ABO3 perovskite materials with small cations at the A site, especially with ordered cation arrangements, have attracted a lot of interest because they show unusual physical properties and deviations from general perovskite tendencies. In this work, A-site-ordered quadruple perovskites, RMn3Ni2Mn2O12 with R = Nd, Sm, Gd, and Dy, were synthesized by a high-pressure, high-temperature method at about 6 GPa. Annealing at about 1500 K produced samples with additional (partial) B-site ordering of Ni2+ and Mn4+ cations, crystallizing in space group Pn-3. Annealing at about 1700 K produced samples with disordering of Ni2+ and Mn4+ cations, crystallizing in space group Im-3. However, magnetic properties were nearly identical for the Pn-3 and Im-3 modifications in comparison with ferromagnetic double perovskites R2NiMnO6, where the degree of Ni2+ and Mn4+ ordering has significant effects on magnetic properties. In RMn3Ni2Mn2O12, one magnetic transition was found at 26 K (for R = Nd), 23 K (for R = Sm), and 22 K (for R = Gd), and two transitions were found at 10 K and 36 K for R = Dy. Curie-Weiss temperatures were close to zero in all compounds suggesting that antiferromagnetic and ferromagnetic interactions are of the same magnitude.

権利情報:

• Creative Commons BY Attribution 4.0 International
  

キーワード: A-site-ordered perovskites, high-pressure synthesis, synchrotron X-ray diffraction, crystal structures, magnetic properties

刊行年月日: 2024-11-21

出版者: MDPI AG

掲載誌:

• Molecules (ISSN: 14203049) vol. 29 issue. 23 5488

研究助成金:

• Japan Society for the Promotion of Science JP22H04601
• the Kazuchika Okura Memorial Foundation 2022-11

原稿種別: 出版者版 (Version of record)

MDR DOI:

公開URL: https://doi.org/10.3390/molecules29235488

関連資料:

その他の識別子:

連絡先:

更新時刻: 2024-12-16 16:30:48 +0900

MDRでの公開時刻: 2024-12-16 16:30:48 +0900