4, 5] [3.9, 6.4, 7.6, 8.1, 8.5]    RCP 157    y = 1.1 81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 7.86 0.00 0.00 0.00 arc_or_ind_melting 240 1323              0.5 290           Time dependence 158    y = 1.6 81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 11.43 0.00 0.00 0.00 arc_or_ind_melting 240 1323              0.5 325           ΔTad  direct and indirect 159   La(0.89Si0.11)13Hy y = 0.0 82.64 10.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323                     2 5.4 189   (mistake in fig. 8) 160    y = 1.6 82.64 10.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 11.43 0.00 0.00 0.00 arc_or_ind_melting 240 1323                     2 4 321 161 37 10.1016/S0304-8853(03)00073-8 La(1-y)Ndy(Fe0.88Si0.12)13 y = 0.0 81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 144 1293            11.458  0.3 210  [2, 3, 4, 5] [4.7, 7.4, 9.8, 12.6] [210.8, 210.3, 210.6, 210.4] [19.9, 22.7, 23.8, 22.9] 162    y = 0.1 81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.43 0.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 144 1293            11.45  0.3 211 163    y = 0.3 81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 144 1293            11.426  0.3 215  [2, 3, 4, 5] [4.6, 6.3, 7.8, 9.7] [215.2, 215.2, 215.2, 215.4] [34.3, 37.8, 40.6, 41] 164    y = 0.4 81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 4.29 2.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 144 1293            11.419  0.3 204 165 38 10.1063/1.4868707 LaFe11.6Si1.4  82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1323                     1.9 7.8 166 39 10.1063/1.4865236 LaFe11.7Si1.3C0.2H1.8  83.57 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.86 1.43 0.00 0.00 arc_or_ind_melting 960 1373  4.5 1       0 5.5      2 11 325.3 12.4    7.08 167 41 10.1016/j.jmmm.2010.06.043 LaFe11.25Co0.65Si1.1 1 80.36 7.86 0.00 0.00 4.64 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00    89.8 5 3.5    1.7   0 100 11.495  0.01 255  [1, 1.4] [8.6, 10.7] [255.6, 255.4] [9, 10.2]    7.24  Vacuumschmelze sintering  168   LaFe11.14Co0.76Si1.1 2 79.57 7.86 0.00 0.00 5.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00    88 5.9 4.5    1.6   0 100 11.498  0.01 266  [1, 1.4] [7.03, 8.9] [265.6, 266.2] [11.4, 12.7] 1 1.8 267.7 7.24 169   LaFe11.05Co0.85Si1.1 3 78.93 7.86 0.00 0.00 6.07 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00    88.3 6.5 4.1    1.1   0 100 11.512  0.01 281  [1, 1.4] [6, 7.66] [279.4, 279.9] [14.3, 16.4]    7.24 170   LaFe10.92Co0.98Si1.1 4 78.00 7.86 0.00 0.00 7.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00    88 6.2 4.4    1.4   0 100 11.509 11.509 0.01 292  [1, 1.4] [4.96, 6.4] [290.6, 291.1] [17.2, 19.2] 1 1.1 292.2 7.24 171   LaFe10.77Co1.13Si1.1 5 76.93 7.86 0.00 0.00 8.07 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00    87.9 6.5 4.5    0.8 0.3  0 100  11.523 0.01 311  [1, 1.4] [4.17, 5.48] [306.7, 306.5] [22.9, 24.1]    7.21 172   LaFe10.61Co1.29Si1.1 6 75.79 7.86 0.00 0.00 9.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00    87.3 6.8 4.8    1.1   0 100  11.541 0.01 327  [1, 1.4] [3.83, 5.12] [325.8, 325.5] [24.5, 26.6]    7.2 173   LaFe10.45Co1.45Si1.1 7 74.64 7.86 0.00 0.00 10.36 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00    85.9 8.8 3.9    1.4   0 100  11.556 0.01 345  [1, 1.4] [3.4, 4.43] [342.9, 345.2] [28.2, 31.5]    7.21 174 42 10.1016/j.intermet.2011.06.005 La(Fe(1-x)Six)13 x = 0.108 82.83 10.03 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00               11.46 175 44 10.1002/aenm.201200297 LaFe11.6Si1.4  82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  197  2 18.4      7 176   LaFe 11.6 Si 1.4 H y   82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.86 0.00 0.00 0.00 arc_or_ind_melting 168 1323               330  2 10.3 329.4 12.2    5.3 177 51 10.1063/1.4928086 LaFe11.22Mn0.46Si1.32H1.65  80.14 9.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 3.29 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 11.79 0.00 0.00 0.00 arc_or_ind_melting  1323               269.7 0 [1, 1.5] [8.7, 10.2] [271.1, 271.3] [6.2, 8.4] 1.5 3.8    Cp values 178   LaFe11.33Mn0.37Si1.30H1.65   80.93 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.64 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 11.79 0.00 0.00 0.00 arc_or_ind_melting  1323               285.4 0.2 [1, 1.5] [11, 12.7] [286.8, 287.2] [5.2, 7.1] 1.5 4.4 179   LaFe11.41Mn0.30Si1.29H1.65  81.50 9.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.14 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 11.79 0.00 0.00 0.00 arc_or_ind_melting  1323               296.6 0.4 [1, 1.5] [11.4, 13.4] [297.5, 297.8] [4.9, 6.8] 1.5 4.4 180   LaFe11.47Mn0.25Si1.28H1.65  81.93 9.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.79 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 11.79 0.00 0.00 0.00 arc_or_ind_melting  1323               303.9 0.5 [1, 1.5] [14.1, 16.1] [305.3, 306] [3.9, 6] 1.5 4.4 181   LaFe11.55Mn0.22Si1.23H1.65  82.50 8.79 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.57 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 11.79 0.00 0.00 0.00 arc_or_ind_melting  1323               313.7 0.7 [1, 1.5] [14, 16] [314.9, 315.5] [4.3, 6.2] 1.5 4.4 182   LaFe11.60Mn0.18Si1.22H1.65  82.86 8.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.29 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 11.79 0.00 0.00 0.00 arc_or_ind_melting  1323               320.6 0.9 [1, 1.5] [14.2, 16.4] [322.1, 322.5] [3.6, 5.7] 1.5 4.2 183   LaFe11.66Mn0.14Si1.20H1.65  83.29 8.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 11.79 0.00 0.00 0.00 arc_or_ind_melting  1323               327.5 1.2 [1, 1.5] [14.1, 17.7] [328.9, 329.5] [3.3, 5.2] 1.5 3.8 184   LaFe11.76Mn0.06Si1.18H1.65  84.00 8.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.43 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 11.79 0.00 0.00 0.00 arc_or_ind_melting  1323               339 1.5 [1, 1.5] [13.9, 18.7] [340.5, 340.9] [3, 4.6] 1.5 3.4 185 55 10.1021/ic701311b LaFe11.7Si1.3  83.57 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1273            11.481   185           c, a parameters for t2 phase but FM/PM unknown, Fe-Fe length 186   LaFe11.1Si1.9  79.29 13.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1273               220 187   LaFe10.6Si2.4  75.71 17.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1273            11.456   240 188   LaFe13-xSix x = 1.7 80.71 12.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1273            11.469 189    x = 2.0 78.57 14.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1273            11.465 190    x = 2.5 75.00 17.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1273            11.444 191   LaFe10.9Al2.1  77.86 0.00 15.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  200 192   LaFe11.4Al1.6  81.43 0.00 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  204 193 64 10.1016/j.actamat.2017.01.054 LaFe11.38Mn0.32Si1.30Hx mono  81.29 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.29 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 11.43 0.00 0.00 0.00 mech_alloying    5        1 5      1.9 14.8 297 9.3 1.9 4.35 295 194    bi 81.29 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.29 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 11.43 0.00 0.00 0.00 mech_alloying    5        1 5      1.9 14.8 297 9.2 1.9 4.3 295 195 67 10.1016/j.jallcom.2008.07.139 LaFe11.6Si1.4  82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 1 1423 22.8 56.2 21       1 100 196     82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 1 1473 73.5 18.9 7.6       1 100 197     82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 1 1573 91.4 4.5 4.1       1 100    190  [2, 5] [13.2, 17.6] [192, 194] [10, 21.6] 198 76 10.1016/j.actamat.2016.12.014 LaFexSi1.4Hy x = 11.6, y = 1.68 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.00 0.00 0.00 0.00 arc_or_ind_melting 168 1323  1.1        1 1.1    334.5  2 19.3 337 8.9 1.93 5.2 334 6.99 199    x = 12.8, y = 1.72 84.21 9.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.58 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 11.32 0.00 0.00 0.00 arc_or_ind_melting 168 1323  6.4        1 6.4    335  2 19.8 336 9.4 1.93 5.2 335 7.1 200    x = 13.9, y = 1.80 85.28 8.59 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.13 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 11.04 0.00 0.00 0.00 arc_or_ind_melting 168 1323  15.5        1 15.5    336  2 18.6 339 8.7 1.93 5.2 334 7.11 201    x = 15.1, y = 1.88 86.29 8.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 10.74 0.00 0.00 0.00 arc_or_ind_melting 168 1323  21.6        1 21.6    338  2 14.0 341 10.1    7.14 202    x = 16.2, y = 1.95 87.10 7.53 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.38 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 10.48 0.00 0.00 0.00 arc_or_ind_melting 168 1323  23.7        1 23.7    339  2 12.7 340 9.8 1.93 4.7 334 7.17 203    x = 11.6, y = 0.00 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1323               192 204    x = 12.8, y = 0.00 84.21 9.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.58 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1323               189 205    x = 13.9, y = 0.00 85.28 8.59 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.13 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1323               188.9 206    x = 15.1, y = 0.00 86.29 8.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1323               188.9 207    x = 16.2, y = 0.00 87.10 7.53 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.38 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1323               185.4 208 82 10.1016/j.jmmm.2006.08.021 La(Fe0.9Si0.1)Bx x = 0.00 83.57 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 144 1173              0.1 199  1.6 19.2 199.0 7.8 209    x = 0.03 83.57 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.21 arc_or_ind_melting 144 1173              0.1 197  1.6 19.3 210    x = 0.06 83.57 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.43 arc_or_ind_melting 144 1173              0.1 194  1.6 20.1 197.1 6.7 211    x = 0.10 83.57 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.71 arc_or_ind_melting 144 1173              0.1 196  1.6 17.0 198.0 6.3 212    x = 0.20 83.57 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 1.43 arc_or_ind_melting 144 1173              0.1 199  1.6 19.0 202.0 7.9 213    x = 0.30 83.57 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 2.14 arc_or_ind_melting 144 1173              0.1 201  1.6 18.7 205.0 6.4 214    x = 0.50 83.57 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 3.57 arc_or_ind_melting 144 1173              0.1 207  1.6 9.9 211.0 8.5 215 83 10.1063/1.3072021 LaFe(13-x)Six x = 1.3 83.57 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1323                 5 28.5 192.0 20.0 216    x = 1.4 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1323                 5 26.8 195.5 18.8 217    x = 1.6 81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1323                 5 24.0 203.9 20.9 218    x = 1.7 80.71 12.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1323                 5 17.5 211.9 23.7 219    x = 1.8 80.00 12.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1323                 5 13.7 216.5 28.3 220    x = 2.2 77.14 15.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1323                 5 7.2 241.1 48.3 221   La(1-y)PryFe(13-x)Six x = 1.5, y = 0.5 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 3.57 0.00 0.00 3.57 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373                 5 28.0 189.2 19.6 222    x = 1.5, y = 0.0 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373                 5 22.5 201.6 20.6 223    x = 1.8, y = 0.3 80.00 12.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373                 5 19.3 206.5 23.1 224    x = 1.8, y = 0.0 80.00 12.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373                 5 12.1 218.7 24.0 225   La0.8Ce0.2Fe(11.7-z)CozSi1.3 z = 0.0 83.57 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373                 5 32.9 180.3 15.5 226    z = 0.4 80.71 9.29 0.00 0.00 2.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373                 5 26.0 226.9 19.3 227    z = 0.6 79.29 9.29 0.00 0.00 4.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373                 5 22.0 248.4 21.5 228    z = 0.8 77.86 9.29 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373                 5 15.3 269.9 26.5 229    z = 1.0 76.43 9.29 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373                 5 15.0 290.9 29.9 230    z = 1.2 75.00 9.29 0.00 0.00 8.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373                 5 13.1 313.7 43.1 231 84 10.1016/j.jallcom.2013.03.036 La(Fe0.89Si0.11)13  82.64 10.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 25 1323 54.4 26.3 19.3       1 100      1 16.8 187.0 3.9 232     82.64 10.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 50 1323 75.4 16 8.6       1 100      1 20.0 190.0 3.7 233     82.64 10.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 100 1323 98.9  1.1       1 100      1 23.3 192.1 4.0 234     82.64 10.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 200 1323 99.5  0.5       1 100      1 22.0 192.0 4.1 235     82.64 10.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 300 1323 99.7  0.3       1 100      1 23.1 192.0 5.0 236 85 10.1016/j.jmmm.2006.10.960 La0.3Pr0.7(Fe0.86Si0.14)13  79.86 13.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.14 0.00 0.00 5.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1423 100          100      5 22.4 197.9 20.6 237 86 10.1007/s10948-014-2515-2 La0.6Pr0.4Fe10.7Co0.8Si1.5  76.43 10.71 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 4.29 0.00 0.00 2.86 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                 0.5 269  [1, 2, 4, 5] [4.0, 7.4, 12.2, 14.2]  [24.1, 23.7, 27.7, 27.7]      H vs S, Tc vs Tpeak!, RCP 238   La0.5Pr0.5Fe10.7Co0.8Si1.5C0.2  76.43 10.71 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 3.57 0.00 0.00 3.57 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.43 0.00 0.00                    [2, 5] [5.8, 11.6] 239   La(Fe0.98Co0.02)11.7Al1.3  81.90 0.00 9.29 0.00 1.67 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                    5 10.6 240   La(Fe0.92Co0.08)11.9Si1.1  78.20 7.86 0.00 0.00 6.80 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                    5 15.6 241   LaFe11.2Co0.7Si1.1  80.00 7.86 0.00 0.00 5.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                    5 20.3 242   LaFe10.7Co0.8Si1.5  76.43 10.71 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                    [1, 2, 4, 5] [4.03, 7.1, 11.8, 13.5]  [25.6, 28.3, 31.3, 32.8] 243 88 10.1063/1.3675985 LaFe11.6Si1.4Cx x = 0.0 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1323 94.19 5.17 0.64       0 100 11.482  0.01 197.1 2 2 19.9 201 10.0 1.9 6.1 198.1 244    x = 0.1 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.71 0.00 0.00 arc_or_ind_melting 168 1323 95.49 3.87 0.64       0 100 11.498  0.01 214.3 0.4 2 19.6 216 9.5 1.9 5.4 216 245    x = 0.2 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.43 0.00 0.00 arc_or_ind_melting 168 1323 92.94 6.74 0.32       0 100 11.51  0.01 226.8 0 2 15.4 230 10.2 1.9 4.2 227.1 246    x = 0.3 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 2.14 0.00 0.00 arc_or_ind_melting 168 1323 88.48 11.20 0.32       0 100 11.522  0.01 242.5 0 2 9.8 244 14.4 1.9 3.9 240 247    x = 0.4 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 2.86 0.00 0.00 arc_or_ind_melting 168 1323 85.89 13.79 0.32       0 100 11.525  0.01 247.2 0 2 7.0 249 20.7 1.9 2.4 249.1 248 91 10.1007/s10948-013-2375-1 LaFe11.5Si1.5  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                    2 18.4 249 94 10.1016/j.actamat.2016.07.039 La(1+x)Fe11.6Si1.4 x = 0.0 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 24 1323 71.7 22.8 5.5  0.0     1 100 250    x = 0.2 81.69 9.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 8.45 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 24 1323 66.3 23.4 10.3  0.0     1 100 251    x = 0.5 80.00 9.66 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 10.34 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 24 1323 77.3 9.7 2.5  10.5     1 100 252    x = 0.7 78.91 9.52 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 11.56 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 24 1323 80.0 6.0 0.0  14.0     1 100      [1, 1.5, 2] [15.7, 16.1, 16.6] [176.4, 176.4, 179.5] [6.8, 10.8, 13.6] 253    x = 1.0 77.33 9.33 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 13.33 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 24 1323 72.5 6.7 0.0  20.8     1 100 254    x = 1.2 76.32 9.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 14.47 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 24 1323 62.2 15.5 0.0  22.3     1 100 255   La(1+x)Fe11.6Si1.4 x = 0.0 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 72 1323 76.3 13.2 10.5  0.0     1 100      [1, 1.5, 2] [13.8, 15.7, 16.6] [194.5, 194.6, 194.6] [5.9, 8.2, 10.7] 256    x = 0.2 81.69 9.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 8.45 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 72 1323 88.9 6.5 4.5  0.0     1 100      [1, 1.5, 2] [15.2, 15.6, 16.2] [176.6, 178, 179.6] [6.5, 9.7, 12.7] 257    x = 0.5 80.00 9.66 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 10.34 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 72 1323 84.9 5.6 2.6  6.8     1 100      [1, 1.5, 2] [14.9, 15.6, 16.2] [179.5, 179.6, 181.5] [6.6, 9.7, 12.3] 258    x = 0.7 78.91 9.52 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 11.56 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 72 1323 84.1 4.4 0.0  11.6     1 100      [1, 1.5, 2] [14.8, 15.0, 15.9] [174.9, 176.5, 178.4] [6.7, 9.8, 12.7] 259    x = 1.0 77.33 9.33 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 13.33 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 72 1323 80.8 2.9 0.0  16.3     1 100 260    x = 1.2 76.32 9.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 14.47 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 72 1323 51.1 23.7 0.0  25.2     1 100      [1, 1.5, 2] [4.5, 5.7, 7.1] [171.9, 174.7, 176.4] [11, 12.8, 14.1] 261   La(1+x)Fe11.6Si1.4 x = 0.0 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 120 1323 97.2 2.8 0.0  0.0     1 100 262    x = 0.2 81.69 9.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 8.45 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 120 1323 90.1 2.9 7.1  0.0     1 100 263    x = 0.5 80.00 9.66 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 10.34 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 120 1323 87.5 2.9 0.0  9.6     1 100 264    x = 0.7 78.91 9.52 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 11.56 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 120 1323 85.0 2.3 0.0  12.7     1 100      [1, 1.5, 2] [15.4, 14.9, 16.1] [173.4, 176.7, 179.1] [6.7, 10.7, 13] 265    x = 1.0 77.33 9.33 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 13.33 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 120 1323 80.3 1.9 0.0  17.8     1 100 266    x = 1.2 76.32 9.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 14.47 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 120 1323 55.2 26.7 0.0  18.1     1 100 267   La(1+x)Fe11.6Si1.4 x = 0.7 78.91 9.52 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 11.56 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 5 1323                 [1, 1.5, 2] [11.6, 12.5, 13.0] [173.6, 176.6, 177.2] [7.6, 14.2, 14.2] 268   La1.7Fe11.6Si1.4H2.9  78.91 9.52 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 11.56 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 20.71 0.00 0.00 0.00 arc_or_ind_melting 5 1323                 [1, 1.5, 2] [13.1, 14.8, 17.0] [344.5, 344.5, 347.5] [5.3, 7, 9.3] 269 95 10.7498/aps.65.217502 LaFe11.4Si1.6  81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 1200 1273              0.01 209  [2, 5] [14.3, 19.3] [207.6, 210.8] [12.1, 24.2] 270   LaFe10.98Co0.22Si1.8  78.43 12.86 0.00 0.00 1.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 1200 1273              0.01 242  [2, 5] [6.3, 11.5] [239.9, 242.5] [26.3, 37.7] 271   LaFe11.12Co0.71Al1.17  79.43 0.00 8.36 0.00 5.07 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 1200 1273              0.01 279  [2, 5] [4.6, 9.1] [276.2, 276.8] [47.2, 63.3] 272   La(Fe0.98Co0.02)11.7Al1.3  81.90 0.00 9.29 0.00 1.67 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  198  [2, 5] [5.9, 10.6] 273   LaFe11.2Co0.7Si1.1  80.00 7.86 0.00 0.00 5.