説明:

Phosphors that exhibit tunable broadband emissions are highly desired in multi-functional LEDs, including pc-WLEDs and pc-NIR LEDs. In this work, broadband emissions were obtained and modulated in the unexpectedly wide spectral range of 517-609 nm for (Lu0.99-xGdxBi0.01)2WO6 phosphors via tuning the Gd3+ content (x = 0-0.99). The effects of Gd3+ doping on phase constituent, particle morphology, crystal structure, and photoluminescence were systematically investigated. Broadband green emission was obtained with the Gd3+-free (Lu0.99Bi0.01)2WO6 phosphor (x = 0), whose emission intensity was enhanced by 50%
with 5 at% of Gd3+ (x = 0.05). Phase transition happened when x ＞ 0.50, and broadband red-NIR emission was obtained when x = 0.75-0.99. Three luminescence centers were proved to be responsible for the broadband emissions via crystal structure, spectral fitting and fluorescence decay analysis. A pc-WLED with high color rendering index (Ra = 91.3), stable emission color, and low color temperature (3951 K) was fabricated from the (Lu0.94Gd0.05Bi0.01)2WO6 broadband green phosphor, and an LED device that simultaneously emits high color rendering white light and NIR light was obtained with the (Gd0.99Bi0.01)2WO6 broadband red-NIR phosphor. Night version and noninvasive imaging were also demonstrated for the latter LED device.

権利情報:

• In Copyright
  

キーワード: Broadband Bi3+ luminescence, Lu2WO6, Gd3+ doping

刊行年月日: 2023-01-14

出版者: Royal Society of Chemistry (RSC)

掲載誌:

• DALTON TRANSACTIONS (ISSN: 14779226) vol. 52 issue. 9 p. 2619-2630

研究助成金:

原稿種別: 著者最終稿 (Accepted manuscript)

MDR DOI: https://doi.org/10.48505/nims.4338

公開URL: https://doi.org/10.1039/D2DT03751C

関連資料:

その他の識別子:

連絡先:

更新時刻: 2024-01-15 11:59:40 +0900

MDRでの公開時刻: 2024-01-15 17:16:05 +0900