We are conducting research aimed at the practical application of sulfonated PPSU, a hydrocarbon electrolyte, as a non-fluorine electrolyte. In this study, we report the synthesis and properties of sulfonated PPSU with high ion exchange capacity (IEC) (calculated value: 5.55meq/g), which has four sulfo groups per repeating unit of PPSU. SPPSU (2S), which has two sulfo groups per repeating unit of PPSU (IEC=3.57meq/g), was obtained by sulfonation of bis(4-fluorophenyl)sulfone using 30% Oleum. Next, polymerization was performed by condensation reaction of sulfonated bis(4-fluorophenyl)sulfone (SFPS) and 4,4'-biphenol (BP). Furthermore, by sulfonating these polymers in sulfuric acid, SPPSU (4S) having four sulfo groups per repeating unit (IEC=5.55meq/g) was synthesized. The molecular weight of SPPSU(4S) was 130,304 – 303,203. Depending on the sulfonation conditions using SPPSU(2S) polymer and sulfuric acid, the viscosity of SPPSU(4S) was 30 to 270 mP·s, which was higher than that of Nafion (D520CS), which was 10 to 40 mPa·s. In addition, the tensile strength, tensile elongation, and flexural modulus of SPPSU (4S) were 22 MPa, 251%, and 296 MPa. Compared to Nafion 212, it exhibited high tensile strength and flexural modulus while having similar tensile elongation properties. Furthermore, the conductivity of SPPSU (4S) was 11.3 mS/cm at 120°C and RH 10%. This value was approximately 4 times higher than the conductivity of Nafion212 (3.2 mS/cm) under the same conditions.

権利情報:

• In Copyright
  

キーワード: Sulfonated Poly(phenylene sulfone)s (SPPSU), High Ion Exchange Capacity, SPPSU ionomer, Electrolyte membranes, PEFCs

刊行年月日:

出版者:

掲載誌:

会議: PRiME 2024 (2024-10-06 - 2024-10-11)

研究助成金:

原稿種別: 著者最終稿 (Accepted manuscript)

MDR DOI: https://doi.org/10.48505/nims.4862

公開URL: https://ecs.confex.com/ecs/prime2024/meetingapp.cgi/Paper/190321

関連資料:

その他の識別子:

連絡先:

更新時刻: 2024-10-17 16:30:20 +0900

MDRでの公開時刻: 2024-10-17 16:30:21 +0900