In determining the specifications for the production or recycling process of Ni-base single crystal superalloys, it is important to clarify the allowable trace impurity concentration. In this study, the effects of Pb and Sb on high-temperature strength and oxidation resistance of 6th generation superalloy TMS-238 were summarized. It was found that both Sb and Pb do not have a large effect on creep rupture life, but they degrade oxidation resistance. The removal of impurities by melting in a CaO crucible was tested and its mechanism was examined. It was found that Ca forms a compound with impurities within the alloy and prevents the segregation of impurities at the oxide film/substrate interface. The effect of CaO was also confirmed in an experiment in which impurity S was removed from 1st generation Ni-base superalloy TMS-1700 by adding CaO particles in a 3-ton commercial melting furnace. Similar results were obtained for this alloy, where it was also found that CaS had formed inside the alloy, thus improving the oxidation resistance of TMS-1700.

権利情報:

• In Copyright
  

キーワード: Creep, Single crystal, Impurity, Oxidation, CaO

刊行年月日: 2024-08-21

出版者: Springer Nature Switzerland

掲載誌:

• The Minerals, Metals & Materials Series (ISSN: 23671181) p. 555-560

研究助成金:

• JST the Advanced Low Carbon Technology Research and Development Program (ALCA)　JPNJAL1302
• NEDO JPNP21007

原稿種別: 著者最終稿 (Accepted manuscript)

MDR DOI: https://doi.org/10.48505/nims.4871

公開URL: https://doi.org/10.1007/978-3-031-63937-1_52

関連資料:

その他の識別子:

連絡先:

更新時刻: 2025-08-21 08:30:15 +0900

MDRでの公開時刻: 2025-08-21 08:19:08 +0900