Magnetic properties and magnetocaloric effect of DyCo9Si4

Naohito Tsujii; Atsushi Miyake; Masashi Tokunaga; Jaroslav Valenta; Hiroya Sakurai

doi:10.1016/j.jallcom.2024.173653

論文 Magnetic properties and magnetocaloric effect of DyCo9Si4

Naohito Tsujii (Research Center for Materials Nanoarchitectonics (MANA)/Nanomaterials Field/Thermal Energy Materials Group, National Institute for Materials Science) ; Atsushi Miyake (Institute for Materials Research, Tohoku University) ; Masashi Tokunaga (ISSP, Univ. of Tokyo) ; Jaroslav Valenta (Research Center for Materials Nanoarchitectonics (MANA)/Nanomaterials Field/Thermal Energy Materials Group, National Institute for Materials Science) ; Hiroya Sakurai (Research Center for Materials Nanoarchitectonics (MANA)/Quantum Materials Field/Frontier Superconducting Materials Group, National Institute for Materials Science)

Download file (1.32MB)
Download as zip (879KB)

コレクション

引用

Naohito Tsujii, Atsushi Miyake, Masashi Tokunaga, Jaroslav Valenta, Hiroya Sakurai. Magnetic properties and magnetocaloric effect of DyCo9Si4. Journal of Alloys and Compounds. 2024, 980 (), 173653. https://doi.org/10.1016/j.jallcom.2024.173653

(BibTeX)

説明:

(abstract)

正方晶LaFe9Si4型構造DyCo9Si4の多結晶試料をアーク溶解により合成した。磁化と比熱の測定により、40 K（Tc）と20 K（Tm）で二つの磁気異常がみられた。Tcでの転移はCo部分格子の強磁性転移であり、Dy3+の磁気モーメントはTC以下で徐々に整列しTm以下で長距離秩序となる。2 Kでの7 Tまでの磁化測定から、Dy3+の磁気モーメントがCoと反強磁性的に結合しフェリ磁性となっていることが分かった。また、50 Tまでのパルス磁場による低温磁化測定により、20 T付近でスピンフリップ転移を起こすことが分かった。スピンフリップ転移は温度上昇でブロードになるもののTcでも残っていることから強い反強磁性結合を示唆する。これらの測定により準断熱プロセスとして求めた磁気熱量効果では、5 Tまでの磁場変化でTm付近で最大エントロピー変化ΔS = 5 J/kg Kと見積もられ、50から0 TではTc付近で最大値ΔS = 24 J/kg Kとなった。