This study investigated the low-temperature fracture toughness of martensite and bainite with various Bain unit sizes. The three-point bending tests revealed that the apparent fracture toughness increased with decreasing the Bain unit size. We also found that even when the carbide size and distribution were almost the same, the apparent fracture toughness of tempered martensite with Bain unit size of 2.5 um was much higher than that of bainite with Bain unit size of 16.2 um. The propagation of micro-crack stopped at the Bain unit boundaries when the Bain unit size was small. The additional load was necessary for further propagation of crack which stopped at the Bain unit boundaries, leading to the improvement of fracture toughness. The critical local fracture toughness corresponding to the propagation of crack across the Bain unit boundaries was estimated at 1.04 MPa m1/2 by finite element simulations. Based on this value, we proposed that the Bain unit boundary whose interval was less than 9.4 um could become obstacle for the crack propagation after penetrating matrix / carbide boundary.

権利情報:

• Creative Commons BY-NC-ND Attribution-NonCommercial-NoDerivs 4.0 International
  

キーワード: low-temperature embrittlement, fracture toughness, cleavage fracture, bainite, martensite

刊行年月日: 2024-01-30

出版者: Iron and Steel Institute of Japan

掲載誌:

• ISIJ International (ISSN: 13475460) vol. 64 issue. 2 p. 381-388 ISIJINT-2023-141

研究助成金:

原稿種別: 出版者版 (Version of record)

MDR DOI:

公開URL: https://doi.org/10.2355/isijinternational.isijint-2023-141

関連資料:

その他の識別子:

連絡先:

更新時刻: 2024-08-20 08:30:40 +0900

MDRでの公開時刻: 2024-08-20 08:30:40 +0900