In this study, we focus on in-plane and out-of-plane crystallinities of the MgB2 superconductor. These two structural properties were evaluated in terms of peak broadening at lower angles in the X-ray diffraction. The angular behavior of the in-plane and out-of-plane peaks was used to compare it with the corresponding behavior estimated in the case of several crystallite sizes (that affect the in-field superconductivity of MgB2). We propose that this comparison allows a simple evaluation to provide insight into the individual influences of in-plane and out-of-plane crystallinities on the in-field critical current density (without needing to calculate numerical values of crystallite sizes and lattice strains of fabricated MgB2 materials). For this study, we used MgB2 samples sintered at different temperatures. The sintering conditions affected not only the crystallinities but also the phase compositions. The behavior of the compositions, including amorphous phases, was also evaluated by using a quantitative analysis for X-ray diffraction results.

権利情報:

• Creative Commons BY Attribution 4.0 International
  

キーワード: Anysotropy, Disorder, MgB2, X-ray diffraction

刊行年月日: 2024-07-01

出版者: Elsevier BV

掲載誌:

• Ceramics International (ISSN: 02728842) vol. 50 issue. 19 p. 36042-36049

研究助成金:

原稿種別: 著者最終稿 (Accepted manuscript)

MDR DOI: https://doi.org/10.48505/nims.4943

公開URL: https://doi.org/10.1016/j.ceramint.2024.06.416

関連資料:

その他の識別子:

連絡先:

更新時刻: 2024-11-13 08:31:23 +0900

MDRでの公開時刻: 2024-11-13 08:31:23 +0900