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  274  5 20.3 274   LaFe11.5Si1.5H1.3  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 9.29 0.00 0.00 0.00                  288  [2, 5] [8.4, 17] 275   La(Fe(1-x)Mnx)11.7Si1.3Hy x = 0.01 82.74 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.84 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.86 0.00 0.00 0.00                  336  [2, 5] [16, 23.4]        These 3 samples considered to be fully hydrogenated 276    x = 0.02 81.90 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.67 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.86 0.00 0.00 0.00                  312  [2, 5] [13, 17.7] 277    x = 0.03 81.06 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.51 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.86 0.00 0.00 0.00                  287  [2, 5] [11, 15.9] 278   La(Fe(1-x)Cox)11.9Si1.1 x = 0.04 81.60 7.86 0.00 0.00 3.40 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  243  [2, 5] [16.4, 23] 279    x = 0.06 79.90 7.86 0.00 0.00 5.10 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  274  [2, 5] [12.2, 19.7] 280    x = 0.08 78.20 7.86 0.00 0.00 6.80 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  301  [2, 5] [8.7, 15.6] 281   La0.5Pr0.5Fe11.5Si1.5C0.3  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 3.57 0.00 0.00 3.57 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  211  [2, 5] [25.2, 27.6] 282   La0.7Nd0.3Fe10.7Co0.8Si1.5  76.43 10.71 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  280  [2, 5] [7.9, 15] 283   La0.5Pr0.5Fe10.7Co0.8Si1.5  76.43 10.71 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 3.57 0.00 0.00 3.57 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  272  [2, 5] [8.1, 14.6] 284   La0.5Pr0.5Fe10.5CoSi1.5  75.00 10.71 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 3.57 0.00 0.00 3.57 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  295  [2, 5] [6, 11.7] 285 99 10.1016/j.jmmm.2017.06.111 LaFe(11.8-x)CoxSi1.2 x = 0.52 80.57 8.57 0.00 0.00 3.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323 82         1 82 11.469   245.2  [1, 2, 4, 5] [3.4, 6.1, 9.6, 10.8] [244.6, 244.9, 244.6, 245.2] [18.9, 21, 27.3, 30.4]      RCP3T data is available 286    x = 0.66 79.57 8.57 0.00 0.00 4.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323 94         1 94 11.476   262.4  [1, 2, 4, 5] [6.3, 10.3, 14.6, 16.25] [260, 260.3, 260.4, 263.4] [13, 15.8, 23.7, 26.9] 287    x = 0.80 78.57 8.57 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323 88         1 88 11.482   273.4  [1, 2, 4, 5] [3.9, 6.7, 11.3, 12.95] [274.6, 274.9, 279.8, 280] [19, 22.7, 28, 30.7] 288    x = 0.94 77.57 8.57 0.00 0.00 6.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323 92         1 92 11.487   289  [1, 2, 4, 5] [3.6, 6.3, 10.2, 11.7] [294.8, 294.7, 295.3, 296.8] [22.1, 25.6, 32.9, 36.5] 289    x = 1.08 76.57 8.57 0.00 0.00 7.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323 92         1 92  11.502  304  [1, 2, 4, 5] [3.2, 5.9, 10, 11.6] [307.5, 309.9, 310.4, 310.5] [24.3, 28.6, 34.9, 38.6] 290 100 10.1016/j.jmmm.2009.10.042 LaFe11.5Si1.5Bx x = 0.0 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting   95.8 0 4.2       1 100 11.47  0.05 183  5 21.3 190.9 22.1      Fe2B phase? 291 103 10310.1063/1.4933261 LaFe11Co0.8Si1.2  78.57 8.57 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting  1323  6.5        1 6.5      2 7.7 283.5 23.7 1.5 2.2 287 7.3 292   LaFe12.1Co0.8Si1.2  80.13 7.95 0.00 0.00 5.30 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.62 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting  1323  14.4        1 14.4      2 7.9 277.5 22 1.5 2.1 279 7.36 293   LaFe13.2Co0.8Si1.2  81.48 7.41 0.00 0.00 4.94 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.17 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting  1323  20.8        1 20.8      2 7.6 271.6 22.15 1.5 2 275 7.39 294   LaFe14.3Co0.8Si1.2  82.66 6.94 0.00 0.00 4.62 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.78 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting  1323  31.5        1 31.5      2 6.7 268.5 22.35 1.5 2 271 7.44 295 104 10.1109/20.951162 LaFe11.44Al1.56  81.71 0.00 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1273  6        0 6   0.01 127  [0.6, 1, 2] [2.6, 3, 3.7] [127.9, 128.2, 144.3] [17.6, 31.9, 52.3] 296 105 10.1016/j.jmmm.2009.10.043 LaFe11.4Si1.6  81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1273 70          70 11.52  0.1 211  5 15 213.5 25.3 297   La(Fe0.99Z0.01)11.4Si1.6 Z = V 80.61 11.43 0.00 0.00 0.00 0.81 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1273 60          60 11.47  0.1 223  [1, 2, 3, 4, 5] [2.2, 4, 5.5, 6.8, 7.8] [219.3, 220.4, 221.5, 222.1, 223.9] [23.9, 30.4, 33.4, 36.9, 40.5] 298    Z = Cr 80.61 11.43 0.00 0.00 0.00 0.00 0.81 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1273 68          68 11.54  0.1 212  5 10 214 28.8 299    Z = Ni 80.61 11.43 0.00 0.00 0.00 0.00 0.00 0.81 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1273 63          63 11.48  0.1 217  5 12 217.7 31.7 300    Z = Cu 80.61 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.81 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1273 62          62 11.49  0.1 221  5 10 222.5 35.2 301 110 10.1016/j.jallcom.2012.01.042 La0.7Pr0.3Fe11.5Si1.5  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 336 1223              0.01 189 4          RCP 302   La0.7Pr0.3Fe11.5Si1.5C0.2Hx x = 0.0 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.43 0.00 0.00 arc_or_ind_melting 336 1223              0.01 210 0.5 [2, 5] [25.6, 28.1] [211.6, 214.6] [7.9, 19.8] 303    x = 0.6 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 100.00 4.29 1.43 0.00 0.00 arc_or_ind_melting 336 1223              0.01 271 0 [2, 5] [19.2, 24.7] [270.6, 272.5] [9.7, 20.7] 304    x = 1.2 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 100.00 8.57 1.43 0.00 0.00 arc_or_ind_melting 336 1223              0.01 321 0 [2, 5] [17.1, 22.1] [322.7, 323.4] [10.1, 20.7] 305 114 10.1063/1.3172927 LaFe11Co0.9Si1.1  78.57 7.86 0.00 0.00 6.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 336 1323                 [1, 2, 4, 5] [4.2, 7.4, 11.8, 13.4] [293.1, 295.1, 295.2, 295.2]  1.48 1.5 294   Non-adiabatic 306   LaFe11.1Co0.8Si1.1  79.29 7.86 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 336 1323                 [1, 2, 4, 5] [4.6, 8, 13.1, 14.9] [280.9, 281.9, 283.1, 283.2] [14.6, 19, 25.4, 26.9] 307 118 10.1063/1.2227631 La(Fe0.89Si0.11)13   82.64 10.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting                0.4 188  2 24 189.4 9 2 7.5 189   RCP 308   La(Fe0.87Mn0.02Si0.11)13  80.79 10.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.86 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting                0.4 150  2 16 152.2 10.3 2 5.7 149.5 309   La0.7Ce0.3(Fe0.87Mn0.02Si0.11)13  80.79 10.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.86 0.00 0.00 0.00 5.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting                0.4 105  2 19 110 12.3 2 6.7 108 310   La0.65Ce0.35(Fe0.860Mn0.025Si0.115)13  79.86 10.68 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.32 0.00 0.00 0.00 4.64 0.00 2.50 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting                0.4 83  2 15 89.1 14.8 2 4.5 84.5 311   La0.65Ce0.35(Fe0.85Mn0.03Si0.12)13  78.93 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.79 0.00 0.00 0.00 4.64 0.00 2.50 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting                0.4 60  2 12 67.8 18.1 2 4.4 312   La0.75Ce0.25(Fe0.850Mn0.035Si0.115)13  78.93 10.68 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 3.25 0.00 0.00 0.00 5.36 0.00 1.79 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting                   2 6 33.4 34.9 2 6.2 313 119 10.1016/j.jmmm.2006.10.962 La(Fe0.88Si0.12)13Hy y = 0.0 81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323               196.9           RCP 314    y = 0.5 81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 3.57 0.00 0.00 0.00 arc_or_ind_melting 240 1323               235.3 315    y = 1.0 81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 7.14 0.00 0.00 0.00 arc_or_ind_melting 240 1323               276.9 316    y = 1.5 81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 10.71 0.00 0.00 0.00 arc_or_ind_melting 240 1323               325.16 317   La(1-z)Cez(Fe0.88Si0.12)13 z = 0.1 81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.43 0.00 0.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323               192.9 318    z = 0.2 81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323               183.9 319    z = 0.3 81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323               176.2 320 120 10.1016/j.jallcom.2007.09.064 LaFe11.2Si1.8  80.00 12.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373 100          100 11.462  0.01 216  [1, 2, 4, 5] [4, 7.7,12.2, 13.2] [214.4, 215.9, 215.9, 219.1] [14.2, 18.1, 25.3, 30.2] 321   La0.7Pr0.3Fe11.2Si1.8  80.00 12.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373 100          100 11.451  0.01 203 0.3 [1, 2, 4, 5] [10.9, 14.4, 18.1, 19.4] [202.1, 204, 205.9, 206] [6.4, 11.2, 19, 23] 322   La0.7Pr0.3Fe10.4Co0.8Si1.8  74.29 12.86 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373 100          100 11.453  0.01 290  [1, 2, 4, 5] [2.6, 4.6, 7.9, 9.3] [285.9, 286.4, 287, 287.2] [31.4, 38.3, 45.8, 49.1] 323 124 10.1016/j.actamat.2018.08.054 LaFe11.6Si1.4  82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 suction_casting 3 1323 97.9 0.2 1.9       0 100 11.4904  0.05 194.2  1.9 19.1 196.1 9 1.9 6.2 194.1 324   LaFe11.5Ni0.1Si1.4  82.14 10.00 0.00 0.00 0.00 0.00 0.00 0.71 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 suction_casting 3 1323 96.8 0.9 2.3       0 100 11.4918  0.05 193.6  1.9 19 193.5 8.4 1.9 4.4 194.1 325   LaFe11.4Ni0.2Si1.4  81.43 10.00 0.00 0.00 0.00 0.00 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 suction_casting 3 1323 96.2 3.8 0       0 100 11.488  0.05 197.9  1.9 12 199 10.5 1.9 3.5 197.3 326   LaFe11.3Ni0.3Si1.4  80.71 10.00 0.00 0.00 0.00 0.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 suction_casting 3 1323 84.9 14.2 0.9       0 100 11.488  0.05 205.4  1.9 8.4 203.8 13.7 1.9 2.7 204.4 327   LaFe11.2Ni0.4Si1.4  80.00 10.00 0.00 0.00 0.00 0.00 0.00 2.86 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 suction_casting 3 1323 77.6 21.3 1.1       0 100 11.486  0.05 214  1.9 4.3 213.3 25.1 1.9 1.8 214.1 328 126 10.1007/s11433-013-5357-1 LaFe11.5Si1.5Hy y = 0.0 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                    5 24.1 199.1 21.5      Hysteresis 329    y = 0.3 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 2.14 0.00 0.00 0.00                    5 17.3 229 29 330    y = 0.6 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 4.29 0.00 0.00 0.00                    5 17.8 258.6 26.7 331    y = 0.9 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 6.43 0.00 0.00 0.00                    5 16.5 272 29.6 332    y = 1.3 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 9.29 0.00 0.00 0.00                    5 16.8 288.8 29.6 333    y = 1.5 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 10.71 0.00 0.00 0.00                    5 16.6 313 25.7 334    y = 1.8 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.86 0.00 0.00 0.00                    5 20.4 340.9 21.2 335   La(Fe(1-x)Mnx)11.7Si1.3Hy x = 0.01 82.74 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.84 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.86 0.00 0.00 0.00                    2 15.9 331.2 10.2      These 3 samples considered to be fully hydrogenated 336    x = 0.02 81.90 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.67 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.86 0.00 0.00 0.00                    2 13 309 10.8 337    x = 0.03 81.06 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.51 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.86 0.00 0.00 0.00                    2 10.9 282.9 12.2 338   La0.5Pr0.5Fe11.4Si1.6Hx x = 0.0 81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 3.57 0.00 0.00 3.57 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                    [2, 5] [22.8, 26.2] [191.4, 197.1] [9.1, 20.7] 339    x = 0.9 81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 3.57 0.00 0.00 3.57 0.00 0.00 0.00 0.00 0.00 0.00 100.00 6.43 0.00 0.00 0.00                    [2, 5] [21.9, 26.3] [262.4, 262.1] [7.6, 18.7] 340    x = 1.6 81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 3.57 0.00 0.00 3.57 0.00 0.00 0.00 0.00 0.00 0.00 100.00 11.43 0.00 0.00 0.00                    [2, 5] [17.5, 22] [318.9, 321.1] [8.1, 18.7] 341   LaFe11.6 Si1.4Cx x = 0.00 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                    5 23.9 200.6 18 342    x = 0.02 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.14 0.00 0.00                    5 24.1 221.8 18 343    x = 0.40 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 2.86 0.00 0.00                    5 18.2 239.8 22.2 344    x = 0.60 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 4.29 0.00 0.00                    5 12.1 251.4 29.4 345   La0.5Pr0.5 Fe11.5Si1.5Cx x = 0.0 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 3.57 0.00 0.00 3.57 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                    [2, 5] [30.5, 32.8] [182.6, 189.3] [5.8, 19.3] 346    x = 0.3 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 3.57 0.00 0.00 3.57 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 2.14 0.00 0.00                    [2, 5] [21.2, 25.3] [211.5, 214.8] [9.3, 21] 347   La1-xCex Fe11.5Si1.5Cy x = 0.0, y = 0.0 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                    5 23.1 204.6 19.6 348    x = 0.1, y = 0.0 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.43 0.00 0.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                    5 26.5 194.9 20 349    x = 0.2, y = 0.0 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                    5 30.2 186.8 15.2 350    x = 0.2, y = 0.2 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.43 0.00 0.00                    5 27.1 211.6 18.9 351    x = 0.2, y = 0.4 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 2.86 0.00 0.00                    5 13.3 246.4 30.4 352   LaFe11.7 Si1.3  83.57 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                    [2, 5] [22.8, 27.3] [194.3, 199.5] [7.3, 18.9] 353   LaFe11.7Si1.3C0.2  83.57 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.43 0.00 0.00                    [2, 5] [17.8, 23.5] [215.4, 218.7] [9.2, 19.9] 354   LaFe11.7Si1.3C0.2H1.7  83.57 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.14 1.43 0.00 0.00                    [2, 5] [13.8, 18.6] [320.9, 324.1] [11.6, 22.8] 355 130 10.1016/j.jallcom.2004.09.021 La(1-x)NdxFe11.5Si1.5 x = 0.0 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 5 1300              0.1 186  1 11 188 8.1 356    x = 0.3 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 5 1300              0.1 192  1 12.7 192 6.1 357    x = 0.5 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 3.57 3.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 5 1300              0.1 196  1 7.1 197 9.1 358 132 10.1109/TMAG.2005.854775 La(Fe0.86Si0.14)13  79.86 13.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323                 2 8.9 215.2 17.9 2 3 215.9   RCP, hysteresis loss 359   La(Fe0.88Si0.12)13  81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323                 2 20.2 194.9 8.4 2 6.4 196.1 360   La0.7Ce0.3(Fe0.86Si0.14)13  79.86 13.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1423                 2 18 191.1 8.7 2 6.4 189.1 361 133 10.1016/j.jallcom.2010.11.144 LaFe11.6Si1.4Bx x = 0.1 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.71 arc_or_ind_melting              11.465  0.02 190.6 3.4 2 15.4 191.2 6.2 362    x = 0.2 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 1.43 arc_or_ind_melting 363    x = 0.3 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 2.14 arc_or_ind_melting              11.466  0.02 193.3 3.2 2 13.5 193.1 7.2 364    x = 0.4 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 2.86 arc_or_ind_melting 365    x = 0.5 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 3.57 arc_or_ind_melting              11.468  0.02 198.3 1.6 2 11.2 198.1 9.6 366 138 10.1016/j.jmmm.2008.03.004 La0.8Ce0.2Fe(11.4-x)CoxSi1.6 x = 0.0 81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 50 1373              0.05 184  [1, 2, 5] [16.9, 23.2, 24.2] [183.7, 183.6, 183.6] [3.4, 7.1, 19.3]      Mistake in the legend of Fig. 5b 367    x = 0.2 80.00 11.43 0.00 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 50 1373              0.05 208  [1, 2, 5] [14.6, 17.7, 19.3] [213.7, 213.6, 213.6] [4.4, 9.9, 13.1] 368    x = 0.4 78.57 11.43 0.00 0.00 2.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 50 1373              0.05 224  [1, 1.5] [12.5, 14.6] [223, 223.3] [5.4, 7.5] 369    x = 0.6 77.14 11.43 0.00 0.00 4.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 50 1373              0.05 252  [1, 1.5] [5.4, 7.5] [248.6, 248.4] [12.9, 15.1] 370    x = 0.8 75.71 11.43 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 50 1373              0.05 272  [1, 1.5] [3.8, 5.4] [271.5, 271.4] [20.2, 22.1] 371    x = 1.0 74.29 11.43 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 50 1373              0.05 294  [1, 1.5] [3.3, 4.7] [292.5, 292.4] [21, 25.6] 372 139 10.1063/1.2803658 LaFe11.4Si1.6  81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 suction_casting  1250               195  5 18  18 373   La0.95Gd0.05Fe11.4Si1.6  81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.79 0.00 0.00 0.00 0.00 0.00 0.36 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 suction_casting  1250               215  5 7  30 374   La0.95Y0.05Fe11.4Si1.6  81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.79 0.00 0.00 0.00 0.00 0.00 0.00 0.36 0.00 0.00 100.00 0.00 0.00 0.00 0.00 suction_casting  1250               226  5 18  30 375 140 10.1016/j.actamat.2019.06.022 LaFe(11.6-x)CrxSi1.4 x = 0.00 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 suction_casting 48  100 0        0 100 11.478  0.05 188.3 1.9 1.9 22.4 191.1 9.3 1.9 6.9 188.1   RCP, hysteresis loss 376    x = 0.12 82.00 10.00 0.00 0.00 0.00 0.00 0.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 suction_casting 48 1379 100 0        0 100 11.476  0.05 188.7 2.3 1.9 21.4 189.7 9.2 1.9 6.6 187 377    x = 0.21 81.36 10.00 0.00 0.00 0.00 0.00 1.50 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 suction_casting 48 1386 97.7 2.3        0 100 11.478  0.05 184 4 1.9 21.1 184.9 9.9 1.9 6.2 183.3 378    x = 0.35 80.36 10.00 0.00 0.00 0.00 0.00 2.50 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 suction_casting 48 1398 94.9 5.1        0 100 11.477  0.05 178.9 2.6 1.9 17 180.1 9.9 1.9 5.8 180.1 379    x = 0.42 79.86 10.00 0.00 0.00 0.00 0.00 3.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 suction_casting 48 1423 92.8 7.2        0 100 11.475  0.05 175.3 0.4 1.9 14.9 179 10.2 1.9 4.6 178 380    x = 0.47 79.50 10.00 0.00 0.00 0.00 0.00 3.36 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 suction_casting 48 1423 87.5 12.5        0 100 11.477  0.05 173 0.4 1.9 11.5 175.1 10.3 1.9 3.25 174 381    x = 0.56 78.86 10.00 0.00 0.00 0.00 0.00 4.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 suction_casting 48 1423 75.5 24.5        0 100 11.476  0.05 170 0 1.9 6.7 172.1 14.1 1.9 2.2 172 382 141 10.1016/j.intermet.2012.12.013 La0.7Pr0.3Fe11.4Si1.6  81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 336 1323 69.1 19.4 11.5       0 100 11.451  0.01 210  [1, 2, 4, 5] [2.1, 3.9, 6, 7] [207.5, 207.6, 209.4, 211.1] [16.8, 20.6, NaN, NaN]      RCP, hysteresis loss 383   La0.7Pr0.3Fe11.4Si1.6  81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 4 1523 96.1 3.5 0.4       0 100 11.459  0.01 197  [1, 2, 4, 5] [7.2, 11.8, 15.9, 17] [198, 198, 201.9, 203.1] [9.4, 12.3, 20.4, 22.7] 384   La0.7Pr0.3Fe11.34Cu0.06Si1.6  81.00 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.43 0.00 0.00 0.00 0.00 0.00 5.00 0.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 4 1523 91.7 7.3 1       0 100 11.46  0.01 210  5 12 210.2 27.2 385   La0.7Pr0.3Fe11.28Cu0.12Si1.6  80.57 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.86 0.00 0.00 0.00 0.00 0.00 5.00 0.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 4 1523 88.2 9.1 2.7       0 100 11.463  0.01 218  5 9 386   La0.7Pr0.3Fe11.17Cu0.23Si1.6  79.79 11.43 0.00 0.00 0.00 0.00 0.00 0.00 1.64 0.00 0.00 0.00 0.00 0.00 5.00 0.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 4 1523 86.8 10.2 3       0 100 11.465  0.01 224  5 7 387   La0.7Pr0.3Fe11.06Cu0.34Si1.6  79.00 11.43 0.00 0.00 0.00 0.00 0.00 0.00 2.43 0.00 0.00 0.00 0.00 0.00 5.00 0.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 4 1523 85.2 10.6 4.2       0 100 11.466  0.01 230  5 5 229.6 54.9 388 143 10.1063/1.2203389 La(Fe(1−x)Cox)11.44Al1.56 x = 0.00 81.71 0.00 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1170              0.01 206  5 2.2 205.3 47.5 389    x = 0.04 78.45 0.00 11.14 0.00 3.27 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1170              0.01 250  5 5.5 249.9 77.7 390    x = 0.08 75.18 0.00 11.14 0.00 6.54 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1170              0.01 320  5 4.65 320.9 104.9 391    x = 0.12 71.91 0.00 11.14 0.00 9.81 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1170              0.01 370  5 4.75 369.6 392 145 10.1016/j.jallcom.2015.02.131 La0.9Ce0.1Fe11.7Si1.3H1.8  83.57 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.43 0.00 0.