The creep behavior of Hastelloy X fabricated by laser powder bed fusion was investigated, focusing on the testing temperatures of 700°C, 800°C, 900°C and 1000°C. For PiHA heat, the stress axis was parallel to the build direction, whereas for PiHC heat it was perpendicular. The creep strength of PiHA was similar to that of the conventional Hastelloy X at 700°C to 1000°C. The creep life of PiHC was one order of magnitude shorter than that of PiHA at 800°C and 900°C. For estimating allowable stress of additively manufactured Hastelloy X, the creep strength of PiHC will be minimum value. The creep ductility was much lower in PiHA and PiHC than in the conventional Hastelloy X at all testing temperatures. No large difference in creep ductility was observed between PiHA and PiHC. Double local minimum values of creep rate were recognized in creep rate versus time curves at 700°C and 800°C for PiHA and PiHC. Creep voids and cracks were observed at grain boundaries perpendicular to the stress axis in PiHA and PiHC. M23C6, µ phase, R phase and M6C particles were observed after creep exposure.

権利情報:

• Creative Commons BY Attribution 4.0 International
  

キーワード: Hastelloy X, Additive manufacturing, creep strength, creep deformation behavior, precipitates

刊行年月日: 2025-12-31

出版者: Informa UK Limited

掲載誌:

• Science and Technology of Advanced Materials: Methods (ISSN: 27660400) vol. 5 issue. 1 2582996

研究助成金:

• Amada Foundation AF-2022201-A3

原稿種別: 出版者版 (Version of record)

MDR DOI:

公開URL: https://doi.org/10.1080/27660400.2025.2582996

関連資料:

その他の識別子:

連絡先:

更新時刻: 2025-11-21 16:30:04 +0900

MDRでの公開時刻: 2025-11-21 16:23:46 +0900