Near-infrared nanophosphors have attracted attention due to their wide application fields, including component analysis, bioimaging, and spectral converters of sunlight for crystalline silicon solar cells (c-Si). Yb3+ ions exhibit near-infrared (NIR) luminescence at around 1000 nm, which is consistent with the first biological window and the maximum responsivity range of c-Si. Therefore, we focused on and successfully synthesized Bi3+/Yb3+-doped NIR luminescence nanophosphors, RE2MoO6:Bi3+,Yb3+ (RE=Gd, Y, and Lu) and Gd2Mo1–xWxO6:Bi3+,Yb3+ (x = 0–0.5), utilizing a solvothermal reaction process. All samples exhibit NIR luminescence of Yb3+ ions under ultra-violet (UV) light excitation and broadband excitation due to the charge transfer transition between the O 2p/Bi 6s and Mo 4d or W 5d orbitals, indicated by their optical properties of photoluminescence (PL), PL excitation (PLE), and reflectance spectra. Furthermore, to evaluate the contribution of the Gd2MoO6:Bi,Yb (GMO:Bi,Yb) nanophosphor to the conversion efficiency of c-Si, a phosphor-converted film was made using dimethylpolysiloxane (PDMS) and the GMO:Bi,Yb nanophosphor. The results showed that the conversion efficiency of c-Si with the PDMS/GMO:Bi,Yb film is higher than that of c-Si with the PDMS-only film. Based on these results, the utilization of down-shifting nanophosphors is able to enhance the conversion efficiency of c-Si, which could be beneficial in addressing future energy challenges.

権利情報:

• Creative Commons BY Attribution 4.0 International
  

  You are free to:
  Share — copy and redistribute the material in any medium or format for any purpose, even commercially.
  Adapt — remix, transform, and build upon the material for any purpose, even commercially.
  The licensor cannot revoke these freedoms as long as you follow the license terms.

キーワード: Absorption, Ions, Luminescence, Optical Properties, Phosphors

刊行年月日: 2024-11-28

出版者: American Chemical Society (ACS)

掲載誌:

• The Journal of Physical Chemistry C (ISSN: 19327447) vol. 128 issue. 47 p. 20360-20368

研究助成金:

• Murata Science Foundation
• Ministry of Education, Culture, Sports, Science and Technology 20H00297
• Ministry of Education, Culture, Sports, Science and Technology 20K15106
• Ministry of Education, Culture, Sports, Science and Technology 22K05264
• Ministry of Education, Culture, Sports, Science and Technology JPMJFS2102

原稿種別: 出版者版 (Version of record)

MDR DOI:

公開URL: https://doi.org/10.1021/acs.jpcc.4c04814

関連資料:

その他の識別子:

連絡先:

更新時刻: 2024-12-11 16:30:44 +0900

MDRでの公開時刻: 2024-12-12 08:30:25 +0900