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.86 0.00 0.00 0.00 arc_or_ind_melting 144 1373              0.05 329  1.5 11.4 334.4 9.3 393   La0.9Ce0.1Fe11.41Mn0.29Si1.3H1.8  81.50 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.07 0.00 0.00 0.00 6.43 0.00 0.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.86 0.00 0.00 0.00 arc_or_ind_melting 144 1373              0.05 283  1.5 10.4 281 8.9 394   LaFe10.99Co0.91Si1.1B0.2  78.50 7.86 0.00 0.00 6.50 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 1.43                    1.5 5.1 294 23.5 1.5 2.2 293 395 151 10.2320/matertrans.47.482 La(Fe(0.88-y)CrySi0.12)13 y = 0.00 81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323              0.01 195.2  4 21.2 200.7 17      Thys at 1T  396    y = 0.01 80.79 11.14 0.00 0.00 0.00 0.00 0.93 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323              0.01 194.1 397    y = 0.02 79.86 11.14 0.00 0.00 0.00 0.00 1.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323              0.01 186  4 20.7 189.7 17.5 398   La(Fe(0.88-y)MnySi0.12)13 y = 0.01 80.79 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.93 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323              0.01 179.9 0 399    y = 0.02 79.86 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.86 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323              0.01 158 0 4 15.2 163.4 21.7 400    y = 0.03 78.93 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.79 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323              0.01 135.8 0 4 11 142.1 29.7 401   La(Fe(0.87-y)NiySi0.13)13 y = 0.00 80.79 12.07 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323              0.01 203.8 402    y = 0.01 79.86 12.07 0.00 0.00 0.00 0.00 0.00 0.93 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323              0.01 206 403    y = 0.02 78.93 12.07 0.00 0.00 0.00 0.00 0.00 1.86 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323              0.01 211.9 404   La0.65Ce0.35(Fe0.85Mn0.03Si0.12)13  78.93 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.79 0.00 0.00 0.00 4.64 0.00 2.50 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 336 1423              1 68 6.5 4 12 75.9 35.6 405 155 10.1016/j.jmmm.2009.02.027 La0.7Pr0.3Fe(13-x)Six x = 1.5 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373              0.01 185.5  [2, 5] [25, 28] [184, 190.9] [7.6, 20.5]      RCP, hysteresis loss 406    x = 1.6 81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373              0.01 190.1  [2, 5] [21.3, 22.7] [192.4, 198.5] [6.8, 20.2] 407    x = 1.8 80.00 12.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373              0.01 204.2  [2, 5] [14.4, 19.3] [204.4, 206.7] [11.2, 23.3] 408    x = 2.0 78.57 14.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 96 1373              0.01 218.3  [2, 5] [6.3, 11.5] [222.3, 224] [28.3, 41] 409 156 10.1016/j.jmmm.2011.05.041 La0.8Ce0.2Fe(11.5-x)CoxSi1.5 x = 0.0 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting                0.02 180.1 3 2 25 178.6 3.4 410    x = 0.1 81.43 10.71 0.00 0.00 0.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting                0.02 193.8 3.2 2 18.6 190.9 4.1 411    x = 0.3 80.00 10.71 0.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting                0.02 215.6 2 2 10.1 216.1 8.8 412    x = 0.5 78.57 10.71 0.00 0.00 3.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting                0.02 240.3 1.2 2 6.75 237 10.5 413    x = 0.7 77.14 10.71 0.00 0.00 5.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting                0.02 265.8 0.2 2 6.5 259.4 22.7 414 165 10.12693/aphyspola.127.576 LaFe11.14Co0.66Si(1.2-x)Alx x = 0.1 79.57 7.86 0.71 0.00 4.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323 87 13        1 100 11.48  0.01 264  [1, 2] [1.3, 3.2] [265.2, 265.2] [15.8, 19.1] 415    x = 0.2 79.57 7.14 1.43 0.00 4.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323 91 9        1 100 11.486  0.01 265  [1, 2] [1.2, 2.8] [263.3, 263.2] [16.9, 17.8] 416    x = 0.3 79.57 6.43 2.14 0.00 4.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323 96 4        1 100 11.489  0.01 266.5  [1, 2] [1, 2.5] [265.5, 265.6] [17.3, 19.9] 417 170 10.1016/j.jmmm.2011.08.028 La(1-x)CexFe11.5Si1.5Cy x = 0.0, y = 0.0 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1373            11.468  0.01 195 2 [2, 5] [19.7, 23.7] [199.8, 203.7] [8.5, 19.8]      RCP, hysteresis loss 418    x = 0.1, y = 0.0 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.43 0.00 0.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1373            11.462  0.01 188  [2, 5] [22.7, 26.6] [189.9, 194.9] [8.5, 20.1] 419    x = 0.2, y = 0.0 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1373  0          11.454  0.01 179 6 [2, 5] [26.7, 30.4] [183.5, 187.1] [8.8, 15.3] 420    x = 0.2, y = 0.2 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.43 0.00 0.00 arc_or_ind_melting 720 1373  0          11.482  0.01 207  [2, 5] [24.6, 28] [208.4, 211.6] [8.5, 18.8] 421    x = 0.2, y = 0.4 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 2.86 0.00 0.00 arc_or_ind_melting 720 1373  5        0 5 11.512  0.01 246 0 [2, 5] [7.6, 13.5] [245.3, 247] [19.7, 30.2] 422 176 10.1016/j.jmmm.2016.08.068 LaFe(11.14-x)Co0.66NixSi1.2 x = 0.1 78.86 8.57 0.00 0.00 4.71 0.00 0.00 0.71 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 320 1323 85 14    1    1 100 11.479 11.499 0.25 272.5  [1, 2, 3] [1.7, 3, 4] [267.8, 267.6, 267.8] [22.2, 26.4, 30.6]      RCP 423    x = 0.2 78.14 8.57 0.00 0.00 4.71 0.00 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 320 1323 86 12    2    1 100 11.483 11.53 0.25 284.9  [1, 2, 3] [1.1, 2, 2.8] [277.5, 279, 279.7] [35, 41, 45.1] 424    x = 0.3 77.43 8.57 0.00 0.00 4.71 0.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 320 1323 82 16    2    1 100 11.49 11.544 0.25 294.2  [1, 2, 3] [0.4, 0.8, 1.1] [287.3, 287.3, 287.5] [48.2, 54.5, 58.6] 425 177 10.1103/physrevb.83.144415 La(Fe0.88Si(0.12-x)Alx)13 x = 0.000 81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 288 1323                 5 20.2 205.3 24.8 426    x = 0.048 81.71 6.69 4.46 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 288 1323                 5 13.7 197.4 31.5 427    x = 0.081 81.71 3.62 7.52 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 288 1323                 5 9.7 179.7 47.2 428 178 10.1016/j.jallcom.2015.04.199 LaFe11.4Si1.6 A1 81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 mech_alloying 0.5 1423 91 5 0    2  2 0 100 11.488  1 213 3 5 16.3  23 429    A1-1273 81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 mech_alloying 0.5 1423 91 5 0    0  4 0 100 11.497  1 230 3 5 12.3  26    6.98 430    NA2-873 81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 mech_alloying   3 84 13    0   0 100 11.499 431    NA2-1273 81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 mech_alloying   89 9     1  1 0 100 11.489  1 219 5 5 10.6  30    7.17 432    NA2-1473 81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 mech_alloying   46 51     2  1 0 100 11.504 433    M3 81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1423 92  8       0 100 11.47  1 201 4.6 5 17.8  25 434 181 10.1016/j.jmmm.2014.04.020 LaFe(11.6-x)Si1.4Cox x = 0.10 82.14 10.00 0.00 0.00 0.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting              11.484  0.02 207.2 5 [1, 1.5, 2] [17.2, 19.1, 19.8] [202.1, 202.1, 202] [2.5, 3.6, 5.4] 435    x = 0.30 80.71 10.00 0.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting              11.474  0.02 225.6 1.1 [1, 1.5, 2] [8.3, 10.3, 12.4] [224.1, 224, 226] [6.7, 8.6, 9.8] 436    x = 0.50 79.29 10.00 0.00 0.00 3.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting              11.474  0.02 250.1 0.1 [1, 1.5, 2] [4.8, 6.4, 8.1] [245, 247, 247] [11.6, 13.7, 14.9] 437    x = 0.70 77.86 10.00 0.00 0.00 5.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting              11.47  0.02 275.9 0.3 2 5.2 271.5 23.4 438    x = 0.75 77.50 10.00 0.00 0.00 5.36 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting              11.469  0.02 281.1 0.2 2 5.2 275.2 23.4 439    x = 0.80 77.14 10.00 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting              11.496  0.02 285.6 0 [1, 1.5, 2] [2.6, 3.6, 4.6] [280.5, 280.6, 280.6] [22.1, 24.8, 26.7] 440    x = 0.00 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting                 195 6.2 441 182 10.1016/j.jmmm.2008.11.096 La(1-x)GdxFe11.4Si1.6 x = 0.20 81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 1.43 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1373                 [1, 2, 3, 4, 5] [14.3, 17.2, 18.8, 19.8, 20.8] [195.6, 195.6, 195.5, 197.5, 199.2] [4.2, 8.5, 12.9, 16.7, 20.3] 442    x = 0.05 81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.79 0.00 0.00 0.00 0.00 0.00 0.36 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1373                 5 15.9 210.6 23.9 443 183 10.1016/j.jallcom.2016.06.259 La0.7Ce0.3(Fe0.92Co0.08)11.4Si1.6 ribbon 74.91 11.43 0.00 0.00 6.51 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 3 1273              0.05 309  [2, 5] [5.5, 10.4] [306.6, 308.7] [33.5, 43.9] 444    bulk 74.91 11.43 0.00 0.00 6.51 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 3 1273              0.05 306  [2, 5] [4.1, 8.2] [297.4, 300.1] 445 185 10.1063/1.3549560 La0.8Ce0.2(Fe(1-x)Mnx)11.5Si1.5Hy x = 0.015 80.91 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.23 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.86 0.00 0.00 0.00 arc_or_ind_melting 360 1393              0 312  [2, 3] [13.6, 15.6] [307.6, 307.5] [9.6, 15]      Hydrogen is assigned to be y = 2.1 in these samples according to the article. But here 1.8 is considered as it is typical for full hydrogenation 446    x = 0.021 80.42 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.73 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.86 0.00 0.00 0.00 arc_or_ind_melting 360 1393              0 292  [2, 3] [11, 13.5] [285.5, 284.9] [12.3, 15] 447    x = 0.025 80.09 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.05 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.86 0.00 0.00 0.00 arc_or_ind_melting 360 1393              0 279  [2, 3] [8.7, 11] [272.4, 272.1] [15, 19.9] 448    x = 0.015, y = 0.0 80.91 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.23 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1393                 [2, 3] [25.2, 26] [165.9, 165.9] [8, 15] 449 186 10.1016/j.jallcom.2010.12.194 La(1-x)CaxFe11.5Si1.5 x = 0.0 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 336 1373 97.9 0 2.1       1 100 11.47  0.05 183  [2, 5] [18.4, 21.3] [NaN, 191] [NaN, 21.7]      RCP, hysteresis loss 450    x = 0.1 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.71 6.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 336 1373 90.2 8.8 1       1 100 11.469  0.05 198  [2, 5] [15.4, 19.5] [NaN, 202] [NaN, 21.9] 451    x = 0.2 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.43 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 336 1373 87.6 11.6 0.8       1 100 11.469  0.05 200  [2, 5] [12.4, 16.9] [NaN, 204] [NaN, 23.6] 452    x = 0.3 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.14 5.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 336 1373 85.9 13.8 0.3       1 100 11.467  0.05 208  [2, 5] [6.8, 11.2] [NaN, 209.4] [NaN, 28.5] 453 190 10.1016/j.matlet.2014.07.060 La2Fe11Si2  73.33 13.33 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 13.33 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 24 1323 59.4 7.1 15.6  17.9     1 100 454     73.33 13.33 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 13.33 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 24 1423 78.5 1.4 0.0  20.2     1 100   0.05 199  [1, 1.5, 2] [11.6, 13.3, 14.4] [200.5, 200.5, 200.5] [5.8, 8, 10.2] 455     73.33 13.33 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 13.33 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 12 1523 70.9 9.3 0.0  19.8     1 100 456 191 10.1063/1.3335603 LaFe10.8Co0.7Si1.5C0.2  77.14 10.71 0.00 0.00 5.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.43 0.00 0.00 arc_or_ind_melting 48 1373  1.8        1 1.8   0.01 303  [1, 2] [2.8,4.9 ] [300.8, 301.2] [28.3, 35]      RCP 457     77.14 10.71 0.00 0.00 5.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.43 0.00 0.00  6 1373  5.8        1 5.8 458   La(Fe0.919Co0.081)11.7Al1.3  76.80 0.00 9.29 0.00 6.77 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  311  2 3.6 459   La(Fe0.88Si0.12)13H1.5  81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 10.71 0.00 0.00 0.00                  323  2 19 460 194 10.1016/j.jallcom.2015.05.164 LaFe11.6Si1.4Hy y = 0.935 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 6.68 0.00 0.00 0.00 arc_or_ind_melting 5 1473               277.7           Hydrogen absorption vs temp, time 461    y = 0.954 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 6.81 0.00 0.00 0.00 arc_or_ind_melting 5 1473               284.1 462    y = 0.960 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 6.86 0.00 0.00 0.00 arc_or_ind_melting 5 1473               285.8 463    y = 0.985 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 7.04 0.00 0.00 0.00 arc_or_ind_melting 5 1473               288.7 464    y = 1.005 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 7.18 0.00 0.00 0.00 arc_or_ind_melting 5 1473               290.1 465    y = 1.010 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 7.21 0.00 0.00 0.00 arc_or_ind_melting 5 1473               292.7 466    y = 1.060 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 7.57 0.00 0.00 0.00 arc_or_ind_melting 5 1473               296.1 467    y = 1.099 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 7.85 0.00 0.00 0.00 arc_or_ind_melting 5 1473               305.3 468    y = 1.138 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 8.13 0.00 0.00 0.00 arc_or_ind_melting 5 1473               310.6 469    y = 1.260 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 9.00 0.00 0.00 0.00 arc_or_ind_melting 5 1473               327 470 197 10.1016/j.jallcom.2014.11.120 LaFe(11.5-x)MnxSi1.5 x = 0.0 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 600 1323              0.01 204.2 471    x = 0.3 80.00 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.14 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 600 1323              0.01 198 472    x = 0.4 79.29 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.86 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 600 1323              0.01 187.5 473    x = 0.7 77.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 600 1323              0.01 186 474 198 10.1016/j.jmmm.2010.12.038 La0.8Ce0.2Fe11.4Si1.6Bx x = 0.0 81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting              11.455  0.1 183.9 1.75 1 25.4 180.5 2.6      RCP 475    x = 0.1 81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.71 arc_or_ind_melting                0.1 179.3 1.4 1 28.3 177.8 2.4 476    x = 0.2 81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 1.43 arc_or_ind_melting              11.457  0.1 187.3 1.5 1 24.3 182.8 2.3 477    x = 0.3 81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 2.14 arc_or_ind_melting              11.464  0.1 188.9 0.4 1 14.6 187 4.1 478    x = 0.4 81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 2.86 arc_or_ind_melting              11.475  0.1 196.6 0.3 1 11 190 4.7 479    x = 0.5 81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 3.57 arc_or_ind_melting              11.485  0.1 201.6 0.25 1 9.4 197.1 5.6 480 208 10.1016/j.jmmm.2012.11.030 La0.8Gd0.2Fe11.4Si1.6Bx x = 0.00 81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 1.43 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 336 1323            11.464   200  5 14.8 481    x = 0.03 81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 1.43 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.21 arc_or_ind_melting 336 1323            11.464   204  5 16 482    x = 0.06 81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 1.43 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.43 arc_or_ind_melting 336 1323            11.465   205  5 15 483    x = 0.20 81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 1.43 0.00 0.00 0.00 100.00 0.00 0.00 0.00 1.43 arc_or_ind_melting 336 1323            11.465   215  5 7.5 484    x = 0.30 81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 1.43 0.00 0.00 0.00 100.00 0.00 0.00 0.00 2.14 arc_or_ind_melting 336 1323            11.473   222  5 6.6 485   La0.8Gd0.2Fe11.4Si1.6  81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 1.43 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  215  5 7.9 486   La0.95Gd0.05Fe11.4Si1.6  81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.79 0.00 0.00 0.00 0.00 0.00 0.36 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  215  5 7 487   La0.95Gd0.05Fe11.4Si1.6  81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.79 0.00 0.00 0.00 0.00 0.00 0.36 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  210  5 15 488 211 10.1016/j.jmmm.2008.11.081 La(Fe0.919Co0.081)11.7Al1.3  76.80 0.00 9.29 0.00 6.77 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1233             11.64 0.05 311.4  [2, 5] [3.6, 7.3] [315.9, 316.8] [48, NaN]      RCP 489   La0.8Pr0.2(Fe0.919Co0.081)11.7Al1.3  76.80 0.00 9.29 0.00 6.77 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1233             11.629 0.05 300 490   La0.8Nd0.2(Fe0.919Co0.081)11.7Al1.3  76.80 0.00 9.29 0.00 6.77 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1233            11.626  0.05 294  [2, 5] [4.6, 9.4] [298.1, 298] [41.8, 58.5] 491 212 10.1016/j.jmmm.2018.02.005 LaFe11.0Co0.7Si1.3  78.57 9.29 0.00 0.00 5.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323 96 4        1 100 11.486   267  [1, 2, 4, 5] [4.7, 8.1, 12.8, 14.6] [268.1, 269.6, 271.7, 272.1] [14.3, 18.4, 25.9, 29.3] 492   La0.9Dy0.1Fe11.0Co0.7Si1.3  78.57 9.29 0.00 0.00 5.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.43 0.00 0.00 0.00 0.71 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323 94 6        1 100 11.483   265.5  [1, 2, 4, 5] [3.15, 5.75, 9.7, 11.2] [267.1, 268.2, 270.1, 270.3] [18.5, 23.1, 29.3, 32.5] 493   La0.8Dy0.2Fe11.0Co0.7Si1.3  78.57 9.29 0.00 0.00 5.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 0.00 0.00 1.43 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323 90 10        1 100 11.481   269  [1, 2, 4, 5] [2.5, 4.6, 7.9, 9.2] [271, 271.2, 272.3, 273.1] [20.8, 25.5, 32.9, 36.5] 494 77 10.1016/j.jmmm.2006.11.211 La(1-x)ErxFe11.44Si1.56 x = 0.0 81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323            11.469  0.1 200  5 20.6 206 21.9 495    x = 0.1 81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.71 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323            11.469  0.1 205  [1, 2, 3, 5] [10.7, 13.3, 15.3, 17.25] [202.9, 203.7, 204.9, 208] [5.2, 9.5, 13.7, 21.9] 496    x = 0.3 81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.14 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323            11.459  0.1 214  5 9.3 214.8 29.1 497 572-15 10.1063/1.2921781 La0.7R0.3Fe11.5Si1.5 R = La 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting              11.468  0.01 194.1 498    R = Ce 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting                0.01 170.2 499    R = Pr 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting                0.01 184.9 500    R = Nd 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting              11.439  0.01 189 501 572-26 10.1063/1.4868703 La0.7Pr0.3Fe(11.4-x)CrxSi1.6 x = 0.00 81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting   96.1 3.5 0.4       0 100 11.459  0.01 197  5 17        RCP 502    x = 0.06 81.00 11.43 0.00 0.00 0.00 0.00 0.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting   85.9 10.6 3.5       0 100 11.456  0.01 180  5 12 503    x = 0.12 80.57 11.43 0.00 0.00 0.00 0.00 0.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting   92.6 6 1.4       0 100 11.454  0.01 185  5 14.2 504    x = 0.23 79.79 11.43 0.00 0.00 0.00 0.00 1.64 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting   94 4.7 1.3       0 100 11.452  0.01 190  5 15.6 505    x = 0.34 79.00 11.43 0.00 0.00 0.00 0.00 2.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting   97.5 2.3 0.2       0 100 11.452  0.01 195  5 17.5 506 574 10.1016/j.matlet.2018.11.055 LaFe10.0Si3.0Cx x = 0.0 71.43 21.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 480 1323            11.408  0.05 232           TEC 507    x = 0.2 71.43 21.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.43 0.00 0.00 arc_or_ind_melting 480 1323            11.4401  0.05 260 508    x = 0.3 71.43 21.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 2.14 0.00 0.00 arc_or_ind_melting 480 1323            11.4503  0.05 265 509    x = 0.4 71.43 21.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 2.86 0.00 0.00 arc_or_ind_melting 480 1323            11.4575  0.05 269 510 576 10.12693/aphyspola.133.232 LaFe11.2Co(0.7-x)MnxSi1.1 x = 0.1 80.00 7.86 0.00 0.00 4.29 0.00 0.00 0.00 0.00 0.00 0.71 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323 93         1 93 11.477   256  [1, 2, 4, 5] [3.4, 6.65, 10.48, 11.8]        H vs. S 511    x = 0.2 80.00 7.86 0.00 0.00 3.57 0.00 0.00 0.00 0.00 0.00 1.43 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323 90         1 90 11.476   246  [1, 2, 4, 5] [3.6, 6.4, 10.1, 11.7] 512 579 10.12693/aphyspola.129.193 LaFe11.14Co0.66Si(1.2-x)Alx x = 0.1 79.57 7.86 0.71 0.00 4.