A polymer solution can be flash-frozen to prepare homopolymers with mesoporous structures in a template-free manner. The flash-freezing method is derived from the ice-templating or freeze-casting method. Herein, we comprehensively investigated the effects of 13 good solvents for polystyrene as well as the polystyrene concentration on the fabrication process. Solvents with high boiling-point-to-melting-point ratios yielded uniformly sized mesoporous polystyrenes at polymer concentrations ≥20 wt %. Such solvents provided a high specific surface area (328 m2/g) and a large mesopore volume (1.78 g/cm3) at the optimal polystyrene concentration. Solvents with medium-boiling-point-to-melting-point ratios formed bimodal mesopores, while a low polystyrene concentration gave hierarchical structures composed of mesopores and macropores. These results provide an understanding of the mechanism associated with the formation of mesopores and enable control over the desired mesopore morphology.

権利情報:

• In Copyright
  This document is the Accepted Manuscript version of a Published Work that appeared in final form in [Solvent Effects during the Flash-Freezing Fabrication of Mesoporous Polystyrenes], copyright © 2022 American Chemical Society after peer review and technical editing by the publisher. To access the final edited and published work see https://pubs.acs.org/doi/10.1021/acs.macromol.2c00535.

キーワード: nanoporous polymers, nanocrystal, ice templating

刊行年月日: 2022-05-10

出版者: American Chemical Society (ACS)

掲載誌:

• Macromolecules (ISSN: 15205835) p. 3734-3746

研究助成金:

原稿種別: 著者最終稿 (Accepted manuscript)

MDR DOI: https://doi.org/10.48505/nims.3959

公開URL: https://doi.org/10.1021/acs.macromol.2c00535

関連資料:

その他の識別子:

連絡先:

更新時刻: 2024-01-05 22:11:20 +0900

MDRでの公開時刻: 2023-05-08 15:55:56 +0900