Solid solutions Nd2MnMn(Mn4−xSbx)O12, belonging to the A-site columnar-ordered quadruple perovskite subfamily A2A’A’’B4O12 and prepared by a high-pressure, high-temperature method at about 6 GPa and about 1700 K, were investigated in a compositional range of 0.2 ≤ x ≤ 2.0. Crystal structures were studied using synchrotron powder X-ray diffraction. Two regions with different cation orders in the B sublattice were found: a narrow region of 0.8 ≤ x ≤ 1.0 had a B-site disordered structure with space group P42/nmc (No. 137), and a wider region of 1.6 ≤ x ≤ 2.0 had a B-site rock-salt-ordered structure with space group P42/n (No. 86). Small anti-site disorder of Nd and Mn was detected among the A, A’, and A’’ sites. In the B-site rock-salt-ordered structures, one B site was solely occupied by Mn, the second B’ site had a mixture of Sb and Mn (for x < 2). The samples showed complex magnetic behavior with two ferrimagnetic transitions. TC1 monotonically increased (from 66 K to 75 K) and TC2 was almost constant (about 6–7 K) for 0.8 ≤ x ≤ 1.0. TC1 monotonically decreased (from 77 K to 63 K) and TC2 monotonically increased (from 19 K to 39 K) for 1.6 ≤ x ≤ 2.0. There was evidence for the third magnetic transition in the 1.7 ≤ x ≤ 2.0 samples, and TC3 increased from 13 K to 20 K with increasing x.

権利情報:

• In Copyright
  

キーワード: A-site columnar-ordered perovskites, crystal structures, synchrotron X-ray, ferrimagnets, magnetic properties

刊行年月日: 2024-10-12

出版者: Elsevier BV

掲載誌:

• Ceramics International (ISSN: 02728842) vol. 50 issue. 24 p. 53099-53106

研究助成金:

• Japan Society for the Promotion of Science
• The Kazuchika Okura Memorial Foundation

原稿種別: 著者最終稿 (Accepted manuscript)

MDR DOI: https://doi.org/10.48505/nims.5118

公開URL: https://doi.org/10.1016/j.ceramint.2024.10.159

関連資料:

その他の識別子:

連絡先:

更新時刻: 2024-12-09 11:52:13 +0900

MDRでの公開時刻: 2026-10-12 08:33:05 +0900