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323 76 24        0 100 513    x = 0.2 79.57 7.14 1.43 0.00 4.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323 88 12        0 100 514    x = 0.3 79.57 6.43 2.14 0.00 4.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323 93 7        0 100 515   LaFe11.14Co0.66Si(1.2-x)Gax x = 0.1 79.57 7.86 0.00 0.71 4.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323 85 15        0 100 516    x = 0.2 79.57 7.14 0.00 1.43 4.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323 74 26        0 100 517    x = 0.3 79.57 6.43 0.00 2.14 4.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323 68 32        0 100 518 467 10.1007/s11664-016-4615-1 LaFe13-xSix x = 2.0 78.57 14.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning                1.2 246  1.2 1.46 52 519    x = 3.0 71.43 21.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning                1.2 230 520   La(1+z)Fe(10.5-z)CoSi1.5 z = 0.0 75.00 10.71 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning                 297  1.2 0.8 52 521    z = 0.5 71.43 10.71 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning                 276  1.2 1.2 44 522    z = 1.0 67.86 10.71 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 14.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning                 273  1.2 0.43 56 523   LaFe(11-y)CoySi2 y = 0.4 75.71 14.29 0.00 0.00 2.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning                 266 524    y = 0.6 74.29 14.29 0.00 0.00 4.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning                 270 525    y = 0.8 72.86 14.29 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning                 290  1.2 1.51 53 526    y = 0.9 72.14 14.29 0.00 0.00 6.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning                 301  1.2 1.53 56 527 592 10.1063/1.2829035 LaFe11.5Si1.5  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373              0.01 194 1.2 [2, 5] [20.9, 23.7]        Hysteresis loss 528   LaFe11.2Si1.8  80.00 12.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373              0.01 216 0 [2, 5] [7.8, 13.7] 529   La0.7Nd0.3Fe11.5Si1.5  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373              0.01 188 3.3 [2, 5] [29.3, 32] 530   La0.7Nd0.3Fe11.2Si1.8  80.00 12.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373              0.01 207 0 [1, 2, 3, 4, 5] [5.8, 10.5, 12.6, 14, 15.2] [206.9, 206.8, 207.2, 209.1] [10.7, 13.35, 17.9, 23.2, 27.4] 531   La0.7Nd0.3Fe10.7Co0.8Si1.5  76.43 10.71 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373              0.01 280 0 [1, 2, 3, 4, 5] [4.4, 7.9, 10.8, 12.9, 15] [276, 277.6, 278.2, 278.1] [20.4, 24.2, 26.4, 29.6, 33] 532 109 10.1016/j.jallcom.2015.05.173 LaFe11.5Si1.5  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 0.033 1273              0.01 189  1.5 12 188.9 8.75 533     82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 2 1273              0.01 201  1.5 16.9 194.9 7.1 534 599 10.1016/j.jmmm.2012.11.049 LaFe11.83Si1.17  84.50 8.36 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting  1323                 5 24.15 186.9 25 535   LaFe11.6Si1.4  82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting  1323                 5 25 201 21.5 536   LaFe10.8Si2.2  77.14 15.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting  1323                 5 7.2 239.4 57.9 537 601 10.1109/tmag.2008.2002523 La(Fe0.893Si0.107)13  82.92 9.94 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                 1 195.4 2.5 1.6 22 195.2 6.6    7.19 538   La(Fe0.887Si0.113)13  82.36 10.49 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                   2.4 1.6 18.9 198.9 7 539   La(Fe0.881Si0.119)13  81.81 11.05 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                 1.6 205.8 0.7 1.6 16.2 202.9 7.2 540   La(Fe0.865Co0.05Si0.085)13  80.32 7.89 0.00 0.00 4.64 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                    1.6 9.4 254.7 13.7    7.24 541   La(Fe0.857Co0.058Si0.085)13  79.58 7.89 0.00 0.00 5.39 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                    1.6 8.7 264 15.4    7.24 542   La(Fe0.85Co0.065Si0.085)13  78.93 7.89 0.00 0.00 6.04 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                    1.6 7.2 274.4 18.3    7.24 543   La(Fe0.84Co0.075Si0.085)13  78.00 7.89 0.00 0.00 6.96 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                    1.6 6.2 287.3 22.3    7.24 544   La(Fe0.828Co0.087Si0.085)13  76.89 7.89 0.00 0.00 8.08 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                    1.6 5.5 302.7 25.6    7.21 545   La(Fe0.816Co0.099Si0.085)13  75.77 7.89 0.00 0.00 9.19 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                    1.6 4.8 320.6 28.2    7.2 546   La(Fe0.803Co0.112Si0.085)13  74.56 7.89 0.00 0.00 10.40 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                    1.6 4.5 336.5 31.5    7.21 547   La(Fe0.915Si0.85)13  84.96 7.89 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00   1423                     1.7 3.7 188.8 548     84.96 7.89 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00   1393                     1.7 4.2 186.7 549     84.96 7.89 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00   1373                     1.7 4.2 185 550     84.96 7.89 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00   1333                     1.7 3.5 185.7 551 603 10.1063/1.2137884 La(Fe(1-x)Cox)11.4Si1.6 x = 0.00 81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 0.33 1273 96.1 3.9        0 100 11.476   202  [1, 5] [7.7, 20.5] [203.1, 208.4] [9.5, 23] 552    x = 0.04 78.17 11.43 0.00 0.00 3.26 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 0.33 1273 98.5 1.5        0 100 11.469   250  [1, 5] [2.7, 11.8] [253.4, 253.1] [15.2, 31.5] 553    x = 0.08 74.91 11.43 0.00 0.00 6.51 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 0.33 1273 97.6 2.4        0 100  11.488 0 306  [1, 5] [2.4, 9.9] [300, 302] [32, 43.8] 554    x = 0.12 71.66 11.43 0.00 0.00 9.77 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 0.33 1273 98.5 1.5        0 100  11.509 0 354 555 54 10.1016/j.jmmm.2008.08.081 LaFe11.7Si1.3N1.3  83.57 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 9.29 0.00 arc_or_ind_melting 360 1323            11.467   230  [1, 2, 3, 5] [0.6, 1.35, 2, 3.5] [227.9, 228.7, 233.2, 236.8] [NaN, 80.9, 83, 83.3]      ΔS values in Fig. 3 are affected by local peaks,peaks were ignored 556   LaFe11.7Si1.3  83.57 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323            11.733   195  [1, 2, 3, 5] [22, 22.3, 24.6, 25.1] [191, 192.9, 195.1, 197.4] [2.9, 8.1, 12.2, 20.4] 557 609 10.1063/1.5022932 LaFe11.5Si1.5  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 336 1323 80.7 13.6 5.7       0 100 558     82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 4 1523 83.3 16.7 0       0 100 559 614 10.1016/j.jssc.2015.10.016 LaFe11.5Si1.5H1.19  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 8.50 0.00 0.00 0.00 mech_alloying 0.5 1423 97.1 0.5       2.4 0 100 11.595  0.01 329.8 560   LaFe11.5Si1.5D0.7  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 5.00 0.00 0.00 0.00 mech_alloying 0.5 1423            11.51 11.56 0.01 264.3 561   LaFe11.5Si1.5D1.49  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 10.64 0.00 0.00 0.00 mech_alloying 0.5 1423              0.01 321 562   LaFe11.4Si1.6H0.21  81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 1.50 0.00 0.00 0.00 mech_alloying 0.5 1423              0.01 234.5  [2, 5] [8.6, 15] [NaN, 249.1] [NaN, 24.4] 563   LaFe11.4Si1.6H0.41  81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 2.93 0.00 0.00 0.00 mech_alloying 0.5 1423              0.01 266.6  [2, 5] [9.8, 15.1] [NaN, 282.2] [NaN, 23.3] 564   LaFe11.4Si1.6H0.86  81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 6.14 0.00 0.00 0.00 mech_alloying 0.5 1423              0.01 281.7  [2, 5] [11.1, 16.5] [NaN, 299.3] [NaN, 19.3] 565   LaFe11.4Si1.6  81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 mech_alloying 0.5 1423              0.01 203  5 22.8 219.9 14.2 566   LaFe11.5Si1.5Cy y = 0.0 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 mech_alloying                0.01 196.6 567    y = 0.7 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 5.00 0.00 0.00 mech_alloying              11.642 11.651 0.01 321.3 568   LaFe10.8Si2.2Cy y = 0.0 77.14 15.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 mech_alloying                0.01 244.2  2 2.3 241.7 63.8 569    y = 0.5 77.14 15.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 3.57 0.00 0.00 mech_alloying                0.01 315.2  2 1.4 315.2 570 617 10.1016/j.jmmm.2014.10.133 LaFe10.95Co0.65Si1.4C0.15  78.21 10.00 0.00 0.00 4.64 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.07 0.00 0.00 arc_or_ind_melting 72 1423               287  [2, 3] [5.9, 8.1] [286.6, 287.9] [29.1, 32.2]      ΔS-Tc for several compounds 571   LaFe10.85Co0.65Si1.5C0.15  77.50 10.71 0.00 0.00 4.64 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.07 0.00 0.00 arc_or_ind_melting 72 1423               291  [2, 3] [5, 6.8] [291.4, 291] [32.9, 38.4] 572   LaFe10.95Co0.65Si1.4C0.2  78.21 10.00 0.00 0.00 4.64 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.43 0.00 0.00 arc_or_ind_melting 72 1423               293.5  [2, 3] [6, 7.9] [293.3, 293.3] [27.2, 33.3] 573 618 10.1016/j.jmmm.2010.08.013 LaFe(13-x-y)CoxSiy x = 0.86, y = 1.08 79.00 7.71 0.00 0.00 6.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                    1 6.1 275.8 14.3 1 2.3 277.1 574    x = 0.94, y = 1.01 78.93 7.21 0.00 0.00 6.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                    1 5.1 287.1 16.4 1 2.1 287.1 575    x = 0.97, y = 1.07 78.29 7.64 0.00 0.00 6.93 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                    1 5.3 289.8 16.4 1 2.2 289.6 576 620 10.1007/s10948-014-2542-z LaFe11.8Si1.2  84.29 8.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 mech_alloying 0.5 1373            11.469  0.01 192.5  2 11  9.9 577   LaFe11.7Si1.3  83.57 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 mech_alloying 0.5 1373            11.468 578   LaFe11.5Si1.5  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 mech_alloying 0.5 1373            11.464  0.01 201  2 17.3  7.4 579   LaFe10.8Si2.2  77.14 15.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 mech_alloying 0.5 1373            11.464  0.02 240  2 2.3  59.9 580   LaFe11.6Si1.4  82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 mech_alloying 0.5 1373              0.01 200.2  2 24.4  5.1 581   LaFe11.4Si1.6  81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 mech_alloying 0.5 1373              0.01 202.5  2 16.5  9.4 582   LaFe11.2Si1.8  80.00 12.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 mech_alloying 0.5 1373              0.01 216.5  2 6.5  21.8 583   LaFe11Si2  78.57 14.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 mech_alloying 0.5 1373              0.01 228.5  2 3.8  32.9 584 630 10.1063/1.3540372 LaFe12Si1  85.71 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 2 1323  27        0 27 11.479 585   LaFe11.8Si1.2  84.29 8.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 2 1323  10.8        0 10.8 11.483 586   LaFe11.6Si1.4  82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 2 1323  20        0 20 11.473 587   LaFe11.4Si1.6  81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 2 1323  27        0 27 11.463 588   LaFe11.2Si1.8  80.00 12.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 2 1323  27        0 27 11.46 589   LaFe11.8Si1.2  84.29 8.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 438 1323  40        0 40 11.481 590   LaFe11.6Si1.4  82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 438 1323  7        0 7 11.476 591   LaFe11.4Si1.6  81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 438 1323  7        0 7 11.47 592   LaFe11.2Si1.8  80.00 12.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 438 1323  7        0 7 11.469 593 632 10.1016/j.intermet.2010.07.022 LaFe11.5Si1.5  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1273 91.4 6.2 2.4        100 11.464 594     82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1373 95.5 1.8 2.7        100 11.469 595     82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 mech_alloying 0.5 1273 95 2.1 1      1.9 0 100 11.478 596     82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 mech_alloying 0.5 1393 96.9 0.5 0      2.6 0 100 11.469 597   LaFe11.4Si1.6  81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 mech_alloying 0.5 1423 96.6 1 0      2.4 0 100 11.469  0.03 202.5  [2, 5] [16.5, 25] [205.2, 217] [9.3, 16.2] 598   LaFe11.2Si1.8  80.00 12.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 mech_alloying 0.5 1423 95.5 1.8 0      2.7 0 100 11.48  0.03 216.5  [2, 5] [6.5, 11.2] [219.4, 229.6] [24.3, 35.9] 599   LaFe11.0Si2.0  78.57 14.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 mech_alloying 0.5 1403 95.3 2.2 0      2.5 0 100 11.464  0.03 228.5  [2, 5] [3.8, 7] [227.3, 238.8] [43.2, NaN] 600   LaFe11.6Si1.4  82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 mech_alloying                0.03 200.2  [2, 5] [24.4, 32.7] [204.3, 237.3] [5.8, 9.3] 601 634 10.1002/adma.200901072 LaFe11.83Si1.17  84.50 8.36 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  175  [2, 5] [21.2, 27.8] 602   LaFe11.8Si1.2  84.29 8.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00               11.488 11.547    [2, 5] [25.4, 29.2] [NaN, 192.8] [NaN, 22.7] 603   LaFe11.7Si1.3  83.57 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  183  [2, 5] [22.9, 26] [NaN, 197.1] [NaN, 22] 604   LaFe11.6Si1.4  82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  188  [2, 5] [20.8, 24.7] [NaN, 200.2] [NaN, 17.8] 605   LaFe11.5Si1.5  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  194  [2, 5] [20.8, 24.8] [NaN, 204.3] [NaN, 22] 606   LaFe11.5Si1.5  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373              0.01 194 1.4 [2, 5] [21, 23.7] 607   LaFe11.5Si1.5  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                 0.01 195  [2, 5] [21.9, 24.6] [NaN, 201.4] [NaN, 20.9] 608   LaFe11.4Si1.6  81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00               11.486 11.524  199  [2, 5] [14.2, 18.7] [NaN, 210] [NaN, 23] 609   LaFe11.4Si1.6  81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  209  [2, 5] [14.3, 19.3] 610   LaFe11.3Si1.7  80.71 12.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  206  [2, 5] [11.9, 17.6] [NaN, 213.8] [NaN, 24.1] 611   LaFe11.2Si1.8  80.00 12.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00               11.476 11.507  210  [2, 5] [7.5, 13] [NaN, 223.1] [NaN, 32.4] 612   LaFe11.0Si2.0  78.57 14.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00               11.472 11.497  221  [2, 5] [4, 7.9] [NaN, 232.5] [NaN, 37.3] 613   LaFe10.6Si2.4  75.71 17.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00               11.465 11.48    2 2.8 614   LaFe10.4Si2.6  74.29 18.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00               11.46 11.468    2 2.3 615   La(Fe0.99Mn0.01)11.7Si1.3Hx  82.74 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.84 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.86 0.00 0.00 0.00                  336  [2, 5] [16, 23.4] [331.9, 335.9] [9.5, 19.6]      These 3 samples considered to be fully hydrogenated 616   La(Fe0.98Mn0.02)11.7Si1.3Hx  81.90 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.67 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.86 0.00 0.00 0.00                  312  [2, 5] [13, 17.7] [309, 312] [10.6, 22] 617   La(Fe0.97Mn0.03)11.7Si1.3Hx  81.06 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.51 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.86 0.00 0.00 0.00                  287  [2, 5] [11, 15.9] [283.6, 287] [12.2, 24.1] 618   LaFe11.12Co0.71Al1.17  79.43 0.00 8.36 0.00 5.07 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  279  [2, 5] [4.6, 9.1] 619   La(Fe0.98Co0.02)11.7Al1.3  81.90 0.00 9.29 0.00 1.67 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  198  [2, 5] [5.9, 10.6] 620   LaFe11.2Co0.7Si1.1  80.00 7.86 0.00 0.00 5.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  274  5 20.3 621   LaFe10.7Co0.8Si1.5  76.43 10.71 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  285  [2, 5] [7, 13.5] 622   LaFe10.98Co0.22Si1.8  78.43 12.86 0.00 0.00 1.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  242  [2, 5] [6.3, 11.5] 623   La0.5Pr0.5Fe10.5Co1.0Si1.5  75.00 10.71 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 3.57 0.00 0.00 3.57 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  295  [2, 5] [6, 11.7] 624 102 10.1088/1674-1056/18/5/055 La(1-x)PrxFe11.5Si1.5 x = 0.1 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.43 0.00 0.00 0.71 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373               191  [2, 5] [24, 26.1]        2T data is taken from 634 625    x = 0.2 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373               188  [2, 5] [26, 28.3] 626    x = 0.3 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373               185  [2, 5] [28, 30.5] [NaN, 183.5] [NaN, 20.3] 627    x = 0.4 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 4.29 0.00 0.00 2.86 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373              0.05 182 4.3 [2, 5] [29, 31.5] 628    x = 0.5 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 3.57 0.00 0.00 3.57 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373              0.01 181 5 [2, 5] [30, 32.4] 629   La(1-x)NdxFe11.5Si1.5 x = 0.1 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.43 0.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373               192  [2, 5] [23, 25.9] 630    x = 0.2 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373               190  [2, 5] [24, 27.1] 631    x = 0.3 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373              0.01 188 3.2 [2, 5] [29, 32] 632   La(1-x)CexFe11.5Si1.5 x = 0.1 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.43 0.00 0.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373               188 633    x = 0.2 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373               182 634    x = 0.3 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373               173  5 23.8 635 634-48 10.1088/0953-8984/15/7/102 LaFe11.5Si1.5H0.3  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 2.14 0.00 0.00 0.00               11.483  0.01 224  5 17.4 231.5 26.3 636   LaFe11.5Si1.5H0.6  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 4.29 0.00 0.00 0.00                 0.01 257  5 17.8 260.7 27.1 637   LaFe11.5Si1.5H0.9  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 6.43 0.00 0.00 0.00                 0.01 272  5 16.9 272.2 26.3 638   LaFe11.5Si1.5H1.3  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 9.29 0.00 0.00 0.00               11.528  0.01 288  [2, 5] [8.4, 17] [NaN, 289.3] [NaN, 27.9] 639   LaFe11.5Si1.5H1.5  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 10.71 0.00 0.00 0.00                 0.01 312  5 16.8 313.6 640   LaFe11.5Si1.5H1.8  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.86 0.00 0.00 0.00                11.602 0.01 341  5 20.5 342 20.9 641 634-51 10.1063/1.1558658 LaFe11.5Si1.5C0.2  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.43 0.00 0.00 arc_or_ind_melting              11.481  1 225  [2, 5] [18, 22.8] [225.5, 227.3] [10, 21.8] 642   LaFe11.5Si1.5C0.5  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 3.57 0.00 0.00 arc_or_ind_melting    5         5 11.518  1 241  [2, 5] [7.4, 12.7] [250.1, 251.9] [21.2, 30.6] 643 664 10.1063/1.2794412 La0.5Pr0.5Fe11.5Si1.5C0.3  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 3.57 0.00 0.00 3.57 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 2.14 0.00 0.00                  211  [2, 5] [25.2, 27.6] [209, 209.1] [8.8, 19.6] 644 46 10.1088/0022-3727/41/24/245005 La0.8Pr0.2Fe10.7Co0.8Si1.5  76.43 10.71 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  280  [2, 5] [7.2, 13.6] 645   La0.6Pr0.4Fe10.7Co0.8Si1.5  76.43 10.71 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 4.29 0.00 0.00 2.86 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  274  [2, 5] [7.4, 14.2] 646   La0.5Pr0.5Fe10.7Co0.8Si1.5  76.43 10.71 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 3.57 0.00 0.00 3.57 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  272  [2, 5] [8.1, 14.6] 647 592 10.1063/1.2829035 La0.7Nd0.3Fe10.7Co0.8Si1.5  76.43 10.71 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  280  [2, 5] [7.9, 15] 648 638 10.1063/1.2404468 LaFe(13-x)Six x = 1.2 84.29 8.