Consideration of Magnetic Flux Distribution in Multi−Filamented YBa2Cu3O7−δ Films by Controlling Crystal Array Using Surface−Modified Substrate

Hiroki Fujimoto; Akiyoshi Matsumoto; Shuuichi Ooi; Minoru Tachiki; Masayoshi Inoue; Ryo Teranishi

doi:10.1109/tasc.2024.3362729

論文 Consideration of Magnetic Flux Distribution in Multi−Filamented YBa₂Cu₃O_7−δ Films by Controlling Crystal Array Using Surface−Modified Substrate

Hiroki Fujimoto ; Akiyoshi Matsumoto (National Institute for Materials Science) ; Shuuichi Ooi (National Institute for Materials Science) ; Minoru Tachiki (National Institute for Materials Science) ; Masayoshi Inoue ; Ryo Teranishi

Download file (801KB)
Download as zip (730KB)

コレクション

引用

Hiroki Fujimoto, Akiyoshi Matsumoto, Shuuichi Ooi, Minoru Tachiki, Masayoshi Inoue, Ryo Teranishi. Consideration of Magnetic Flux Distribution in Multi−Filamented YBa₂Cu₃O_7−δ Films by Controlling Crystal Array Using Surface−Modified Substrate. IEEE Transactions on Applied Superconductivity. 2024, 34 (3), 1-4. https://doi.org/10.1109/tasc.2024.3362729

(BibTeX)

説明:

(abstract)

Large direct currents can flow through REBa2Cu3O7−δ (REBCO) wires without energy loss because of zero resistance. However, they suffer from alternating current (AC) loss. Here, a multifilament is produced by creating areas with disordered YBa2Cu3O7−δ (YBCO) using the metal−organic deposition method on SrTiO3 substrates with Zr patterning. YBCO crystal orientation without Zr patterning was ordered, whereas it was disordered in the sample with Zr patterning. Additionally, controlling the YBCO crystal array correlated with superconductivity and enabled it to be a multifilament. Therefore, this method can realize AC loss reduction.