説明:

Mo2NiB2-Ni cermets, a type of boride-based cermet, exhibit attractive mechanical properties such as high hardness and good wear resistance. However, the mechanical properties of these cermets have predominantly been evaluated at room temperature. In this study, three-point bending tests were conducted at high temperatures to investigate the mechanical properties and fractography of Mo2NiB2-Ni cermets. A ternary Mo2NiB2-Ni cermet was prepared using a calcination process to synthesize Mo2NiB2 before intering. The calcination process resulted in finer and more uniform Mo2NiB2 particles, enhancing the microstructure. Consequently, hardness and transverse rupture strength (TRS) were improved. Three-point bending strengths were measured for samples measuring 4.0 × 3.0 × 24 mm at temperatures up to 800°C in an argon environment, using silicon carbide jigs with a 16 mm span. The results indicated that TRS remained approximately constant at about 1.6 GPa up to 500°C but decreased sharply above 600°C, reaching about 0.12 GPa at 800°C. This decrease was attributed to the softening of the nickel binder phase, which adversely affected the TRS.

権利情報:

• Creative Commons BY-NC-ND Attribution-NonCommercial-NoDerivs 4.0 International
  

キーワード: boride, cermets, mechanical properties

刊行年月日: 2024-11-15

出版者: Japan Society of Powder and Powder Metallurgy

掲載誌:

• Journal of the Japan Society of Powder and Powder Metallurgy (ISSN: 05328799) vol. 71 issue. 11 p. 551-555 24-00014

研究助成金:

原稿種別: 出版者版 (Version of record)

MDR DOI:

公開URL: https://doi.org/10.2497/jjspm.24-00014

関連資料:

その他の識別子:

連絡先:

更新時刻: 2025-05-09 16:30:17 +0900

MDRでの公開時刻: 2025-05-09 16:21:40 +0900