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1273               189  5 29.2 193 185.4 649    x = 1.3 83.57 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1273               194.4  5 25.9 650    x = 1.4 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1273               200.1  5 24 651    x = 1.5 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1273               205.1  5 24.1 652    x = 1.6 81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1273               210.2  5 18.9 653    x = 1.7 80.71 12.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1273               215  5 17.2 654    x = 1.8 80.00 12.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1273               220.2  5 12.9 196.6 655 641 10.1063/1.1847871 LaFe(13-x)Six x = 1.00 85.71 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 2 1323                 5 25.4 201.5 20.9 656    x = 1.20 84.29 8.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 2 1323                 [1, 2, 4, 5] [21.9, 25.3, 29.3, 30.95] [195.1, 198.1, 201, 201.3] [4.6, 9.3, 16.7, 20.4] 657    x = 1.43 82.64 10.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 2 1323                 5 17.8 210.4 25.1 658    x = 1.60 81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 2 1323                 5 12.9 228.6 30.2 659    x = 1.80 80.00 12.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 2 1323                 [1, 2, 4, 5] [2.7, 5.2, 8.8, 10.3] [236, 237.1, 240, 240.1] [25.4, 29.4, 35.6, 39] 660 644 10.1063/1.1448793 LaFe(13-x)Six x = 2.4 75.71 17.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1273  0         0 11.47  0.01 247  5 5.8 246.1 76.3 661    x = 2.6 74.29 18.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1273  0         0 11.45  0.01 248  5 5.9 246.3 83.7 662    x = 2.8 72.86 20.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1273  0         0 11.43  0.01 195  5 3.7 189.5 123.9 663 648 10.1109/20.281070 LaFe(13-x)Six x = 1.5 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 96 1243               193 664    x = 2.0 78.57 14.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 96 1243               257 665    x = 2.4 75.71 17.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 96 1243               262 666    x = 3.5 67.86 25.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 96 1243               103 667    x = 4.0 64.29 28.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 96 1243               88 668    x = 5.0 57.14 35.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 96 1243               82 669   LaFe11.5Si1.5N1.6  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 11.43 0.00 arc_or_ind_melting 96 1243            11.81   273 670   LaFe11Si2N1.2  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 8.57 0.00 arc_or_ind_melting 96 1243             11.72  317 671   LaFe10.6Si2.4N1.2  75.71 17.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 8.57 0.00 arc_or_ind_melting 96 1243             11.66  314 672 653 10.1063/1.1664431 La(Fe0.88Al0.12)13Cx x = 0.0 81.71 0.00 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1273            11.591   197 673    x = 0.2 81.71 0.00 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.43 0.00 0.00 arc_or_ind_melting 360 1273            11.624   224 674    x = 0.4 81.71 0.00 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 2.86 0.00 0.00 arc_or_ind_melting 360 1273            11.65   250.3 675    x = 0.6 81.71 0.00 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 4.29 0.00 0.00 arc_or_ind_melting 360 1273  5.4        1 5.4 11.66   264.7 676    x = 0.8 81.71 0.00 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 5.71 0.00 0.00 arc_or_ind_melting 360 1273  9.6        1 9.6 11.675   279 677 653-4 10.1016/S0304-8853(03)00207-5 La(Fe(1-x)Cox)11.4Si1.6 x = 0.00 81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1273            11.473   202.8 678    x = 0.02 79.80 11.43 0.00 0.00 1.63 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1273            11.474   228  [1, 3, 5] [8.4, 16.6, 20.4] [224.6, 224.5, 224.5] [7.8, 14.5, NaN] 679    x = 0.04 78.17 11.43 0.00 0.00 3.26 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1273            11.476   255.6 680    x = 0.06 76.54 11.43 0.00 0.00 4.89 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1273            11.473   279.4  [1, 3, 5] [2.65, 6.8, 10.1] [277.5, 277.5, 280.5] [26.7, 26.3, 38] 681    x = 0.08 74.91 11.43 0.00 0.00 6.51 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1273             11.474  304.1 682    x = 0.10 73.29 11.43 0.00 0.00 8.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1273             11.495  323.3 683 654 10.1063/1.1502919 La(Fe(1-x)Cox)11.2Si1.8 x = 0.00 80.00 12.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1323  6        0 6   0.01 222  [2, 5] [7.4, 13] [220.9, 223] [20.6, 32.8] 684    x = 0.02 78.40 12.86 0.00 0.00 1.60 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1323  6        0 6   0.01 242.4  [2, 5] [6.2, 11.5] [240.5, 242.8] [27.2, 36.2] 685    x = 0.04 76.80 12.86 0.00 0.00 3.20 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1323  6        0 6   0.01 266.9  5 8.65 686    x = 0.07 74.40 12.86 0.00 0.00 5.60 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1323  6        0 6   0.01 296.2  [2, 5] [4, 7.9] [292.3, 294.3] [49.4, 60.9] 687    x = 0.08 73.60 12.86 0.00 0.00 6.40 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1323  6        0 6   0.01 307  5 7.1 688 661 10.1063/1.3359807 La(1-x)PrxFe11.44Si1.56 x = 0.0 81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 3 1300              0.01 203 0.2 5 14.3 211 23.9 689    x = 0.1 81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.43 0.00 0.00 0.71 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 3 1300              0.01 198 0.4 5 19.2 204.9 21.9 690    x = 0.2 81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 3 1300              0.01 197 0.8 5 19 203.1 21.7 691 662 10.1063/1.3063067 LaFe11.7(Si(1-x)Cux)1.3 x = 0.0 83.57 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1323  4.5        0 4.5 11.475  0.01 185 3 [2, 5] [25.3, 29.1] [185.1, 193.2] [10.3, 23] 692    x = 0.1 83.57 8.36 0.00 0.00 0.00 0.00 0.00 0.00 0.93 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1323  4.5        0 4.5 693    x = 0.2 83.57 7.43 0.00 0.00 0.00 0.00 0.00 0.00 1.86 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1323  4.5        0 4.5 11.468  0.01 200 0 [2, 5] [16.1, 20.2] [198.2, 201.1] [10, 21.2] 694 316 10.1007/s10853-020-04449-1 LaFe11.6Si1.4  82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 strip_casting 24 1323 84.7 15.3         100 11.478  0.05 197  2 11.1 200.0 14.3 695 320 10.1088/2043-6262/4/2/025018 LaFe(11-x)CoxSi2 x = 0 78.57 14.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning                1.2 220  1.2 1.4  55.0 696    x = 1 71.43 14.29 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning                1.2 315  1.2 1.3  67.0 697    x = 2 64.29 14.29 0.00 0.00 14.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning                1.2 410  1.2 1.3  70.0 698    x = 3 57.14 14.29 0.00 0.00 21.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning                1.2 480 699    x = 4 50.00 14.29 0.00 0.00 28.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning                1.2 530 700 274 10.1063/1.3335892 La(Fe0.767Co0.17Si0.063)13  71.22 5.85 0.00 0.00 15.79 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 288 1323                 5 1.2 161.1 20.9 701   La(Fe0.745Co0.17Si0.085)13  69.18 7.89 0.00 0.00 15.79 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 288 1323                 5 1.1 157.2 22.3 702   La(Fe0.745Co0.17Si0.085)13  69.18 7.89 0.00 0.00 15.79 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 2 1323                 5 1.0 163.0 36.0 703 214 10.1109/tmag.2009.2018921 La(1-z)Cez(Fe0.88Si0.12)13 z = 0.0 81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1423            11.468   195.1  2 19.9 195  2 6.4 195 704    z = 0.1 81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.43 0.00 0.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1423            11.462   190  2 23.7 190 705    z = 0.2 81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1423            11.457   182  2 27.1 182 706    z = 0.3 81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1423            11.452   175  2 29.1 175  2 7.4 175 707   La(1-z)Prz(Fe0.88Si0.12)13 z = 0.1 81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.43 0.00 0.00 0.71 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1423            11.464   194  2 23.0 194  2 6.7 194 708    z = 0.3 81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1423            11.456   190  2 25.7 190  2 7.3 190 709    z = 0.5 81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 3.57 0.00 0.00 3.57 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1423            11.447   186  2 28.7 186  2 7.1 186 710   La(Fe0.88Si0.12)13H1.5  81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 10.71 0.00 0.00 0.00 arc_or_ind_melting 240 1423                 2 19.1 324 8.0 711   La0.7Ce0.3(Fe0.88Si0.12)13H1.7  81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.14 0.00 0.00 0.00 arc_or_ind_melting 240 1423                 2 21.1 323 7.8 712   La0.5Pr0.5(Fe0.88Si0.12)13H1.6  81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 3.57 0.00 0.00 3.57 0.00 0.00 0.00 0.00 0.00 0.00 100.00 11.43 0.00 0.00 0.00 arc_or_ind_melting 240 1423                 2 22.1 325 7.8 713 434 10.1007/s40195-020-01107-y La1.7Fe11.6Al1.4  78.91 0.00 9.52 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 11.56 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 36 1248  0         0   0.02 196  [1.2, 2] [2.2, 3.5] [187.7, 189] 714   La1.7Fe11.6Al1.3Si0.1  78.91 0.68 8.84 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 11.56 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 36 1198  0         0   0.02 201  [1.2, 2] [3, 4.6] [195.3, 197] 715   La1.7Fe11.6AlSi0.4  78.91 2.72 6.80 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 11.56 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 36 1248  0         0   0.02 182  [1.2, 2] [2.9, 4.4] [179.2, 179.2] [23.7, 27.7] 716 213 10.1016/j.jallcom.2013.11.173 LaFe(11-x)Six x = 2.2 73.33 18.33 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 8.33 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting    0            0.05 249  1.5 2.0 252.1 40.2 717    x = 1.2 81.67 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 8.33 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 100 1373              0.05 187  1.5 14.8 196.1 6.7 718    x = 1.4 80.00 11.67 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 8.33 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 100 1373  0         0   0.05 191 719 18 10.1088/0953-8984/12/46/101 La(Fe0.98Co0.02)11.7Al1.3  81.90 0.00 9.29 0.00 1.67 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1273              0.02 198  [2, 5] [5.8, 10.6] [197.8, 202.6] [35.5, 53.6] 720 45 10.1088/0953-8984/15/43/020 LaFe(13-x)Six x = 1.6 81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1273            11.465   203 721    x = 2.0 78.57 14.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1273            11.461   235 722    x = 2.6 74.29 18.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1273  0         0 11.443   249 723 46 10.1088/0022-3727/41/24/245005 La(1-x)PrxFe10.7Co0.8Si1.5 x = 0.0 76.43 10.71 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373            11.48  0.01 285.1  [2, 5] [7.1, 13.6] [283.9, 285] [25.5, 35.1] 724    x = 0.1 76.43 10.71 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.43 0.00 0.00 0.71 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373            11.473  0.01 283.1 725    x = 0.2 76.43 10.71 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373            11.467  0.01 280.1  [2, 5] [7.2, 13.6] [279, 278.9] [24.4, 35.1] 726    x = 0.3 76.43 10.71 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373            11.461  0.01 279.1 727    x = 0.4 76.43 10.71 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 4.29 0.00 0.00 2.86 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373            11.454  0.01 274.2  [2, 5] [7.4, 14.2] [273, 275.1] [22.7, 32.2] 728    x = 0.5 76.43 10.71 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 3.57 0.00 0.00 3.57 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373            11.45  0.01 272.1  [2, 5] [8.1, 14.6] [270.9, 273] [21.8, 31.6] 729 47 10.1088/1674-1056/22/1/017502 La(Fe(1-x)Cox)11.7Al1.3 x = 0.02 81.90 0.00 9.29 0.00 1.67 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                    [2, 5] [5.9, 10.6] [197.8, 202.8] [36.4, 53.3] 730    x = 0.04 80.23 0.00 9.29 0.00 3.34 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                    [2, 5] [4.8, 9.4] [237.5, 242.2] [40.5, 56] 731    x = 0.06 78.56 0.00 9.29 0.00 5.01 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                    [2, 5] [4.6, 9.1] [277.6, 277.6] [47.2, 62.7] 732    x = 0.08 76.89 0.00 9.29 0.00 6.69 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                    [2, 5] [4.3, 8.4] [307.6, 307.7] [54.6, 75.6] 733   LaFe11.4Al(1.6-x)Six x = 0.30 81.43 2.14 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                    [1, 2, 4, 5] [3.4, 4.2, 6.6, 7.8] [140.8, 144.8, 163.1, 168.8] [22.8, 38.2, 66, 71.4] 734    x = 0.80 81.43 5.71 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                    [1, 2, 4, 5] [5.7, 9.2, 12.2, 13.5] [180.8, 180.9, 184.8, 184.8] [12.7, 18.1, 31.1, 35.9] 735   LaFe11.03Co0.8Al(1.17-x)Six x = 0.47 78.79 3.36 5.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                    [1, 2, 4, 5] [2.6, 4.5, 7.5, 8.8] [289, 290.8, 291.1, 292.9] [31.6, 39.2, 47.6, 51.4] 736    x = 0.70 78.79 5.00 3.36 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                    [1, 2, 4, 5] [4.3, 7.7, 12.6, 14.4] [281.4, 283.1, 282.9, 283] [21.6, 26.6, 34.2, 38.1] 737    x = 0.94 78.79 6.71 1.64 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                    [1, 2, 4, 5] [5.2, 9.2, 14.8, 16.9] [279, 281.1, 280.9, 280.9] [17.4, 21.4, 28.9, 31.9] 738    x = 1.17 78.79 8.36 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                    [1, 2, 4, 5] [6.6, 11.1, 16.4, 18.5] [277.1, 277, 279, 281] [13, 16.4, 23.8, 27.1] 739   LaFe11.5Al1.5Cy x = 0.10 82.14 0.00 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.71 0.00 0.00                    [2, 5] [5.5, 9.5] [182.5, 185.3] [30.1, 48.6] 740    x = 0.20 82.14 0.00 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.43 0.00 0.00                    [2, 5] [5.8, 10.8] [211.7, 211.5] [26, 40.5] 741    x = 0.40 82.14 0.00 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 2.86 0.00 0.00                    [2, 5] [5.5, 10.4] [237.4, 237.5] [31.2, 45.1] 742    x = 0.50 82.14 0.00 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 3.57 0.00 0.00                    [2, 5] [5.1, 10.1] [253.7, 256.4] [28.3, 44.5] 743   LaFe11.5Al1.5Hx x = 0.12 82.14 0.00 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.86 0.00 0.00 0.00                    [2, 5] [5.4, 10.1] [223.2, 228] [35.7, 51.3] 744    x = 0.60 82.14 0.00 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 4.29 0.00 0.00 0.00                    [2, 5] [6.1, 11.6] [249.4, 253.4] [31.8, 46] 745    x = 1.30 82.14 0.00 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 9.29 0.00 0.00 0.00                    [2, 5] [6.7, 12.3] [297.1, 298.9] [27.9, 39.1] 746   LaFe11.5Al1.5C0.2Hx x = 0.00 82.14 0.00 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.43 0.00 0.00                    [2, 5] [6.7, 11.9] [218.5, 218.4] [28.9, 44.1] 747    x = 0.50 82.14 0.00 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 3.57 1.43 0.00 0.00                    [2, 5] [7.4, 13.4] [262, 262.1] [24, 36.7] 748    x = 1.00 82.14 0.00 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 7.14 1.43 0.00 0.00                    [2, 5] [8.5, 13.8] [309.4, 310.9] [20.1, 34.8] 749 52 10.1088/0953-8984/16/45/026 LaFe11.4Si1.6  81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 336 1273                 [1, 3, 5] [11.9, 18.4, 20.3] [200, 201.7, 205.8] [5.5, 13.5, 21.4] 750     81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 0.33 1273                 [1, 3, 5] [7.7, 16.3, 19.8] [202.9, 206.1, 209] [9.3, 16.4, 23.2] 751 111 10.1088/1009-1963/16/12/049 La(1-x)PrxFe11.5Si1.5 x = 0.0 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373            11.467   194.1  5 22.9 201.0 20.8 752    x = 0.1 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.43 0.00 0.00 0.71 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373            11.462   191.1  5 25.8 199.4 21.3 753    x = 0.2 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373            11.459   188.1  5 26.1 194.7 20.7 754    x = 0.3 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373            11.453   185.1  5 28.5 192.9 19.1 755    x = 0.4 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 4.29 0.00 0.00 2.86 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373            11.449   182  5 27.0 188.4 18.4 756    x = 0.5 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 3.57 0.00 0.00 3.57 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373            11.444   181.1  5 28.4 190.3 19.1 757 142 10.1088/0022-3727/37/18/001 La(Fe0.88Al0.12)13Cx x = 0.2 81.71 0.00 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.43 0.00 0.00 arc_or_ind_melting 360 1173               217  [1, 3, 5] [2.5, 6.6, 9.4] [212.4, 217.2, 218.4] [32.9, 43.6, 53.2] 758    x = 0.4 81.71 0.00 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 2.86 0.00 0.00 arc_or_ind_melting 360 1173               247  [1, 3, 5] [2.3, 6.1, 8.9] [247.2, 247.2, 248.6] 759    x = 0.6 81.71 0.00 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 4.29 0.00 0.00 arc_or_ind_melting 360 1173               266  [1, 3, 5] [2.2, 5.6, 8.2] [262.2, 262.4, 263.3] 760 171 10.1016/j.matdes.2017.05.038 La0.9Pr0.1Fe11.2Co0.7Si1.1  80.00 7.86 0.00 0.00 5.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.43 0.00 0.00 0.71 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323            11.474  0.01 259  [1, 2, 4, 5] [5.8, 9.5, 13.9, 15.7] [260.3, 260.3, 260.3, 260.2] [11.4, 14.7, 22.3, 25.2] 761   La0.9Ho0.1Fe11.2Co0.7Si1.1  80.00 7.86 0.00 0.00 5.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.43 0.00 0.00 0.00 0.00 0.71 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323            11.47  0.01 263  [1, 2, 4, 5] [3.3, 6.1, 9.7, 10.9] [265.3, 265.2, 265, 265.2] [18.2, 20.5, 27.2, 30.6] 762 179 10.1016/s1002-0721(16)60026-1 LaFe11.3Co0.4Si1.3C0.15  80.71 9.29 0.00 0.00 2.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.07 0.00 0.00 arc_or_ind_melting 3  90.8 5.9    3.4    1 100      2 9.0 254.9 18.0 763     80.71 9.29 0.00 0.00 2.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.07 0.00 0.00 arc_or_ind_melting 12  95.6 2.3    2.1    1 100      2 9.8 254.9 16.3 764     80.71 9.29 0.00 0.00 2.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.07 0.00 0.00 arc_or_ind_melting 72  95.7 1.0    3.3    1 100      2 9.9 256.0 15.4 765     80.71 9.29 0.00 0.00 2.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.07 0.00 0.00 arc_or_ind_melting 168  98.8 0.7    0.5    1 100      2 8.8 259.1 17.3 766 193 10.1088/0953-8984/9/35/019 La(1-x)CexFe10.4Si2.6 x = 0.0 74.29 18.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 12 1350            11.439   239 767    x = 0.1 74.29 18.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.43 0.00 0.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 12 1350            11.425   236 768    x = 0.2 74.29 18.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 12 1350            11.418   231 769    x = 0.3 74.29 18.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 12 1350            11.407   230 770    x = 0.4 74.29 18.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 4.29 0.00 2.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 12 1350            11.394   226 771    x = 0.5 74.29 18.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 3.57 0.00 3.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 12 1350            11.386   224 772    x = 0.6 74.29 18.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.86 0.00 4.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 12 1350            11.38   221 773    x = 0.7 74.29 18.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.14 0.00 5.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 12 1350            11.364   217 774    x = 0.8 74.29 18.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.43 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 12 1350            11.35   215 775    x = 0.9 74.29 18.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.71 0.00 6.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 12 1350            11.342   212 776    x = 1.0 74.29 18.