The high-cycle fatigue strength of 22Cr-12Ni austenitic stainless steel was evaluated at 77 K for three types of materials with partially recrystallized (PR), finely recrystallized (FR), and solution-treated (ST) microstructures. Subsurface crack initiation was detected at the lower stress level and/or higher cycles in the materials, such that the fatigue crack initiation sites were shifted from the specimen surface to the interior of the specimen with increasing cycles. The ST showed a significant decrease in fatigue strength over 106 cycles due to subsurface crack initiation. Both PR and FR showed a significant improvement in their high-cycle fatigue strength in the high-cycle regime, although the increase in fatigue strength in the low-cycle regime was approximately equal to the increase in tensile strength.

権利情報:

• Creative Commons BY Attribution 4.0 International
  

キーワード: austenitic stainless steel, high-cycle fatigue property, cryogenic temperature

刊行年月日: 2024-05-01

出版者: IOP Publishing

掲載誌:

• IOP Conference Series: Materials Science and Engineering (ISSN: 17578981) vol. 1302 issue. 1 012001

研究助成金:

原稿種別: 著者最終稿 (Accepted manuscript)

MDR DOI: https://doi.org/10.48505/nims.5162

公開URL: https://doi.org/10.1088/1757-899x/1302/1/012001

関連資料:

その他の識別子:

連絡先:

更新時刻: 2024-12-17 16:30:37 +0900

MDRでの公開時刻: 2024-12-17 16:30:37 +0900