 H O Mg Si
   1.0
     5.3266439700000001    0.0000000000000000    0.0000000000000000
    -2.6633219800000001    4.6130089900000000    0.0000000000000000
     0.0000000000000000    0.0000000000000000    7.2347949500000004
 H O Mg Si
   4   9   3   2
Direct
   0.0000000000000000  0.0000000000000000  0.1710080300000000
   0.3525202600000000  0.3525202600000000  0.7284287600000000
   0.0000000000000000  0.6474797400000001  0.7284287600000000
   0.6474797400000001  0.0000000000000000  0.7284287600000000
   0.0000000000000000  0.0000000000000000  0.3051979300000000
   0.3333333300000000  0.6666666700000000  0.2958055800000000
   0.6666666700000000  0.3333333300000000  0.2958055800000000
   0.5162855200000001  0.0000000000000000  0.9889331900000000
   0.0000000000000000  0.5162855200000001  0.9889331900000000
   0.4837144800000000  0.4837144800000000  0.9889331900000000
   0.6644623500000000  0.0000000000000000  0.5941141999999999
   0.0000000000000000  0.6644623500000000  0.5941141999999999
   0.3355376500000000  0.3355376500000000  0.5941141999999999
   0.3309249200000000  0.0000000000000000  0.4602880000000000
   0.0000000000000000  0.3309249200000000  0.4602880000000000
   0.6690750800000000  0.6690750800000000  0.4602880000000000
   0.3333333300000000  0.6666666700000000  0.0743951900000000
   0.6666666700000000  0.3333333300000000  0.0743951900000000