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 12 1350            11.333   209 777 201 10.1016/j.jmst.2017.11.023 LaFe11.6Si1.4  82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 1 1373 76.1 17.6 6.3       1 100   0.05 187.6  [1, 2, 3] [11.1, 19.6, 21] [184.8, 187.5, 187.4] [6.1, 9, 12.7] 778     82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 3 1373 89.8 6.4 3.8       1 100   0.05 188.8  [1, 2, 3] [11.8, 20.6, 22.2] [185, 187.7, 187.5] [6, 8.9, 12.5] 779 625 10.1016/s1002-0721(12)60210-5 LaFe(13-y)SiyC0.2  y = 0.8 87.14 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.43 0.00 0.00 arc_or_ind_melting 408 1353 51.3 39.2 9.5       1 100               ΔS values in Fig. 5c are affected by local peaks; the peaks were ignored 780    y = 1.0 85.71 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.43 0.00 0.00 arc_or_ind_melting 408 1353 68.8 25.2 6.0       1 100    206  [2, 3] [10.9, 12.3] [204.5, 204.6] [10, 12.8] 781    y = 1.2 84.29 8.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.43 0.00 0.00 arc_or_ind_melting 408 1353 96.4 3.6 0.0       1 100    215  [2, 3] [18.6, 19.9] [213.1, 214.1] [8, 13.7] 782    y = 1.3 83.57 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.43 0.00 0.00 arc_or_ind_melting 408 1353 98.4 1.6 0.0       1 100 783    y = 1.4 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.43 0.00 0.00 arc_or_ind_melting 408 1353 100.0 0.0 0.0       1 100    220  [2, 3] [19.9, 21.6] [218.5, 218.5] [8.7, 12.3] 784   LaFe(13-y)SiyC0.2  y = 0.8 87.14 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.43 0.00 0.00 arc_or_ind_melting 72 1353 22.7 62.4 14.9       1 100 785    y = 1.0 85.71 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.43 0.00 0.00 arc_or_ind_melting 72 1353 64.6 27.4 8.0       1 100 786    y = 1.2 84.29 8.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.43 0.00 0.00 arc_or_ind_melting 72 1353 89.0 9.3 1.7       1 100 787    y = 1.3 83.57 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.43 0.00 0.00 arc_or_ind_melting 72 1353 95.3 4.3 0.4       1 100 788    y = 1.4 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.43 0.00 0.00 arc_or_ind_melting 72 1353 94.3 0.7 5.0       1 100 789 659 10.4028/www.scientific.net/amm.84-85.667 LaFe11.1Co0.8Si1.1B0.2  79.29 7.86 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 1.43 arc_or_ind_melting 225 1353            11.448  0.05 285  1.5 5.9 286 20.5 790   LaFe11.1Co0.8Si1.1B0.25  79.29 7.86 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 1.79 arc_or_ind_melting 225 1353            11.501  0.05 290  1.5 5.3 282 791 660 10.1016/s1002-0721(10)60459-0 LaFex*11.6Si1.4 x = 0.96 82.27 10.34 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.39 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting              11.433   190.2  2 15.2 191.1 8.6      ΔS data with small number of points, high uncertainty 792    x = 0.98 82.57 10.17 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.26 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting              11.435   188.3  2 16.7 186.9 7.1 793    x = 1.00 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting              11.451   191.1  2 17.8 188.1 7.1 794    x = 1.02 83.14 9.84 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.03 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting              11.454   191.5  2 24.7 189 4.6 795 900 10.1002/aelm.201700636 La0.7Ce0.3Fe11.48Mn0.12Si1.4  82.00 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.86 0.00 0.00 0.00 5.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 20 1393               133 796   La0.7Ce0.3Fe11.48Mn0.12Si1.4H1.8  82.00 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.86 0.00 0.00 0.00 5.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.86 0.00 0.00 0.00 melt_spinning 20 1393  4.9        0 4.9    299.5  2 14.5 797 902 10.1002/mdp2.96 LaFe11.7Si1.2Mn0.1  84.34 7.65 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.98 0.00 0.00 0.00 7.02 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1373 89         0 89    170 1.3 2 20.4 176.9 11 798     81.67 8.24 0.00 0.00 0.00 0.00 0.00 0.00 1.43 0.00 1.68 0.00 0.00 0.00 6.99 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 24 1373 78         0 78    186  2 7.5 189 16.4 799     82.96 9.09 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.21 0.00 0.00 0.00 6.73 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 suction_casting 72 1373 86         0 86    175 1.1 2 10.5 178.6 14.9 800 904 10.1002/pssr.201700143 LaFe11.74Mn0.06Si1.20  83.86 8.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.43 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting                1 180.3 3 [1, 2] [16.5, 18] [173.5, 176.3] 801   LaFe11.76Mn0.06Si1.18H1.65  83.86 8.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.43 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 11.79 0.00 0.00 0.00 arc_or_ind_melting                1 342 1.9 [1, 2] [19, 20.4] [338.4, 340.4] 802 906 10.1007/s10948-014-2532-1 LaFe11.5Si1.5B0.2  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 1.43 arc_or_ind_melting 504 1393              0.01 200 6 3 13 803   La0.7Pr0.3Fe11.5Si1.5B0.2  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 1.43 arc_or_ind_melting 504 1393  0         0   0.01 190 6 3 17.9 804 907 10.1007/s11664-016-4626-y La0.8Ce0.2 Fe11.5Si1.5  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 0.166 1273              0.1 193  1.5 9.7       1 805     82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 0.25 1273              0.1 188  1.5 23       1 806     82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 0.333 1273              0.1 183  1.5 33.8       1 807     82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 0.5 1273              0.1 184  1.5 31.4       1 808     82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 1 1273              0.1 183  1.5 32.8       1 809 908 10.1007/s12598-011-0395-1 La(1-x)CexFe11.5Si1.5 x = 0.00 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 7 1480            11.472  0.02 196 4.1 2 12.8       1 Averaged annealing conditions 810    x = 0.10 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.43 0.00 0.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 7 1480              0.02 188 6.6 2 32.2       1 811    x = 0.20 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 7 1480              0.02 180 6.1 2 34.8       1 812    x = 0.35 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 4.64 0.00 2.50 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 7 1480            11.445  0.02 168 11.7 2 57.3       1 813 910 10.1007/s12598-017-0917-6 LaFe11.35Co0.6Si1.05  81.07 7.50 0.00 0.00 4.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323 95 5        0 100 11.479  0.01 268  [0.5, 1, 2] [1.4, 5.3, 12.2]       1 814     81.07 7.50 0.00 0.00 4.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323 95 5        0 100 11.479  0.01 268  1.5 8.7       1 815     81.07 7.50 0.00 0.00 4.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323 95 5        0 100 11.479  0.01 268  2.5 15.9       1 816     81.07 7.50 0.00 0.00 4.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323 95 5        0 100 11.479  0.01 268  3 19.7       1 817 911 10.1007/s12598-021-01849-3 La0.7Ce0.3Fe(11.55-y)MnySi1.45H1.8 y = 0.175 81.25 10.36 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.25 0.00 0.00 0.00 5.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.86 0.00 0.00 0.00 melt_spinning 20 1393              0 284.9 818    y = 0.190 81.14 10.36 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.36 0.00 0.00 0.00 5.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.86 0.00 0.00 0.00 melt_spinning 20 1393              0 282.6  1 15.6 819    y = 0.220 80.93 10.36 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.57 0.00 0.00 0.00 5.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.86 0.00 0.00 0.00 melt_spinning 20 1393              0 278.2  1 14 820    y = 0.235 80.82 10.36 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.68 0.00 0.00 0.00 5.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.86 0.00 0.00 0.00 melt_spinning 20 1393              0 274  1 15.1 821   La0.7Ce0.3Fe(11.55-y)MnySi1.45 y = 0.175 81.25 10.36 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.25 0.00 0.00 0.00 5.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 20 1393  0         0   0 129.3 822    y = 0.190 81.14 10.36 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.36 0.00 0.00 0.00 5.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 20 1393  0         0   0 126.2 823    y = 0.220 80.93 10.36 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.57 0.00 0.00 0.00 5.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 20 1393  0         0   0 117.9 824    y = 0.235 80.82 10.36 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.68 0.00 0.00 0.00 5.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 20 1393  0         0   0 114.4 825   La0.7Ce0.3Fe(11.5-x)MnxSi1.5H1.8 x = 0.125 81.25 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.89 0.00 0.00 0.00 5.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.86 0.00 0.00 0.00 melt_spinning 20 1393              0 294.4  1 10 826    x = 0.200 80.71 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.43 0.00 0.00 0.00 5.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.86 0.00 0.00 0.00 melt_spinning 20 1393              0 279.8  1 7.9 827    x = 0.220 80.57 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.57 0.00 0.00 0.00 5.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.86 0.00 0.00 0.00 melt_spinning 20 1393 95.4 4.6        0 100   0 276  1 6.3 828    x = 0.260 80.29 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.86 0.00 0.00 0.00 5.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.86 0.00 0.00 0.00 melt_spinning 20 1393              0 273.5  1 5.95 829 912 10.1016/j.actamat.2012.04.027 LaFe(12-x)SiCox x = 0.0 85.71 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                   2.4 1.9 6.1 176.9 830    x = 0.3 83.57 7.14 0.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                   2 1.9 5.5 214.2 831    x = 0.4 82.86 7.14 0.00 0.00 2.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                   0 1.9 4 231.8 832    x = 1.0 78.57 7.14 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                   1.7 1.9 3.1 297.7 833    x = 1.3 76.43 7.14 0.00 0.00 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                   0 1.9 2.6 322 834 914 10.1016/j.actamat.2020.01.030 LaFe13.92Si1.4  85.29 8.58 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.13 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 24 1323               194.5 0.3 [1, 2, 5] [4, 6.5, 10.7]       1 835     85.29 8.58 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.13 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 72 1323               187.9 1.4 [1, 2, 5] [6.7, 9.7, 13.2]       1 836 916 10.1016/j.actamat.2021.116687 (La(1-x)Cex)2Fe11Si2 x = 0.0 78.57 14.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 12 1423                 [1, 2] [10.8, 15.6]       1 837    x = 0.4 78.57 14.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 4.29 0.00 2.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 12 1423              0.05 172 8.5 [1, 2] [18.3, 21.1] [170.6, 170.6] [3.7, 7.0]     1 838   (La(1-x)Cex)2Fe11Si2H1.8 x = 0.0 78.57 14.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.86 0.00 0.00 0.00 arc_or_ind_melting 12 1423                 [1, 2] [8.0, 11.3]       1 839    x = 0.4 78.57 14.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 4.29 0.00 2.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.86 0.00 0.00 0.00 arc_or_ind_melting 12 1423              0.05 313 1 [1, 2] [9.8, 12.1] [314.5, 314.5] [5, 9.3]     1 840   (La(1-x)Cex)2Fe11Si2 x = 0.1 78.57 14.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.43 0.00 0.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 12 1423                 [1, 2] [11.0, 15.4]       1 841    x = 0.2 78.57 14.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 12 1423                 [1, 2] [13.5, 16.6]       1 842    x = 0.3 78.57 14.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 12 1423                 [1, 2] [14.5, 18.7]       1 843   (La(1-x)Cex)2Fe11Si2H1.8 x = 0.1 78.57 14.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.43 0.00 0.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.86 0.00 0.00 0.00 arc_or_ind_melting 12 1423                 [1, 2] [9.5, 12.0]       1 844    x = 0.2 78.57 14.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.86 0.00 0.00 0.00 arc_or_ind_melting 12 1423                 [1, 2] [9.6, 12.1]       1 845    x = 0.3 78.57 14.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.86 0.00 0.00 0.00 arc_or_ind_melting 12 1423                 [1, 2] [9.7, 12.3]       1 846 917 10.1016/j.actamat.2021.117286 La0.7Ce0.3)1.0Mn0.34Fe11.06Si1.6  79.00 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.43 0.00 0.00 0.00 5.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1323 93 7 0 0      1 100 11.4493  1 101 1 [2, 5] [8.6, 11.4]  [17.6, 35.9]     0 847   (La0.7Ce0.3)1.1Mn0.34Fe11.06Si1.6  78.44 11.35 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.41 0.00 0.00 0.00 5.46 0.00 2.34 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1323 99.1 0 0.9 0      1 100 11.4522  1 74 8 [2, 5] [9.5, 12.6]  [20.7, 40.9]     0 848   (La0.6Ce0.4)1.1Mn0.34Fe11.06Si1.6  78.44 11.35 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.41 0.00 0.00 0.00 4.68 0.00 3.12 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1323 87.8 1.5 1 9.7      1 100 11.45  1 64 1.5 [2, 5] [7.8, 10.4]  [21.4, 45.5]     0 849   (La0.6Ce0.4)1.0Mn0.40Fe11.06Si1.6  78.66 11.38 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.84 0.00 0.00 0.00 4.27 0.00 2.84 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1323 85.7 7.6 1 5.7      1 100 11.45  1 69 0 [2, 5] [4.4, 7.3]  [26.8, 50.8]     0 850   (La0.6Ce0.4)1.1Mn0.40Fe11.06Si1.6  78.11 11.30 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.82 0.00 0.00 0.00 4.66 0.00 3.11 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1323 83.7 7.4 1 7.9      1 100 11.4495  1 31 1 [2, 5] [5.4, 8.6]  [31.9, 53.6]     0 851 920 10.1016/j.intermet.2015.03.012 La1-xFe11.4+xSi1.6  x = 0 81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323              0.05 198.9 2.6 [2, 5] [18.4, 22.4]  [NaN, 17.7]     1 852    x = 0.05 81.79 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.79 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323              0.05 203.2 4.1 [2, 5] [17.5, 21.9]  [NaN, 17.8]     1 853    x = 0.1 82.14 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323              0.05 205.2 2.3 [2, 5] [9.7, 14.6]  [NaN, 20.4]     1 854    x = 0.15 82.50 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.07 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323              0.05 205.8 2.4 [2, 5] [11.8, 17.1]  [NaN, 19.7]     1 855    x = 0.2 82.86 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323              0.05 218.2 0.9 [2, 5] [8.0, 13.7]  [NaN, 23.4]     1 856 921 10.1016/j.intermet.2017.10.020 LaxFe11.5Si1.5 x = 1 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 100 1423              0.05 198.1 3.5 3 17.1  13.8     1 857    x = 1.1 81.56 10.64 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.80 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 100 1423              0.05 192.5 3.4 3 18.3  13.8     1 858    x = 1.2 80.99 10.56 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 8.45 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 100 1423              0.05 194.1 3.7 3 19.8  13.2     1 859    x = 1.3 80.42 10.49 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 9.09 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 100 1423              0.05 191.7 4.6 3 18.3  13.2     1 860 922 10.1016/j.intermet.2018.10.002 La2-xCexFe11Si2 x = 0.2 73.33 13.33 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 12.00 0.00 1.33 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 12 1423              0.05 192 0 [0.5, 1, 1.5, 2] [6.0, 11.1, 14.6, 15.7]  [4.5, 5.7, 6.3, 7.7]     1 861    x = 0.4 73.33 13.33 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 10.67 0.00 2.67 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 12 1423              0.05 186 2.1 [0.5, 1, 1.5, 2] [10.3, 14.5, 15.4, 16.5]  [3.4, 5.8, 7.1, 9.5]     1 862    x = 0.6 73.33 13.33 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 9.33 0.00 4.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 12 1423              0.05 179 4.8 [0.5, 1, 1.5, 2] [11.2, 13.3, 17.7, 18.7]  [3.2, 6.0, 6.7, 8.9]     1 863    x = 0.8 73.33 13.33 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 8.00 0.00 5.33 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 12 1423              0.05 169 8.1 [0.5, 1, 1.5, 2] [6.2, 18.4, 20.7, 21.1]  [5.5, 3.8, 5.7, 7.5]     1 864    x = 1.0 73.33 13.33 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.67 0.00 6.67 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 12 1423              0.05 169 5.5 [0.5, 1, 1.5, 2] [3.6, 9.4, 10, 10.7]  [5.6, 4.9, 7.1, 9.5]     1 865    x = 1.2 73.33 13.33 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.33 0.00 8.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 12 1423              0.05 170 5.1 [0.5, 1, 1.5, 2] [1.7, 3.5, 4.2, 4.6]  [6.3, 6.3, 8.6, 10.9]     1 866 926 10.1016/j.intermet.2021.107269 La0.7(La–Ce)0.3FexAl11.5− xSi1.5/La0.999Ce0.001FexAl11.5-xSi1.5 x = 11 78.57 10.71 3.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.01 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 100 1423              0.05 211.3 2.2 2 4.8       1 867    x = 11.1 79.29 10.71 2.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.01 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 100 1423              0.05 206.3 2.5 2 6.2       1 868    x = 11.2 80.00 10.71 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.01 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 100 1423              0.05 194.3 2.4 2 10.4       1 869    x = 11.3 80.71 10.71 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.01 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 100 1423              0.05 188.8 3.5 2 15.1       1 870    x = 11.4 81.43 10.71 0.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.01 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 100 1423              0.05 184.3 5.2 2 23.1       1 871    x = 11.5 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.01 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 100 1423              0.05 184.3          1 872 928 10.1016/j.jallcom.2013.12.193 LaFe11.5Al1.5Bx x = 0.1 82.14 0.00 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.71 arc_or_ind_melting 480 1223              0.01 178  [2, 3, 5] [7.5, 7.6, 9.7]  [22, 22, 21.3]     1 873    x = 0.2 82.14 0.00 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 1.43 arc_or_ind_melting 480 1223              0.01 185  [2, 3, 5] [7.3, 7.4, 9.3]  [19.3, 19.2, 20.2]     1 874    x = 0.3 82.14 0.00 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 2.14 arc_or_ind_melting 480 1223              0.01 189  [2, 3, 5] [7.1, 7.3, 9.2]  [18.6, 18.9, 17.7]     1 875 929 10.1016/j.jallcom.2014.02.163 La1.3Fe11.7Si1.3  81.82 9.09 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 9.09 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1323              0.1 198  [0.6, 0.8, 1] [21.8, 22.5, 23]  [2.2, 2.9, 3.8]     1 Sintering 876   La1.3Fe11.83Si1.17  82.73 8.18 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 9.09 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1323              0.1 195  [0.6, 0.8, 1] [22.7, 24.2, 24.6]       1 877 930 10.1016/j.jallcom.2015.07.133 LaFe11.5Al1.5Cy y = 0.1 82.14 0.00 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.71 0.00 0.00 arc_or_ind_melting 480 1223              0.01 190.1  [2, 5] [5.4, 9.5]  [30.1, 48.3]     1 878    y = 0.2 82.14 0.00 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.43 0.00 0.00 arc_or_ind_melting 480 1223              0.01 217.3  [2, 5] [5.7, 10.8]  [28.2, 40.7]     1 879    y = 0.3 82.14 0.00 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 2.14 0.00 0.00 arc_or_ind_melting 480 1223              0.01 234.6          1 880    y = 0.4 82.14 0.00 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 2.86 0.00 0.00 arc_or_ind_melting 480 1223              0.01 242.8  [2, 5] [5.5, 10.4]  [31.1, 43.5]     1 881    y = 0.5 82.14 0.00 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 3.57 0.00 0.00 arc_or_ind_melting 480 1223              0.01 260.5  [2, 5] [5.2, 10.1]  [28.7, 45.5]     1 882 931 10.1016/j.jallcom.2016.01.211 LaFe11.5Si1.5  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 2 1273              0.01 194  [1, 6] [11.4, 22.0]  [5.2, 25.2]     1 Wheel speed 35 m/s 883 932 10.1016/j.jallcom.2016.11.360 La1 Fe11.09 Co0.86 Si1.05  79.21 7.50 0.00 0.00 6.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting                0.05 284.5 3.3 2 8.7  18.6 1.9 3.3   1 Reactive sintering 884   La1 Fe10.81 Co1.18 Si1.01  77.21 7.21 0.00 0.00 8.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting                0.05 316.9 3.8 2 7.2  23.7 1.9 3   1 885   La1 Fe10.63 Co1.33 Si1.04  75.93 7.43 0.00 0.00 9.50 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting                0.05 325.1 3.3 2 6.6  26.2 1.9 2.6   1 886   La1 Fe10.54 Co1.43 Si1.03  75.29 7.36 0.00 0.00 10.