Download file (10.5MB)
Download as zip (9.6MB)

コレクション

引用

説明:

The new fatigue data sheets, Nos. 135 and 136, disclose the gigacycle fatigue properties of A2017-T4 aluminium alloys. No. 135 shows gigacycle fatigue test results at a stress ratio of R = −1 up to 10^10 cycles, obtained by rotating bending fatigue testing at 100 Hz and by ultrasonic fatigue testing at 20 kHz, together with the results obtained by uniaxial loading fatigue testing at 100 Hz up to 10^8 cycles. No. 136 details the results from high stress ratios obtained by ultrasonic fatigue testing and 100 Hz uniaxial loading fatigue testing. Many specimens failed at over 10^7 cycles, so conventional fatigue limits were not confirmed, while fatigue failures at over 10^9 cycles were very rare, suggesting that the fatigue limits are in the gigacycle region. The results of the three types of fatigue tests showed good agreement, indicating the frequency and the stress gradient effects to be negligible. The fatigue strength of the aluminium alloys was proportional to the tensile strength, similar to observations made with low-strength steels at 10^7 cycles, but lower, at 10^10 cycles. The stress ratio effects, which reduced the fatigue strength in stress amplitudes, were not remarkable. The fatigue strengths at high stress ratios were close to the modified Goodman lines, meaning that the stress ratio effects could be estimated using conventional methods.

権利情報:

• Creative Commons BY Attribution 4.0 International
  

キーワード: Fatigue, structural materials, gigacycle fatigue, aluminium alloy, data sheet

刊行年月日: 2024-12-31

出版者: Informa UK Limited

掲載誌:

• Science and Technology of Advanced Materials: Methods (ISSN: 27660400) vol. 4 issue. 1

研究助成金:

原稿種別: 出版者版 (Version of record)

MDR DOI:

公開URL: https://doi.org/10.1080/27660400.2024.2365126

関連資料:

その他の識別子:

連絡先:

更新時刻: 2024-06-21 16:30:18 +0900

MDRでの公開時刻: 2024-06-21 16:30:18 +0900