 Be O Si Ca
   1.0
     7.4081346200000002    0.0000000000000000    0.0000000000000000
     0.0000000000000000    7.4081346200000002    0.0000000000000000
     0.0000000000000000    0.0000000000000000    4.9719727200000001
 Be O Si Ca
   2  14   4   4
Direct
   0.0000000000000000  0.0000000000000000  0.0000000000000000
   0.5000000000000000  0.5000000000000000  0.0000000000000000
   0.0871474900000000  0.1632588600000000  0.8164161900000000
   0.9128525100000000  0.8367411400000000  0.8164161900000000
   0.1632588600000000  0.9128525100000000  0.1835838100000000
   0.8367411400000000  0.0871474900000000  0.1835838100000000
   0.4128525100000000  0.6632588600000000  0.1835838100000000
   0.6632588600000000  0.5871474900000000  0.8164161900000000
   0.3367411400000000  0.4128525100000000  0.8164161900000000
   0.5871474900000000  0.3367411400000000  0.1835838100000000
   0.0000000000000000  0.5000000000000000  0.8312079999999999
   0.5000000000000000  0.0000000000000000  0.1687920000000000
   0.1399607500000000  0.3600392500000000  0.2849992800000000
   0.3600392500000000  0.8600392500000000  0.7150007199999999
   0.6399607500000000  0.1399607500000000  0.7150007199999999
   0.8600392500000000  0.6399607500000000  0.2849992800000000
   0.8521710400000000  0.6478289600000000  0.9609528899999999
   0.6478289600000000  0.1478289600000000  0.0390471100000000
   0.3521710400000000  0.8521710400000000  0.0390471100000000
   0.1478289600000000  0.3521710400000000  0.9609528899999999
   0.6638465300000000  0.8361534700000000  0.5135621900000000
   0.8361534700000000  0.3361534700000000  0.4864378100000000
   0.1638465300000000  0.6638465300000000  0.4864378100000000
   0.3361534700000000  0.1638465300000000  0.5135621900000000