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting                0.05 335 2.2 2 6.2  28.8 1.9 2.5   1 887 935 10.1016/j.jallcom.2018.01.381 La0.8Ce0.2Fe12.5Mn0.2Si1.3  83.33 8.67 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.33 0.00 0.00 0.00 5.33 0.00 1.33 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 192 1323              0.05 152  [1, 2, 3, 4, 5] [11.9, 12.4, 13.5, 14.4, 14.9]  [6.1, 11.8, 17.1, 21.8, 21.6]     1 888 936 10.1016/j.jallcom.2019.06.069 La(Fe0.99Ni0.01)11.5Si1.5  81.32 10.7142857143 0.00 0.00 0.00 0.00 0.00 0.82 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 100 1323              0.05 199.9 2.9 [0.5, 1, 2, 3, 4, 5] [2.2, 5.3, 8.8, 11.3, 12.9, 14.0]  [7.3, 9.1, 12.9, 17.2, 21.4, 25.4]     1 889     81.32 10.7142857143 0.00 0.00 0.00 0.00 0.00 0.82 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 100 1373              0.05 200.2 1 [0.5, 1, 2, 3, 4, 5] [4.9, 12.2, 15.8, 18.2, 19.6, 20.8]  [6.1, 5.7, 10.4, 15.5, 19.4, 23.2]     1 890 937 10.1016/j.jallcom.2019.06.082 La1.7Fe11.6Si1.4  78.91 9.52 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 11.56 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 strip_casting 12 1323              0.05 181.6 2.9 [0.5, 1, 1.5, 2] [11.9, 13.6, 15.5, 16]  [3.3, 6.1, 8.9, 10.9] 891 940 10.1016/j.jallcom.2020.153846  LaFe11Co0.8Si1.2  78.57 8.57 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 strip_casting 24 1323                 2 6.6 282.5 24 892 983 10.1063/1.4992057 La0.8Ce0.2(Fe0.95Co0.05)11.8Si1.2  80.07 8.57 0.00 0.00 4.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 strip_casting 2 1323 81.7 15 3.3       0 100 11.4614  0.05 250.4  [2, 5] [2.8, 5.9] [248, 250] [22.4, 33]     1 893     80.07 8.57 0.00 0.00 4.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 strip_casting 6 1323 89.3 7.5 3.2       0 100 11.4635  0.05 249.7  [2, 5] [10.4, 16.4] [247, 249] [15, 25.3]     1 894     80.07 8.57 0.00 0.00 4.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 strip_casting 12 1323 93.5 4 2.5       0 100 11.4642  0.05 247.5  [2, 5] [12.5, 18.1] [245, 246] [10.3, 24.16]     1 895     80.07 8.57 0.00 0.00 4.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 strip_casting 18 1323 88.3 11.3 0.4       0 100 11.4633  0.05 247.6  [2, 5] [11.7, 17.5] [246, 248] [13.7, 23.8]     1 896     80.07 8.57 0.00 0.00 4.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 strip_casting 24 1323 89.2 10.5 0.3       0 100 11.4628  0.05 247.9  [2, 5] [11.7, 17.4] [246, 248] [13.7, 24.5]     1 897 985 10.1063/251.5006089 La1-x(La0.35Ce0.65)xFe11.5Si1.5 x = 0  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 100 1423            11.4713  0.05 198.1 3.5 3 17.2 201.3 13.8     1 898    x = 0.1 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.68 0.00 0.46 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 100 1423            11.469  0.05 193.2 5.2 3 19.2 195.4 12.64     1 899    x = 0.2 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.21 0.00 0.93 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 100 1423            11.4633  0.05 188.8 6.3 3 23.5 190.7 11.8     1 900    x = 0.3 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.75 0.00 1.39 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 100 1423            11.4593  0.05 184.3 8.2 3 26.6 186.7 12.4     1 901 987 10.1063/1.5139449 LaFe11.5Si1.5C0.13  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.93 0.00 0.00 arc_or_ind_melting 48 1353              0.01 214.3 2.8 2 15.97 213 10.1     1 902 989 10.1088/1361-6463/aa893e LaFe11.74Mn0.06Si1.20  83.86 8.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.43 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting  1323              1 180.2 5.4          Sintered and annealead  903 990 10.1088/1361-6463/aaad28 LaFe11.85Si1.15  84.64 8.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 4 1323              1 205 10 5 10.04       1 904 992 10.1088/1674-1056/24/7/077503 La1.7Fe11.6Si1.4  78.91 9.52 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 11.56 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 72 1323              0.2 173.5  [0.2, 0.4, 0.6, 1.0, 1.4, 1.8, 2] [5.53, 12.15, 14.87, 14.87, 15.02, 15.69, 15.89] [173.5, 173.5, 173.5, 174.9, 177, 177.8, 178] [3, 3.1, 3.9, 6.9, 9.6, 12, 12.9]     1 905   La1.0Fe11.6Si1.4  82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting  1323              0.2 192.6  2 20.38 201.2 9.9     1 906   La1.7Fe11.6Si1.4H2.9  78.91 9.52 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 11.56 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 19.73 0.00 0.00 0.00 arc_or_ind_melting 72 1323                 [0.2, 0.4, 0.6, 1.0, 1.4, 1.8, 2] [2, 5, 8.3, 13.1, 14.8, 15.9, 16.7] [344.4, 344.4, 344.4, 344.4, 344.4, 346, 346.3] [5.97, 5.5, 4.8, 4.7, 6.4, 7.7, 9.3]     1 907   La1.0Fe11.6Si1.4H1.9  82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 13.57 0.00 0.00 0.00 arc_or_ind_melting  1323                 2 15.6 323.5 9.7     1 908 993 10.1088/1674-1056/25/2/027501 La(Fe0.99Mn0.01)11.5Si1.5  81.32 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.82 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1353            11.5076  0 184          1 909   La(Fe0.98Mn0.02)11.5Si1.5  80.50 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.64 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1353            11.4957  0 173          1 910   La(Fe0.97Mn0.03)11.5Si1.5  79.68 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.46 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1353            11.4837  0 151          1 911   La(Fe0.99Mn0.01)11.5Si1.5H1.61  81.32 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.82 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 11.50 0.00 0.00 0.00 arc_or_ind_melting 240 1353            11.6248  0 313  [1, 2] [7.9, 10.9] [316.8, 317.7] [6.7, 11.4]     1 912 994 10.1088/1674-1056/26/6/067502 La0.8Pr0.2Fe11.4Si1.6  81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 672 1393              0.01 195.1 8.9 3 21.75 200.8 14.5     1 913   La0.8Pr0.2Fe11.4Si1.6H0.13  81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.93 0.00 0.00 0.00 arc_or_ind_melting 672 1393              0.01 327.7 6.1 3 14.85 323.4 9.7     1 914   La0.6Pr0.4Fe11.4Si1.6  81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 4.29 0.00 0.00 2.86 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 672 1393              0.01 192.8 6.3 3 21.45 196.1 13.7     1 915   La0.6Pr0.4Fe11.4Si1.6H0.87  81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 4.29 0.00 0.00 2.86 0.00 0.00 0.00 0.00 0.00 0.00 100.00 6.21 0.00 0.00 0.00 arc_or_ind_melting 672 1393              0.01 321.1 7 3 17.9 320 12.9     1 916 997 10.1103/PhysRevB.94.134405  a 80.14 9.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 3.29 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323              1 116 1.1         1 917    b 80.93 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.64 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323              1 129 1.7 [1.5, 8] [11.46, 20] [130.5, 142.4] [11.3, 41.8]     1 918    c 81.50 9.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.14 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323              1 138 2.6         1 919    d 82.13 9.08 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.64 0.00 0.00 0.00 7.15 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323              1 150 2.6         1 920    e 83.23 8.78 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.86 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323              1 167 3.4 [1.5, 8] [17, 28.5] [177.25, 189.35] [10, 34.3]     1 921    f 83.86 8.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.43 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323              1 173 4.3         1 922    m 80.14 9.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 3.29 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 11.79 0.00 0.00 0.00 arc_or_ind_melting 240 1323              1 270 2.3         1 923    n 80.93 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.64 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 11.79 0.00 0.00 0.00 arc_or_ind_melting 240 1323              1 285 2 [1.5, 8] [14.2, 21.3] [285.9, 291.4] [7.5, 31.8]     1 924    o 81.50 9.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.14 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 11.79 0.00 0.00 0.00 arc_or_ind_melting 240 1323              1 295 2.6         1 925    p 82.55 8.73 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.57 0.00 0.00 0.00 7.15 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 11.80 0.00 0.00 0.00 arc_or_ind_melting 240 1323              1 310 2.6         1 926    q 83.18 8.59 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.07 0.00 0.00 0.00 7.16 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 11.81 0.00 0.00 0.00 arc_or_ind_melting 240 1323              1 319 2.6         1 927    r 84.00 8.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.43 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 11.79 0.00 0.00 0.00 arc_or_ind_melting 240 1323              1 339 3.4         1 928 998 10.1103/PhysRevB.95.064411  e 82.66 8.92 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.28 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323               158  [1.5, 8] [16.3, 24.9] [162.1, 172.4] [9.7, 37.6]     1 929 999 10.1103/PhysRevLett.101.177203 LaFe11.57Si1.43  82.64 10.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 1 1323              0.01 202  [2, 5] [14.55, 20.4] [210.4, 215.4] [13.5, 23.5]     1 930   LaFe11.57Si1.43H1.64  82.64 10.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 11.71 0.00 0.00 0.00 melt_spinning 1 1323              0.01 329  [2, 5] [12.4, 19.6] [329.6, 332.3] [14.5, 26.3]     1 931 1000 10.1109/TMAG.2005.854764  x = 0.87 80.79 12.07 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 240 1323              0.02 208  2 14.7  9.7     1 932 1001 10.1109/TMAG.2006.879746 La(Fe0.88Si0.12)13  81.71 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 strip_casting 1 1323               189.5  [0.1, 0.2] [2.2, 5.9] [190, 191.4] [1.88, 2.6]     1 933 1002 10.1109/TMAG.2011.2147295 La0.5Pr0.5Fe11.4Si1.6H1.33  81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 3.57 0.00 0.00 3.57 0.00 0.00 0.00 0.00 0.00 0.00 100.00 9.50 0.00 0.00 0.00 melt_spinning 3 1323              0.01 314  5 17.4 317 20.4     1 934   La0.6Pr0.5Fe11.4Si1.6H1.47  80.85 11.35 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 4.26 0.00 0.00 3.55 0.00 0.00 0.00 0.00 0.00 0.00 100.00 10.43 0.00 0.00 0.00 melt_spinning 3 1323              0.01 321  5 18.9 323 20.39     1 935   La0.7Pr0.5Fe11.4Si1.6H1.64  80.28 11.27 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 4.93 0.00 0.00 3.52 0.00 0.00 0.00 0.00 0.00 0.00 100.00 11.55 0.00 0.00 0.00 melt_spinning 3 1323              0.01 331  5 15.9 330 24.1     1 936   La0.6Pr0.5Fe11.4Si1.6  80.85 11.35 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 4.26 0.00 0.00 3.55 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 3 1323              0.01 193  5 22.4 193 19.1     1 937 1003 10.1109/TMAG.2011.2157092 La(Fe0.89Si0.11)13  82.64 10.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 25 1323              1 190.4 938     82.64 10.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 50 1323              1 192.3 939     82.64 10.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 100 1323              1 194.3 940     82.64 10.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 300 1323              1 195 941 1004 10.1109/TMAG.2012.2196987 LaFe11.29(Si1-wAlw)1.71Hs w = 0 80.64 12.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 10.14 0.00 0.00 0.00 arc_or_ind_melting                 325.4  1.6 9.2 942    w = 0.2 80.64 9.77 2.44 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 10.30 0.00 0.00 0.00 arc_or_ind_melting                 323.3  1.6 6.5 943    w = 0.4 80.64 7.33 4.89 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 10.60 0.00 0.00 0.00 arc_or_ind_melting                 328.8  1.6 4.1 944    w = 0.6 80.64 4.89 7.33 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 11.80 0.00 0.00 0.00 arc_or_ind_melting                 325.7  1.6 3.4 945    w = 0.8 80.64 2.44 9.77 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 11.20 0.00 0.00 0.00 arc_or_ind_melting                 328  1.6 2.8 946    w = 1 80.64 0.00 12.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.40 0.00 0.00 0.00 arc_or_ind_melting                 324.7  1.6 2.25 947   LaFe11.57(Si1-wAlw)1.43Hs w = 0 82.64 10.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 10.80 0.00 0.00 0.00 arc_or_ind_melting                 331  1.6 17.5 948    w = 0.2 82.64 8.17 2.04 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 11.40 0.00 0.00 0.00 arc_or_ind_melting                 334  1.6 13.3 949    w = 0.4 82.64 6.13 4.09 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 11.73 0.00 0.00 0.00 arc_or_ind_melting                 336.7  1.6 6.7 950    w = 0.6 82.64 4.09 6.13 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 11.60 0.00 0.00 0.00 arc_or_ind_melting                 345  1.6 4.9 951    w = 0.8 82.64 2.04 8.17 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.75 0.00 0.00 0.00 arc_or_ind_melting                 348.8  1.6 4.3 952    w = 1 82.64 0.00 10.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.35 0.00 0.00 0.00 arc_or_ind_melting                 351.8  1.6 3.6 953   LaFe11.86(Si1-wAlw)1.14Hs w = 0 84.71 8.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.80 0.00 0.00 0.00 arc_or_ind_melting                 341.4  1.6 17.95 954    w = 0.2 84.71 6.51 1.63 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.84 0.00 0.00 0.00 arc_or_ind_melting                 349.5  1.6 11.65 955    w = 0.4 84.71 4.89 3.26 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 13.07 0.00 0.00 0.00 arc_or_ind_melting                 352.4  1.6 7.4 956    w = 0.6 84.71 3.26 4.89 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 13.83 0.00 0.00 0.00 arc_or_ind_melting                 367.4  1.6 5.1 957    w = 0.8 84.71 1.63 6.51 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 14.81 0.00 0.00 0.00 arc_or_ind_melting                 371.8  1.6 4.3 958    w = 1 84.71 0.00 8.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 15.11 0.00 0.00 0.00 arc_or_ind_melting                 375.7  1.6 3.8 959   LaFe11.29(Si1-wAlw)1.71 w = 0 80.64 12.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  207.2 960    w = 0.2 80.64 9.77 2.44 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  203.6 961    w = 0.4 80.64 7.33 4.89 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  201.6 962    w = 0.6 80.64 4.89 7.33 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  194.25 963    w = 0.8 80.64 2.44 9.77 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  186.35 964    w = 1 80.64 0.00 12.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  188.7 965   LaFe11.57(Si1-wAlw)1.43 w = 0 82.64 10.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  192.9 966    w = 0.2 82.64 8.17 2.04 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  186.2 967    w = 0.4 82.64 6.13 4.09 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  182 968    w = 0.6 82.64 4.09 6.13 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  169.5 969    w = 0.8 82.64 2.04 8.17 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  160.7 970    w = 1 82.64 0.00 10.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  200.7 971   LaFe11.86(Si1-wAlw)1.14 w = 0 84.71 8.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  188.1 972    w = 0.2 84.71 6.51 1.63 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  201.7 973    w = 0.4 84.71 4.89 3.26 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  205.6 974    w = 0.6 84.71 3.26 4.89 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  211.67 975    w = 0.8 84.71 1.63 6.51 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  218.8 976    w = 1 84.71 0.00 8.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  224.3 977 1005 10.1109/TMAG.2012.2199744 LaFe11.5Si1.5C0.2  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.43 0.00 0.00 arc_or_ind_melting 72 1353              0 223          1 978   LaFe11.5Si1.5C0.2  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.43 0.00 0.00 strip_casting 12 1353              0 224  [1, 1.5] [9.4, 11] [222.7, 223] [7.2, 10.1]     1 979   LaFe10.85Co0.65Si1.5C0.2  77.50 10.71 0.00 0.00 4.64 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.43 0.00 0.00 strip_casting 24 1353              0 292  [1, 1.5] [2.8, 3.8] [295, 295.3] [30, 33.8]     1 980 1007 10.1109/TMAG.2015.2439299 LaFe11.1Co0.7Si1.2  79.29 8.57 0.00 0.00 5.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 strip_casting 48 1323              0.05 269  [1, 2] [6, 9.8]  [15, 18]     1 981   LaFe11.05Co0.75Si1.2  78.93 8.57 0.00 0.00 5.36 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 strip_casting 48 1323              0.05 276  [1, 2] [5.1, 8.7]  [17, 21]     1 982   LaFe11Co0.8Si1.2  78.57 8.57 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 strip_casting 48 1323              0.05 280  [1, 2] [4.8, 8.2]  [19, 22]     1 983   LaFe10.95Co0.85Si1.2  78.21 8.57 0.00 0.00 6.07 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 strip_casting 48 1323              0.05 286  [1, 2] [4.5, 7.7]  [20, 23]     1 984   LaFe10.9Co0.9Si1.2  77.86 8.57 0.00 0.00 6.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 strip_casting 48 1323              0.05 292  [1, 2] [4.7, 7.9]  [19, 23]     1 985   LaFe11Co0.8Si1.2  78.57 8.57 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 strip_casting 24 1323              0.05 281  [1, 2] [4.8, 8.4]  [18, 20]     1 986   LaFe11Co0.8Si1.2  78.57 8.57 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 strip_casting 12 1323              0.05 278  [1, 2] [4.9, 8]  [17, 20]     1 987   LaFe11Co0.8Si1.2  78.57 8.57 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 strip_casting 24 1373              0.05 281 988 1009 10.1134/S1063776111150118 La(Fe0.86Si0.14)13  79.86 13.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00                  210 989 1010 10.12693/APhysPolA.128.87 LaFe11.14Co0.66Si1.2−xGax x = 0.1 79.57 7.86 0.00 0.71 4.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323 92 8        1 100 11.4802   271  [1, 2] [1.94, 6.4]  [16, 22]     1 990    x = 0.2 79.57 7.14 0.00 1.43 4.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323 88 12        1 100 11.4832   275  [1, 2] [1.2, 3.91]  [26, 29]     1 991    x = 0.3 79.57 6.43 0.00 2.14 4.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323 86 14        1 100 11.4866   285  [1, 2] [0.66, 2.19]  [32, 38]     1 992 1011 10.12693/APhysPolA.133.648 LaFe11.2-xMnxCo0.7Si1.1 x = 0.1 79.29 7.86 0.00 0.00 5.00 0.00 0.00 0.00 0.00 0.00 0.71 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323 92 8        1 100 11.4745   241  [1, 2, 3, 4, 5] [4.9, 8.36, 11.3, 13.4, 14.9]  [14.27, 18, 19.9, 24.4, 28]     1 993    x = 0.2 78.57 7.86 0.00 0.00 5.00 0.00 0.00 0.00 0.00 0.00 1.43 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323 91 9        1 100 11.4708   222  [1, 2, 3, 4, 5] [4.1, 6.83, 9.1, 11, 12.34]  [15.6, 20, 22.7, 25.2, 30]     1 994    x = 0.3 77.86 7.86 0.00 0.00 5.00 0.00 0.00 0.00 0.00 0.00 2.14 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1323 90 10        1 100 11.4676   198  [1, 2, 3, 4, 5] [5.2, 8.41, 11.3, 13.2, 14.54]  [11.7, 15, 22.6, 18.9, 26]     1 995 1012 10.1557/mrc.2018.105 La0.8Ce0.2(Fe0.95Co0.05)11.8Si1.2  80.07 8.57 0.00 0.00 4.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 strip_casting 12 1323               246  2 10.7  14.3 996 1013 10.2497/jjspm.54.10 La(Fe0.89Si0.11)13  82.64 10.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 strip_casting 4 1323              0.1 191 997 1014 10.3390/coatings12040534 LaFe11.5Si1.5  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 480 1393              0.01 194 2.8 3 18.3 194.6 12.4     1 998   La0.8Nd0.2Fe11.5Si1.5  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 480 1393              0.01 188 4.3 3 22.6 189.8 13.57     1 999   LaFe11.5Si1.5C0.2  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.43 0.00 0.00 arc_or_ind_melting 480 1393              0.01 232 1.3 3 16.5 232 14.7     1 1000 1015 10.3390/en13061491 vacuum GmbH  83.58 8.64 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.97 0.00 0.00 0.00 6.81 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.86 0.00 0.00 0.00 arc_or_ind_melting                 318 1001   vacuum GmbH  82.39 8.56 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.09 0.00 0.00 0.00 7.96 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.86 0.00 0.00 0.00 arc_or_ind_melting                 313 1002   vacuum GmbH  82.31 8.66 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.94 0.00 0.00 0.00 7.09 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.86 0.00 0.00 0.00 arc_or_ind_melting                 298 1003 1016 10.3390/ma15010343 LaFe11.5Si1.5C0.2  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.43 0.00 0.00 melt_spinning              11.4985   224  1.5 2.4  18.6     1 Not annealed 1004     82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.43 0.00 0.00 melt_spinning 0.05 1273            11.5036   231  1.5 6.1  13.6     1 1005     82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.43 0.00 0.00 melt_spinning 2 1273            11.5107   255  1.5 9.45  12.75     1 1006 10171017-70 10.3390/magnetochemistry701001310.1007/978-3-030-05861-6_56  LaFe9.7Co0.8Si1.5Hy y = 0 76.43 10.71 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 mech_alloying                 291.1  1 1.95 291.14 39      data from Fig.14; suspicious was wrong (chk reference 70 for correct composition) 1007   LaFe9.7Co0.8Si1.5Hy y = 1.4 76.43 10.71 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 10.00 0.00 0.00 0.00 mech_alloying                 390.8  1 2.05 390.8 32.5 1008   LaFe10.5Si1.5Hy y = 0 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 mech_alloying                 219.5 1009    y = 0.3 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 2.14 0.00 0.00 0.00 mech_alloying                 248 1010    y = 1 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 7.14 0.00 0.00 0.00 mech_alloying                 292 1011    y = 1.4 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 10.00 0.00 0.00 0.00 mech_alloying                 329.9 1012    y = 1.6 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 11.43 0.00 0.00 0.00 mech_alloying                 348.3 1013   LaFe10.18Co0.32Si1.5Hy y = 0 79.86 10.71 0.00 0.00 2.