 O Cl Pb Bi
   1.0
     5.6141098200000004    0.0000000000000000    0.0000000000000000
     0.0000000000000000   12.2385252599999994    0.0000000000000000
     0.0000000000000000    0.0000000000000000    5.5714534100000002
 O Cl Pb Bi
   8   4   4   4
Direct
   0.2389432400000000  0.0000000000000000  0.0000000000000000
   0.7610567600000000  0.0000000000000000  0.5000000000000000
   0.7610567600000000  0.0000000000000000  0.0000000000000000
   0.2389432400000000  0.0000000000000000  0.5000000000000000
   0.7389432400000000  0.5000000000000000  0.0000000000000000
   0.2610567600000000  0.5000000000000000  0.5000000000000000
   0.2610567600000000  0.5000000000000000  0.0000000000000000
   0.7389432400000000  0.5000000000000000  0.5000000000000000
   0.5000000000000000  0.2453588500000000  0.2500000000000000
   0.0000000000000000  0.2546411500000000  0.7500000000000000
   0.0000000000000000  0.7453588500000000  0.2500000000000000
   0.5000000000000000  0.7546411500000000  0.7500000000000000
   0.0000000000000000  0.3915671900000000  0.2500000000000000
   0.5000000000000000  0.1084328100000000  0.7500000000000000
   0.5000000000000000  0.8915671900000000  0.2500000000000000
   0.0000000000000000  0.6084328100000000  0.7500000000000000
   0.0000000000000000  0.0915315400000000  0.2500000000000000
   0.5000000000000000  0.4084684600000000  0.7500000000000000
   0.5000000000000000  0.5915315400000001  0.2500000000000000
   0.0000000000000000  0.9084684600000000  0.7500000000000000