In this study, we evaluated the material properties of 1180MPa class recycled steel sheets created from waste scrap and conducted two types of fatigue tests to evaluate the required performance of parts as steel sheets for automobiles. The obtained results are shown below. In the fatigue test with R = -1, when a mirror-finished test piece was used, the fatigue limit of 107 times was 600 MPa for both bending and axial force. The 107-time fatigue limit was 500 MPa for the pickled and untouched test pieces. It was shown that this difference in fatigue limit is due to the effect of surface roughness. As a result of investigating the influence of the stress ratio by the bending fatigue test, the 107th fatigue limit was 610MPa for R = -1 and 476MPa for R = 0. As a result of plotting the fatigue limit diagram, it was shown that the fatigue limit of R = 0 is located almost on the modified goodman line, and that this test material can evaluate the effect of average stress by the fatigue limit diagram.

権利情報:

• In Copyright
  

キーワード: High-strength recycled steel; 10^7 cycles fatigue limit; Stress ratio; Fatigue limit diagram

会議: 13th International Fatigue Congress (FATIGUE2022+1) (2023-11-06 - 2023-11-10)

研究助成金:

原稿種別: 著者最終稿 (Accepted manuscript)

MDR DOI: https://doi.org/10.48505/nims.4320

公開URL:

関連資料:

その他の識別子:

連絡先:

更新時刻: 2024-01-04 13:40:01 +0900

MDRでの公開時刻: 2023-12-29 08:30:22 +0900