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 mech_alloying                 240.3 1014    y = 1.2 79.86 10.71 0.00 0.00 2.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 8.57 0.00 0.00 0.00 mech_alloying                 339.2 1015    y = 1.5 79.86 10.71 0.00 0.00 2.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 10.71 0.00 0.00 0.00 mech_alloying                 362.3 1016   LaFe9.69Co0.81Si1.5Hy y = 0 76.36 10.71 0.00 0.00 5.79 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 mech_alloying                 291.8 1017    y = 0.7 76.36 10.71 0.00 0.00 5.79 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 5.00 0.00 0.00 0.00 mech_alloying                 338 1018    y = 1.1 76.36 10.71 0.00 0.00 5.79 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 7.86 0.00 0.00 0.00 mech_alloying                 369.4 1019    y = 1.3 76.36 10.71 0.00 0.00 5.79 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 9.29 0.00 0.00 0.00 mech_alloying                 385.6 1020   LaFe9.5CoSi1.5Hy y = 0 75.00 10.71 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 mech_alloying                 315.9 1021    y = 1.2 75.00 10.71 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 8.57 0.00 0.00 0.00 mech_alloying                 390.3 1022    y = 1.4 75.00 10.71 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 10.00 0.00 0.00 0.00 mech_alloying                 400.4  1 2.23 408.8 31.96 1023   LaFe11.4Si1.6Hy y = 0 81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 mech_alloying                   2 22.95 219.6 13.76      1017-70 is a Ref.70 from 1017 1024    y = 0.21 81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 1.50 0.00 0.00 0.00 mech_alloying                   2 15.1 248.9 24.77 1025    y = 0.41 81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 2.93 0.00 0.00 0.00 mech_alloying                   2 15 282 23.4 1026    y = 0.86 81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 6.14 0.00 0.00 0.00 mech_alloying                   2 16.46 299.3 19.66 1027   LaFe11.5Si1.5H1.4  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 10.00 0.00 0.00 0.00 mech_alloying                   1 3.78 345.1 14.25 1028   LaFe11.2Co0.3Si1.5H1.6  80.00 10.71 0.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 11.43 0.00 0.00 0.00 mech_alloying                   1 2.85 364.9 22.16 1029   LaFe10.9Co0.6Si1.5H1.7  77.86 10.71 0.00 0.00 4.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.14 0.00 0.00 0.00 mech_alloying                   1 3.27 375.3 17.45 1030   LaFe10.7Co0.8Si1.5H1.4  76.43 10.71 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 10.00 0.00 0.00 0.00 mech_alloying                   1 2.08 390.6 33.137 1031 1018 10.3390/met12010112 LaFe11.6Si1.4  82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 strip_casting 24 1323               212  [2, 5] [5.2, 8.8]  [28.2, 49.8]     1 Best RCP value 1032 1019 10.3390/met9040432 LaFe11.6Si1.4  82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 strip_casting 72 1373              0.05 205 5.2 3 6.8 205.3 16.7     1 Centrifugal casting; sub-rapid quenching, including annealing conditions maybe misleading 1033   LaFe11.6Si1.4Zn0.03  82.68 9.98 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.21 0.00 7.13 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 strip_casting 72 1373              0.05 192 5.2 3 5.82 194.5 14.9     1 1034   LaFe11.6Si1.4P0.03  82.68 9.98 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.21 0.00 0.00 7.13 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 strip_casting 72 1373              0.05 194 8.2 3 31.15 193.6 10.4     1 1035 1020 10.4028/www.scientific.net/AMR.750-752.919 LaFe11.6Si1.4Bx x = 0 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 6 1273               190.4  1 12.48 189 6.824     1 1036    x = 0.3 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 2.14 melt_spinning 6 1273               192.4  1 12.28 190.8 5.687     1 1037    x = 0.5 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 3.57 melt_spinning 6 1273               195.8 2.8 1 11.97 194.1 8.3     1 1038    x = 0.7 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 5.00 melt_spinning 6 1273               197.7 0 1 5.75 196 15.356     1 1039 1021 10.4028/www.scientific.net/SSP.170.248 LaFe11Co0.95Si1.05  78.57 7.50 0.00 0.00 6.79 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting                   [1, 2, 3, 5] [4.3, 7, 10.1, 13.8] [295.7, 296.8, 296.9, 297.4] [12.7, 20.2, 20.9, 28.9]     1 1040 1022 10.7498/aps.70.20211085 LaFe11.5Si1.5  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1373              0.05 205.5 1041   LaFe11.25Mn0.125Co0.125Si1.5  80.36 10.71 0.00 0.00 0.89 0.00 0.00 0.00 0.00 0.00 0.89 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1373              0.05 201.3 1042   LaFe11Mn0.375Co0.125Si1.5  78.57 10.71 0.00 0.00 0.89 0.00 0.00 0.00 0.00 0.00 2.68 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1373              0.05 170 1043 942 10.1016/j.jallcom.2021.159796 LaFe11.6Si1.4  82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 strip_casting 24 1323 84.7 15.3         100 11.51  0.05 220  [1, 2] [2.6, 4] [217, 217] [27.4, 29.4]     1 1044 943 10.1016/j.jallcom.2021.162597 La1.3Fe11.6Si1.4  81.12 9.79 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 9.09 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1373 88.2 3.49    8.31     100 11.469  0.05 183 2.2 [1, 3, 5, 7] [17.9, 19.55, 21.4, 22.8] [181.9, 185.9, 189.1, 193.6] [4.34, 13.8, 22, 29.56]     1 1045   La1.7Fe11.6Si1.4  78.91 9.52 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 11.56 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1373 70.9 3.83    25.27     100 11.487  0.05 184 7.6 [1, 3, 5, 7] [13.62, 17.4, 19.5, 19.9] [181.0, 184.3, 188.3, 190.4] [4.94, 14.3, 22.7, 27.6]     1 1046 946 10.1016/j.jallcom.2022.164858 La1−xGdxFe11.5Si1.5 x = 0 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 216 1323              0.02 195 5.2 2 16.5  9.3     1 1047    x = 0.05 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.79 0.00 0.00 0.00 0.00 0.00 0.36 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 216 1323              0.02 196 5 2 15.3  9.2     1 1048    x = 0.1 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.43 0.00 0.00 0.00 0.00 0.00 0.71 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 216 1323              0.02 196 4.5 2 12.6  9.3     1 1049    x = 0.15 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.07 0.00 0.00 0.00 0.00 0.00 1.07 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 216 1323              0.02 198 3.6 2 9.5  11.6     1 1050    x = 0.2 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 1.43 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 216 1323              0.02 200 3.8 2 7.9  10.9     1 1051    x = 0.25 82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.36 0.00 0.00 0.00 0.00 0.00 1.79 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 216 1323              0.02 204 4 2 6.8  13.4     1 1052 947 10.1016/j.jmmm.2006.09.010  La(Fe1-xCox)11.4Al1.6 x = 0 81.43 0.00 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1170                 5 2.1 205.3 47.6     1 1053    x = 0.04 78.17 0.00 11.43 0.00 3.26 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1170                 5 5.3 250.75 77.4     1 1054    x = 0.08 74.91 0.00 11.43 0.00 6.51 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1170                 5 4.64 320.25 97.7     1 1055    x = 0.12 71.66 0.00 11.43 0.00 9.77 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1170                 5 4.8 369.3      1 1056   La(Fe1-xCox)11.4Si1.6 x = 0 81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1170                 5 17.58 201.7 22.67     1 1057    x = 0.04 78.17 11.43 0.00 0.00 3.26 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1170                 5 9.06 252.5 39     1 1058    x = 0.08 74.91 11.43 0.00 0.00 6.51 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1170                 5 5.1 314.6      1 1059 948 10.1016/j.jmmm.2006.10.1058  La(Fe0.88Co0.055 Si0.065)13  81.71 6.04 0.00 0.00 5.11 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 264 1323              0.1 274  [1, 2, 5] [5.1, 9.6, 17.4] [273.7, 274.4, 276] [13.7, 16.8, 26.2]     1 1060 950 10.1016/j.jmmm.2013.09.027 La0.6Pr0.5Fe11.4Si1.6  80.85 11.35 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 4.26 0.00 0.00 3.55 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1373              0.01 190 5 5 23.8 193.6 21.5     1 1061     80.85 11.35 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 4.26 0.00 0.00 3.55 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 melt_spinning 4 1373              0.01 192 3.8 5 21.8 195 21.1     1 1062 951 10.1016/j.jmmm.2014.10.035 LaFe11.6Si1.4   82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 strip_casting 5 1323              0.01 199 0 [0.5, 1, 1.5, 2] [6.4, 9.2, 12.8, 14.4] [196.5, 196.5, 199.4, 199.5] [6.5, 6.6, 9.1, 9.5]     1 1063     82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 strip_casting 12 1323              0.01 202 0 [0.5, 1, 1.5, 2] [10.66, 16.77, 18.2, 19.17] [200.6, 200.5, 200.4, NaN] [4.3, 5.5, 7.5, 9.9]     1 1064   LaFe11.6-xMnxSi1.4  x = 0.1 82.14 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.71 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 strip_casting 12 1323                 2 16.1 188.3 10.6     1 1065    x = 0.2 81.43 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.43 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 strip_casting 12 1323                 2 13.6 168.4 12.7     1 1066 953 10.1016/j.jmmm.2017.10.123 LaFe11.65Si1.35  83.21 9.64 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 72 1323                 3 12.4 212.8 16.7     1 1067 954 10.1016/j.jmmm.2017.11.047 La0.8Ce0.2Fe11.5xCoxSi1.5C0.2  x = 0.3 80.00 10.71 0.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.43 0.00 0.00 melt_spinning 10 1373            11.4576  0.01 239 1.9 [1, 2, 3, 5] [3.3, 5.9, 7.85, 10.53] [237, 236.9, 237.1, 236.9] [19.2, 23.1, 27.5, 34]     1 1068    x = 0.5 78.57 10.71 0.00 0.00 3.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.43 0.00 0.00 melt_spinning 10 1373            11.4544  0.01 253 1.2 [1, 2, 3, 5] [3.3, 5.85, 7.8, 10.68] [250.1, 250.8, 250.9, 251.8] [17.4, 26.1, 30.4, 41.8]     1 1069    x = 0.7 77.14 10.71 0.00 0.00 5.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.43 0.00 0.00 melt_spinning 10 1373            11.4536  0.01 277 0.8 [1, 2, 3, 5] [2.64, 4.8, 6.64, 9.4] [274.8, 274.9, 276.2, 277.2] [24.37, 29.13, 32.3, 40.46]     1 1070 956 10.1016/j.jmmm.2018.01.063 LaFe11.5Si1.5   82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1423              0.2 194.1 8.1 2 22.2 193.9 8.7     1 1071   La0.95Tb0.05Fe11.5Si1.5   82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.79 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.36 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1423              0.2 194.1 10.2 2 25.8 193.9 12.1     1 1072   La0.9Tb0.1Fe11.5Si1.5   82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 6.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.71 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1423              0.2 194.1 9.4 2 20 195.9 8.54     1 1073   La0.8Tb0.2Fe11.5Si1.5   82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 1.43 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1423              0.2 194.8 8.9 2 16.7 196 8.75     1 1074   La0.7Tb0.3Fe11.5Si1.5   82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 2.14 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1423              0.2 197.1 6.1 2 10.5 196.9 10     1 1075 957 10.1016/j.jmmm.2018.02.009 LaFe11.6Si1.4  82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 strip_casting 48 1323              0.05 189 7 [1, 2, 3] [18, 21.3, 22.4] [187.5, 187.5, 187.5] [3.41, 7.6, 12]     1 Centrifugal casting; sub-rapid quenching, including annealing conditions maybe misleading 1076 958 10.1016/25j.jmmm.2018.04.063  LaFe10.85Co0.75Si1.4C0.15  77.50 10.00 0.00 0.00 5.36 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.07 0.00 0.00 arc_or_ind_melting 144 1353              0.01 296  2 6.5 293 25.95     1 1077   LaFe11.4Co0.3Si1.3C0.15  81.43 9.29 0.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.07 0.00 0.00 arc_or_ind_melting 144 1353              0.01 248          1 1078   LaFe10.8Co0.9Si1.3C0.15  77.14 9.29 0.00 0.00 6.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.07 0.00 0.00 arc_or_ind_melting 144 1353              0.01 314          1 1079   LaFe11.5Si1.5  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 144 1353              0.01 199          1 1080   LaFe11.2Co0.5Si1.3C0.15  80.00 9.29 0.00 0.00 3.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.07 0.00 0.00 arc_or_ind_melting 144 1353              0.01 263          1 1081 961 10.1016/j.jmmm.2020.167652 LaFe11.6Si1.4  82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 strip_casting 24 1323 90.46 9.54         100 11.492  0.05 197  2 11.09 200 14.27     1 1082     82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 strip_casting   80.53 19.47         100 11.486  0.05 197  2 8.82 196 24.8     1 Not annealed 1083 962 10.1016/j.jmmm.2021.168932 LaFe11.7-xCoxSi1.3C0.15 x = 0.7 78.57 9.29 0.00 0.00 5.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.07 0.00 0.00 arc_or_ind_melting 336 1353              0.01 291.8  2 6.5       1 1084    x = 0.8 77.86 9.29 0.00 0.00 5.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.07 0.00 0.00 arc_or_ind_melting 336 1353              0.01 301.8  2 6       1 1085    x = 0.9 77.14 9.29 0.00 0.00 6.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.07 0.00 0.00 arc_or_ind_melting 336 1353              0.01 311.8  2 5.4       1 1086 965 10.1016/j.jssc.2012.01.030 La0.7Nd0.3Fe13 xSix x = 1.2 84.29 8.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 96 1400 94 6         100 11.45  0.2 181 9 [1, 2, 3, 4] [16.5, 27, 28, 28.8] [177.3, 177.4, 177.3, 177.3] [5.5, 7.14, 11, 15.2]     1 Thys to be taken from either from text or image. Not consistent. 1087    x = 1.4 82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 96 1400 95.9 4.1         100 11.46  0.2 188  2 19.2 187.4 10.6     1 1088    x = 1.6 81.43 11.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 96 1400 97.9 2.1         100 11.45  0.2 197  2 13 197.6 11.9     1 1089    x = 1.8 80.00 12.86 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 96 1400 98.8 1.2         100 11.45  0.2 213 5 [1, 2, 3, 4] [4.1, 7.9, 10.6, 12.5] [212.6, 212.5, 212.3, 212.3] [18, 19.3, 23.3, 26.5]     1 1090 966 10.1016/j.matlet.2013.09.045 LaFe11.5Si1.5C0.2  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.43 0.00 0.00 arc_or_ind_melting 72 1373               220  3 18.4 217.5 13     1 1091 967 10.1016/j.physb.2015.03.012 La1.7Fe11Co0.8Si1.2  74.83 8.16 0.00 0.00 5.44 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 11.56 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 24 1323              0.05 271 0 [0.5, 1, 1.5, 2] [2.3, 4.2, 5.9, 7.2] [269.4, 269.4, 269.4, 269.5] [13.2, 15.7, 17.15, 19.4]     1 Ann. conditions are suspecious for other samples in the paper  1092 969 10.1016/j.scriptamat.2014.10.002 LaFe11.6Si1.4  82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 168 1323                 2 24.7 189.2 9     1 1093 971 10.1021/acs.chemmater.9b03915  La(Fe0.92Co0.08)11.9Si1.1  78.20 7.86 0.00 0.00 6.80 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1353              1 304  [2, 5] [7.8, 14.1] [297.3, 299.1] [22.3, 32.4]     1 1094 972 10.1021/acs.jpcc.9b08629 LaFe11.5Si1.5C0.15  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.07 0.00 0.00 arc_or_ind_melting 168 1353              0.01 223  1.5 10.4 222.5 10     1 1095   LaFe11.5Si1.5C0.15 + Fe0.1  82.27 10.64 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.09 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.06 0.00 0.00 arc_or_ind_melting 168 1353              0.01 227  1.5 8.6 226.5 12.7     1 1096   LaFe11.5Si1.5C0.15 + Nb0.1  81.56 10.64 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.71 0.00 0.00 0.00 0.00 7.09 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.07 0.00 0.00 arc_or_ind_melting 168 1353              0.01 212  1.5 12 210.9 8.7     1 1097 980 10.1063/1.4800629 LaFe11.5 xCrxSi1.5 x = 0.1 81.43 10.71 0.00 0.00 0.00 0.00 0.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1393            11.475  0.01 189  5 21.2 194.8 20.87     1 1098    x = 0.15 81.07 10.71 0.00 0.00 0.00 0.00 1.07 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1393            11.475  0.01 187  5 21.3 191.3 22.5     1 1099    x = 0.2 80.71 10.71 0.00 0.00 0.00 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1393            11.475  0.01 185  5 20.7 189.9 22.1     1 1100   LaFe11.5 xNixSi1.5 x = 0.1 81.43 10.71 0.00 0.00 0.00 0.00 0.00 0.71 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1393            11.474  0.01 197  5 17.5 199 23.5     1 1101    x = 0.15 81.07 10.71 0.00 0.00 0.00 0.00 0.00 1.07 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1393            11.473  0.01 200  5 14.4 202.7 25.8     1 1102    x = 0.2 80.71 10.71 0.00 0.00 0.00 0.00 0.00 1.43 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1393            11.473  0.01 206  5 12.2 207.6 27.2     1 1103   LaFe11.5Si1.5  82.14 10.71 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 360 1393            11.474  0.01 193  5 24.1       1 1104 977 10.1063/1.4760262 La0.7Ce0.3Fe11.6Si1.4  82.86 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.00 2.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1353              0.02 163 9         1 1105   La0.7Ce0.213Pr0.023Nd0.064Fe11.6Si1.4  82.87 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.46 1.50 0.16 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 720 1353              0.02 169 8 5 29.1 173 15.4     1 1106   La0.7Ce0.213Pr0.023Nd0.064Fe11.6Si1.4H1.6  82.87 10.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 5.00 0.46 1.50 0.16 0.00 0.00 0.00 0.00 0.00 0.00 100.00 11.43 0.00 0.00 0.00 arc_or_ind_melting 720 1353              0.02 314 0 [2, 5] [24.9, 25.4] [315, 317] [6.9, 18.65]     1 1107 976 10.1063/1.3670608 LaFe11.7Si1.3  83.57 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting 960 1373              0.05 189 2 [2, 5] [22.7, 28] [194, 199.7] [6.9, 18.7]     1 1108   LaFe11.7Si1.3C0.2  83.57 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 1.43 0.00 0.00 arc_or_ind_melting 168 1373              0.05 212 0 [2, 5] [18, 23.9] [215, 221] [9.35, 19.8]     1 1109   LaFe11.7Si1.3C0.2H1.7  83.57 9.29 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 12.14 1.43 0.00 0.00 arc_or_ind_melting 168 1373              0.05 320 0 [2, 5] [13.8, 19] [321.2, 320.9] [11.3, 22.2]     1 1110 975 10.1063/1.2713219  La(FexAl1−x)13 x = 0.86 79.86 0.00 13.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting                0.01 183 0 [1, 1.5, 2, 3, 4, 5] [1.7, 2.5, 3.1, 4.4, 5.4, 6.4] [180.8, 181.1, 182.4, 182.4, 184.7, 185.4] [45.8, 50, 55, 60.8, 68, 70.9]     1 Three transitions are found in M(T),may be better to use transition temperatures from S-T curves 1111    x = 0.87 80.79 0.00 12.07 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting                0.01 181 5 [1.5, 2, 3, 4, 5] [3.6, 4.2, 5.6, 6.5, 7.8] [151.7, 154.3, 161.5, 170, 182.5] [38.6, 51.7, 59.5, 69.7, 73.2]     1 1112    x = 0.88 81.71 0.00 11.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting                0.01 186 10 [0.6, 1, 2] [2.6, 3.0, 3.7] [126.8, 127.5, 142.5] [17.3, 32.3, 53.6]     1 1113    x = 0.89 82.64 0.00 10.21 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 7.14 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 100.00 0.00 0.00 0.00 0.00 arc_or_ind_melting                0.01 204 0 [4, 5] [2.1, 3] [143.1, 147.7] [48.3, 62.2]     1