# Fileset

[Fatigue test data for Hastelloy X at RT.xlsx](https://mdr.nims.go.jp/filesets/6ee4dcd7-cdc2-4b58-aae3-e68e7a15929e/download)

## Creator

[Yoshiyuki Furuya](https://orcid.org/0000-0002-3039-5280), [Hideaki Nishikawa](https://orcid.org/0000-0002-2484-6903), [Kota Sawada](https://orcid.org/0000-0001-7780-1648), [Tomotaka Hatakeyama](https://orcid.org/0000-0002-2904-8177), [Masahiro Kusano](https://orcid.org/0000-0002-5061-0195), [Makoto Watanabe](https://orcid.org/0000-0002-5064-9583)

## Rights

[Creative Commons BY Attribution 4.0 International](https://creativecommons.org/licenses/by/4.0/)

## Other metadata

[Gigacycle fatigue properties of additively manufactured Hastelloy X](https://mdr.nims.go.jp/datasets/fc54fa49-98ec-4a3e-8918-314b431748dd)

## Fulltext

Conventional_Servo Specimen Stress amplitude (MPa) Number of cycles to failure Failure Origin CS-1 360 1.81E+05 Failed Surface CS-2 360 5.00E+05 Failed Surface CS-3 400 2.95E+04 Failed Surface CS-4 380 1.68E+05 Failed SurfaceConventional_Ultrasonic Specimen Stress amplitude (MPa) Number of cycles to failure Failure Origin CU-1 326 1.64E+08 Failed Internal CU-2 330 6.82E+07 Failed Internal CU-3 307 1.00E+09 Runout CU-4 300 1.00E+09 Runout CU-5 320 1.00E+09 RunoutAM Z_Servo Specimen Stress amplitude (MPa) Number of cycles to failure Failure Origin ZS-1 360 1.00E+07 Runout ZS-2 370 1.00E+07 Runout ZS-3 370 1.00E+07 Runout ZS-4 420 3.37E+06 Failed Surface ZS-5 440 1.43E+06 Failed SurfaceAM Z_Ultrasonic Specimen Stress amplitude (MPa) Number of cycles to failure Failure Origin ZU-1 300 1.47E+08 Failed Internal ZU-2 260 1.00E+09 Runout ZU-3 280 1.00E+09 Runout ZU-4 300 1.00E+09 Runout ZU-5 340 1.08E+08 Failed Internal ZU-6 320 1.43E+08 Failed Internal ZU-7 325 5.83E+07 Failed Surface ZU-8 300 4.62E+07 Failed SurfaceAM X_Servo Specimen Stress amplitude (MPa) Number of cycles to failure Failure Origin XS-1 400 9.29E+06 Failed Internal XS-2 420 3.22E+06 Failed Surface XS-3 440 7.42E+05 Failed Surface XS-4 380 1.00E+07 Runout XS-5 380 1.41E+07 Failed Internal XS-6 400 6.02E+06 Failed SurfaceAM X_Ultrasonic Specimen Stress amplitude (MPa) Number of cycles to failure Failure Origin XU-1 300 1.00E+09 Runout XU-2 340 4.46E+07 Failed Internal XU-3 320 1.32E+08 Failed Internal XU-4 300 6.97E+08 Failed Surface XU-5 300 1.00E+09 Runout XU-6 300 4.97E+07 Failed Internal XU-7 280 1.00E+09 Runout XU-8 320 3.29E+07 Failed Surface